A set of correct expressions for calculating activities and activity coefficients from binary phase diagrams involving intermediate compounds are presented in this paper by the introduction of a correct parameter θ. ...A set of correct expressions for calculating activities and activity coefficients from binary phase diagrams involving intermediate compounds are presented in this paper by the introduction of a correct parameter θ. The application of these expressions to system Mg-Sn shows that they are quite feasible.展开更多
New formulae for calculating activities and activity coefficients from binary phase diagrams containing solidsolution are presented. In the new formulae, a parameterθ is introduced. It seems be more efficient The app...New formulae for calculating activities and activity coefficients from binary phase diagrams containing solidsolution are presented. In the new formulae, a parameterθ is introduced. It seems be more efficient The application ofthese formulae to system Ag-Pb proves its efficiency.展开更多
The 5Cu40Zn55Al and 15Cu20Zn65Al alloys were prepared in the Al-Zn-Cu system. There exist the metastable phases ε and θ in the two alloys after homogenization treatment and furnace cooling,respectively. It is shown ...The 5Cu40Zn55Al and 15Cu20Zn65Al alloys were prepared in the Al-Zn-Cu system. There exist the metastable phases ε and θ in the two alloys after homogenization treatment and furnace cooling,respectively. It is shown that the particles are refined from 3 mm to less than 10 μm after hammering the two alloys but there are still metastable phases. This means that the phase constituents of the two alloys have no changes by the deformation,which is different from that by balling. The phase constituents are not changed at room temperature by hammering,which is dependent on the deformation mechanism of hammering.展开更多
The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calcul...The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calculated according to DSC curves using single heating rate method. The microstructures of as-rolled and peak-aged alloys were observed by transmission electron microscopy（TEM）. The result shows that the age hardenability reduces and the activation energy rises with increasing the reduction from 7% to 40%. Nonuniform dislocations are found in as-rolled alloy and inhomogeneous distribution of θ′ phase is revealed in peak-aged alloy when the reduction is 15%. The inhomogeneous distribution of θ′ phase may be related to the age hardenability reducing and activation energy rising.展开更多
The stress aging behavior of Al-Cu alloy under various applied stresses, i.e., elastic stress, yield stress and plasticdeformation stress, was investigated using single crystals. The resulting microstructures and the ...The stress aging behavior of Al-Cu alloy under various applied stresses, i.e., elastic stress, yield stress and plasticdeformation stress, was investigated using single crystals. The resulting microstructures and the yield strength were examined bytransmission electron microscopy （TEM） and compression tests, respectively. The results indicate that an elastic stress of 15 MPa ishigh enough to influence the precipitation distribution of θ′ during aging at 180℃. The applied stress loading along [116]Aldirection results in increased number density of θ′ on （001）Al habit planes. This result becomes more significant with increasingapplied stress and leads to lower yield strength of Al-Cu single crystals during aging. Moreover, the generation of the preferentialorientation of θ′ was discussed by the effect of the dislocation induced by applied stress as well as the role of the misfit between theθ′-precipitate and Al matrix. The results are in agreement with the effect of the latter one.展开更多
文摘A set of correct expressions for calculating activities and activity coefficients from binary phase diagrams involving intermediate compounds are presented in this paper by the introduction of a correct parameter θ. The application of these expressions to system Mg-Sn shows that they are quite feasible.
文摘New formulae for calculating activities and activity coefficients from binary phase diagrams containing solidsolution are presented. In the new formulae, a parameterθ is introduced. It seems be more efficient The application ofthese formulae to system Ag-Pb proves its efficiency.
基金Project(50171019) supported by the National Natural Science Foundation of ChinaProject(1063293) supported by Shenyang Science and Technology Foundation, China
文摘The 5Cu40Zn55Al and 15Cu20Zn65Al alloys were prepared in the Al-Zn-Cu system. There exist the metastable phases ε and θ in the two alloys after homogenization treatment and furnace cooling,respectively. It is shown that the particles are refined from 3 mm to less than 10 μm after hammering the two alloys but there are still metastable phases. This means that the phase constituents of the two alloys have no changes by the deformation,which is different from that by balling. The phase constituents are not changed at room temperature by hammering,which is dependent on the deformation mechanism of hammering.
基金Project(2012CB619500)supported by the National Basic Research Program of China
文摘The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calculated according to DSC curves using single heating rate method. The microstructures of as-rolled and peak-aged alloys were observed by transmission electron microscopy（TEM）. The result shows that the age hardenability reduces and the activation energy rises with increasing the reduction from 7% to 40%. Nonuniform dislocations are found in as-rolled alloy and inhomogeneous distribution of θ′ phase is revealed in peak-aged alloy when the reduction is 15%. The inhomogeneous distribution of θ′ phase may be related to the age hardenability reducing and activation energy rising.
基金Project(51375503)supported by the National Natural Science Foundation of China
文摘The stress aging behavior of Al-Cu alloy under various applied stresses, i.e., elastic stress, yield stress and plasticdeformation stress, was investigated using single crystals. The resulting microstructures and the yield strength were examined bytransmission electron microscopy （TEM） and compression tests, respectively. The results indicate that an elastic stress of 15 MPa ishigh enough to influence the precipitation distribution of θ′ during aging at 180℃. The applied stress loading along [116]Aldirection results in increased number density of θ′ on （001）Al habit planes. This result becomes more significant with increasingapplied stress and leads to lower yield strength of Al-Cu single crystals during aging. Moreover, the generation of the preferentialorientation of θ′ was discussed by the effect of the dislocation induced by applied stress as well as the role of the misfit between theθ′-precipitate and Al matrix. The results are in agreement with the effect of the latter one.