The as-cast microstructure, element segregation and solidification behavior of a multi-alloyed superalloy ЭК151 have been investigated. The results show that the severe element segregation leads to the complicated p...The as-cast microstructure, element segregation and solidification behavior of a multi-alloyed superalloy ЭК151 have been investigated. The results show that the severe element segregation leads to the complicated precipitations at the inter-dendritic region, including η-Ni3(Ti, Nb), eutectic(γ + γ’) and Laves, which shows the characteristics of both Ti, Al-strengthened and Nb-strengthened alloys. Differential thermal analysis, heating and quenching tests reveal the solidification sequence as follows: Liquids →γ matrix →(Nb, Ti)C →η-Ni 3(Ti, Nb) →eutectic( γ+γ’) → Laves. The melting points are between 1250 and 1260 °C for(Nb, Ti)C, between 1200 and 1210 °C for η phase, between 1180 and 1190 °C for eutectic(γ+γ’) and Laves. γ’ initially precipitates from matrix at 1150 °C and achieves the maximum precipitation at 1130 °C. According to the microstructure evolution captured during solidification and composition analysis by an energy dispersive spectrometer and electron probe microanalyzer,(Nb, Ti)/Al ratio is put forward to explain the formation of η-Ni3(Ti, Nb) and eutectic( γ+γ’). The solidification of γ matrix increased the Nb, Ti concentration in the residual liquids, so the high(Nb, Ti)/Al ratio would result in the formation of η-Ni3(Ti, Nb); the precipitation of the phase consumed Nb and Ti and decreased the(Nb, Ti)/Al ratio in the liquid, which led to the precipitation of eutectic(γ + γ’). Laves formed by the sides of η-Ni3(Ti, Nb) and in front of the eutectic( γ + γ’) after Al, Ti were further depleted by the two phases and Cr, Co, Mo were rejected to liquids.展开更多
文摘The as-cast microstructure, element segregation and solidification behavior of a multi-alloyed superalloy ЭК151 have been investigated. The results show that the severe element segregation leads to the complicated precipitations at the inter-dendritic region, including η-Ni3(Ti, Nb), eutectic(γ + γ’) and Laves, which shows the characteristics of both Ti, Al-strengthened and Nb-strengthened alloys. Differential thermal analysis, heating and quenching tests reveal the solidification sequence as follows: Liquids →γ matrix →(Nb, Ti)C →η-Ni 3(Ti, Nb) →eutectic( γ+γ’) → Laves. The melting points are between 1250 and 1260 °C for(Nb, Ti)C, between 1200 and 1210 °C for η phase, between 1180 and 1190 °C for eutectic(γ+γ’) and Laves. γ’ initially precipitates from matrix at 1150 °C and achieves the maximum precipitation at 1130 °C. According to the microstructure evolution captured during solidification and composition analysis by an energy dispersive spectrometer and electron probe microanalyzer,(Nb, Ti)/Al ratio is put forward to explain the formation of η-Ni3(Ti, Nb) and eutectic( γ+γ’). The solidification of γ matrix increased the Nb, Ti concentration in the residual liquids, so the high(Nb, Ti)/Al ratio would result in the formation of η-Ni3(Ti, Nb); the precipitation of the phase consumed Nb and Ti and decreased the(Nb, Ti)/Al ratio in the liquid, which led to the precipitation of eutectic(γ + γ’). Laves formed by the sides of η-Ni3(Ti, Nb) and in front of the eutectic( γ + γ’) after Al, Ti were further depleted by the two phases and Cr, Co, Mo were rejected to liquids.
