Low temperature mechanical properties of AZ91D magnesium alloy fabricated by solid recycling process from recycled scraps were studied. Various microstructural analyses were performed using optical microscopy （OM） a...Low temperature mechanical properties of AZ91D magnesium alloy fabricated by solid recycling process from recycled scraps were studied. Various microstructural analyses were performed using optical microscopy （OM） and scanning electron microscopy （SEM）. The recycled specimens consist of fine grains due to dynamic recrystallization and the interfaces of original individual scraps are not identified. Tensile tests were performed at a strain rate of 5 x 10 3 s 1 at room temperature （27 ~C）, -70, -100 and 130 ~C, respectively. Ultimate tensile strength of the specimens increases slightly with decreasing the tensile temperature, and elongation to failure decreases with decreasing the tensile temperature. The tensile specimens at -130 ~C show the highest ultimate tensile strength of 360.65 MPa and the lowest elongation to failure of 5.46%. Impact tests were performed at room temperature （27 ~C）, -70 and -130 ~C, respectively. Impact toughness decreases with decreasing the impact temperature. The impact specimens at -130 ~C show the lowest impact toughness of 3.06 J/cm2.展开更多
This study aimed to grasp the characteristics of woody biomass use and application in leading examples of Japanese biomass towns, and made the following two points clear： （1） Biomass town plans had been officially ...This study aimed to grasp the characteristics of woody biomass use and application in leading examples of Japanese biomass towns, and made the following two points clear： （1） Biomass town plans had been officially announced in 318 districts by 2011, and in about 71% of the districts, woody biomass use and application, which is classified into four types, was being conducted; （2） In each example studied, regional characteristics were reflected and there were distinct characteristics. Shimokawa Town in Hokkaido made the most number of efforts, and after 2008 the number of efforts was increasing; however, along with each of the other examples, the use and application of forest timber offcuts is a task for the future.展开更多
基金Projects(50674038,50974048)supported by the National Natural Science Foundation of ChinaProject(200802140004)supported by Doctoral Fund of Ministry of Education of China
文摘Low temperature mechanical properties of AZ91D magnesium alloy fabricated by solid recycling process from recycled scraps were studied. Various microstructural analyses were performed using optical microscopy （OM） and scanning electron microscopy （SEM）. The recycled specimens consist of fine grains due to dynamic recrystallization and the interfaces of original individual scraps are not identified. Tensile tests were performed at a strain rate of 5 x 10 3 s 1 at room temperature （27 ~C）, -70, -100 and 130 ~C, respectively. Ultimate tensile strength of the specimens increases slightly with decreasing the tensile temperature, and elongation to failure decreases with decreasing the tensile temperature. The tensile specimens at -130 ~C show the highest ultimate tensile strength of 360.65 MPa and the lowest elongation to failure of 5.46%. Impact tests were performed at room temperature （27 ~C）, -70 and -130 ~C, respectively. Impact toughness decreases with decreasing the impact temperature. The impact specimens at -130 ~C show the lowest impact toughness of 3.06 J/cm2.
文摘This study aimed to grasp the characteristics of woody biomass use and application in leading examples of Japanese biomass towns, and made the following two points clear： （1） Biomass town plans had been officially announced in 318 districts by 2011, and in about 71% of the districts, woody biomass use and application, which is classified into four types, was being conducted; （2） In each example studied, regional characteristics were reflected and there were distinct characteristics. Shimokawa Town in Hokkaido made the most number of efforts, and after 2008 the number of efforts was increasing; however, along with each of the other examples, the use and application of forest timber offcuts is a task for the future.