The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing ...The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing temperature gradient in the plate with decreasing quenching rate,which leads to weakened inhomogeneous plastic deformation and decreased residual stress.No dynamic precipitation on the grain boundary happens after either cold water cooling or air cooling,however,air cooling leads to dynamic precipitation of Mg-Zn phase on Mn particles around which a low-density precipitate zone develops after aging treatment.Moreover,the fine and densely distributed Mg-Zn precipitates observed after aging treatment of the cold water cooled alloy are replaced by coarse precipitates with low density for the air cooled alloy.Both the low-density precipitate zone near Mn particles and the coarsening of precipitates are the source of the decrease in hardness and tensile properties of the air cooled alloy.The residual stress drops faster than the hardness with decreasing quenching rate,which makes it possible to lower the residual stress without sacrificing too much age-hardening ability of the alloy.展开更多
Al0.3CrFe1.5MnNi0.5 high entropy alloys(HEA)have special properties.The microstructures and shear strengths of HEA/HEA and HEA/6061-Al joints were determined after direct active soldering(DAS)in air with Sn3.5Ag4Ti ac...Al0.3CrFe1.5MnNi0.5 high entropy alloys(HEA)have special properties.The microstructures and shear strengths of HEA/HEA and HEA/6061-Al joints were determined after direct active soldering(DAS)in air with Sn3.5Ag4Ti active filler at 250°C for 60 s.The results showed that the diffusion of all alloying elements of the HEA alloy was sluggish in the joint area.The joint strengths of HEA/HEA and HEA/6061-Al samples,as analyzed by shear testing,were(14.20±1.63)and(15.70±1.35)MPa,respectively.Observation of the fracture section showed that the HEA/6061-Al soldered joints presented obvious semi-brittle fracture characteristics.展开更多
基金supported by the National Key Research and Development Program of China[2016YFB0301105]the National Key Research and Development Plan[2017YFB0103904]
文摘The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing temperature gradient in the plate with decreasing quenching rate,which leads to weakened inhomogeneous plastic deformation and decreased residual stress.No dynamic precipitation on the grain boundary happens after either cold water cooling or air cooling,however,air cooling leads to dynamic precipitation of Mg-Zn phase on Mn particles around which a low-density precipitate zone develops after aging treatment.Moreover,the fine and densely distributed Mg-Zn precipitates observed after aging treatment of the cold water cooled alloy are replaced by coarse precipitates with low density for the air cooled alloy.Both the low-density precipitate zone near Mn particles and the coarsening of precipitates are the source of the decrease in hardness and tensile properties of the air cooled alloy.The residual stress drops faster than the hardness with decreasing quenching rate,which makes it possible to lower the residual stress without sacrificing too much age-hardening ability of the alloy.
基金financial support of this work from the Ministry of Science and Technology, Taibei, China, under Projects No. MOST 105-ET-E-020002-ET, 105-2622-E-020-003-CC3
文摘Al0.3CrFe1.5MnNi0.5 high entropy alloys(HEA)have special properties.The microstructures and shear strengths of HEA/HEA and HEA/6061-Al joints were determined after direct active soldering(DAS)in air with Sn3.5Ag4Ti active filler at 250°C for 60 s.The results showed that the diffusion of all alloying elements of the HEA alloy was sluggish in the joint area.The joint strengths of HEA/HEA and HEA/6061-Al samples,as analyzed by shear testing,were(14.20±1.63)and(15.70±1.35)MPa,respectively.Observation of the fracture section showed that the HEA/6061-Al soldered joints presented obvious semi-brittle fracture characteristics.