The hydrothermal reaction of NH 4VO 3, CoCl 2·6H 2O, o-phen and H 2O gave a novel two-dimensional layered polyoxovanadate, [Co(o-phen)]V 2O 6·H 2O, which was constructed from {V 2O 6} chains linked by Co(o-p...The hydrothermal reaction of NH 4VO 3, CoCl 2·6H 2O, o-phen and H 2O gave a novel two-dimensional layered polyoxovanadate, [Co(o-phen)]V 2O 6·H 2O, which was constructed from {V 2O 6} chains linked by Co(o-phen) complex fragments. [Co(o-phen)]V 2O 6·H 2O was characterized by IR, TG and single-crystal X-ray diffraction. It crystallizes in monoclinic space group P2(1)/c with a= 0.785 2(9) nm, b=2.118 3(2) nm, c=0.946 3(11) nm, β=112.827(2)°, V=0.145 1(3) nm3, D c=2.074 g/cm3, Z=4, R 1=0.038 8, wR 2=0.094 1.展开更多
A new isopolyoxovanadate [Ni(1,10′-phen) 3] 2 [V Ⅳ 2V Ⅴ 8O 26] was hydrothermally synthesized and structurally characterized by the single crystal X-ray diffraction. The compound crystallizes in orthorhombic system...A new isopolyoxovanadate [Ni(1,10′-phen) 3] 2 [V Ⅳ 2V Ⅴ 8O 26] was hydrothermally synthesized and structurally characterized by the single crystal X-ray diffraction. The compound crystallizes in orthorhombic system, space group Pbcn with a=1.362 9(3) nm, b=2.215 6(4) nm, c= 2.571 2(4) nm, V=7.764(2) nm 3, Z=4, R=0.040 3, wR 2=0.044 6. The compound exhibits an unusual empty ellipsoidal cage, which is constructed by eight {V ⅤO 4} tetrahedra and two {V ⅣO 5} square pyramids via corner-sharing modes. The chiral [Ni(1,10′-phen) 3] 2+ complexes act as the counter cations.展开更多
采用平面波超软赝势密度泛函理论的方法研究了Zn_3V_2O_8的能带结构、电子态密度和光学特性。能带结果显示Zn_3V_2O_8呈间接带隙的绝缘体型能带,其禁带宽度为2.9 e V。详细的电子态密度结果显示其费米面上的态密度达到20 e/e V,费米能...采用平面波超软赝势密度泛函理论的方法研究了Zn_3V_2O_8的能带结构、电子态密度和光学特性。能带结果显示Zn_3V_2O_8呈间接带隙的绝缘体型能带,其禁带宽度为2.9 e V。详细的电子态密度结果显示其费米面上的态密度达到20 e/e V,费米能级附近的能级由Zn3p、V3p和O2p电子形成,Zn3d和O2s之间有强的杂化作用。介电性能结果显示在4.4~5.7 e V附近有强的吸收峰,在20.6 e V附近有一个次强吸收峰;吸收光谱显示在6.8 e V处有强吸收,在20.7 e V处有一个较弱的吸收峰。展开更多
A novel compound Ni(phen)(H2O)(V2O6) has been hydrothermally synthesized and structurally determined to be a two-dimensional compound, which contains {V2O6}n2n- chains interconnected by nickel(II) complexes via oxygen...A novel compound Ni(phen)(H2O)(V2O6) has been hydrothermally synthesized and structurally determined to be a two-dimensional compound, which contains {V2O6}n2n- chains interconnected by nickel(II) complexes via oxygen atoms. The crystallographic data measured by single-crystal X-ray diffraction analysis are as follows: C12H10N2NiO7V2, Mr=454.81, monoclinic, space group P21 / c, a=0.784 6(3), b=2.103 6(8), c=0.942 3(4) nm, β=112.872(5)°, V=1.433 0(10) nm3, Z=4, Dc=2.104 Mg·m-3, μ(Mo Kα)=2.615 mm-1, F(000)=904, T=298(2) K, 4 480 reflections collected, 2 470 independent (Rint=0.032 2), the final R=0.058 4 and wR2=0.145 7 for 2 303 observed reflections with I>2σ(I). CCDC: 192520.展开更多
A new complex[Ni(en) 2V 6O 14] n was hydrothermally synthesized and characterized by 2-dimensional vanadium oxide framework pillared by Ni(en) 2 group. Single crystal X-ray analysis indicates that this compound crysta...A new complex[Ni(en) 2V 6O 14] n was hydrothermally synthesized and characterized by 2-dimensional vanadium oxide framework pillared by Ni(en) 2 group. Single crystal X-ray analysis indicates that this compound crystallizes in monoclinic system, space group P2 1/c with a= 0.892 17(18) nm, b= 1.711 1(3) nm, c=0.662 73(13) nm, β=111.58(3)°, V=0.940 8(3) nm 3, Z=2, D c= 2.501 g/cm 3, R=0.042 3, wR=0.060 9, S=1.006.展开更多
文摘The hydrothermal reaction of NH 4VO 3, CoCl 2·6H 2O, o-phen and H 2O gave a novel two-dimensional layered polyoxovanadate, [Co(o-phen)]V 2O 6·H 2O, which was constructed from {V 2O 6} chains linked by Co(o-phen) complex fragments. [Co(o-phen)]V 2O 6·H 2O was characterized by IR, TG and single-crystal X-ray diffraction. It crystallizes in monoclinic space group P2(1)/c with a= 0.785 2(9) nm, b=2.118 3(2) nm, c=0.946 3(11) nm, β=112.827(2)°, V=0.145 1(3) nm3, D c=2.074 g/cm3, Z=4, R 1=0.038 8, wR 2=0.094 1.
文摘A new isopolyoxovanadate [Ni(1,10′-phen) 3] 2 [V Ⅳ 2V Ⅴ 8O 26] was hydrothermally synthesized and structurally characterized by the single crystal X-ray diffraction. The compound crystallizes in orthorhombic system, space group Pbcn with a=1.362 9(3) nm, b=2.215 6(4) nm, c= 2.571 2(4) nm, V=7.764(2) nm 3, Z=4, R=0.040 3, wR 2=0.044 6. The compound exhibits an unusual empty ellipsoidal cage, which is constructed by eight {V ⅤO 4} tetrahedra and two {V ⅣO 5} square pyramids via corner-sharing modes. The chiral [Ni(1,10′-phen) 3] 2+ complexes act as the counter cations.
文摘采用平面波超软赝势密度泛函理论的方法研究了Zn_3V_2O_8的能带结构、电子态密度和光学特性。能带结果显示Zn_3V_2O_8呈间接带隙的绝缘体型能带,其禁带宽度为2.9 e V。详细的电子态密度结果显示其费米面上的态密度达到20 e/e V,费米能级附近的能级由Zn3p、V3p和O2p电子形成,Zn3d和O2s之间有强的杂化作用。介电性能结果显示在4.4~5.7 e V附近有强的吸收峰,在20.6 e V附近有一个次强吸收峰;吸收光谱显示在6.8 e V处有强吸收,在20.7 e V处有一个较弱的吸收峰。
文摘A novel compound Ni(phen)(H2O)(V2O6) has been hydrothermally synthesized and structurally determined to be a two-dimensional compound, which contains {V2O6}n2n- chains interconnected by nickel(II) complexes via oxygen atoms. The crystallographic data measured by single-crystal X-ray diffraction analysis are as follows: C12H10N2NiO7V2, Mr=454.81, monoclinic, space group P21 / c, a=0.784 6(3), b=2.103 6(8), c=0.942 3(4) nm, β=112.872(5)°, V=1.433 0(10) nm3, Z=4, Dc=2.104 Mg·m-3, μ(Mo Kα)=2.615 mm-1, F(000)=904, T=298(2) K, 4 480 reflections collected, 2 470 independent (Rint=0.032 2), the final R=0.058 4 and wR2=0.145 7 for 2 303 observed reflections with I>2σ(I). CCDC: 192520.
文摘A new complex[Ni(en) 2V 6O 14] n was hydrothermally synthesized and characterized by 2-dimensional vanadium oxide framework pillared by Ni(en) 2 group. Single crystal X-ray analysis indicates that this compound crystallizes in monoclinic system, space group P2 1/c with a= 0.892 17(18) nm, b= 1.711 1(3) nm, c=0.662 73(13) nm, β=111.58(3)°, V=0.940 8(3) nm 3, Z=2, D c= 2.501 g/cm 3, R=0.042 3, wR=0.060 9, S=1.006.