The ultrasonic wedge bonding with d25 μm copper wire was achieved on Au/Ni plated Cu substrate at ambient temperature.Ultrasonic wedge bonding mechanism was investigated by using SEM/EDX,pull test,shear test and micr...The ultrasonic wedge bonding with d25 μm copper wire was achieved on Au/Ni plated Cu substrate at ambient temperature.Ultrasonic wedge bonding mechanism was investigated by using SEM/EDX,pull test,shear test and microhardness test.The results show that the thinning of the Au layer occurs directly below the center of the bonding tool with the bonding power increasing.The interdiffusion between copper wire and Au metallization during the wedge bonding is assumed negligible,and the wedge bonding is achieved by wear action induced by ultrasonic vibration.The ultrasonic power contributes to enhance the deformation of copper wire due to ultrasonic softening effect which is then followed by the strain hardening of the copper wedge bonding.展开更多
The rock-breaking mechanism and effect of confined blasting were analysed by blasting and impact dynamic mechanics, fluid dynamic mechanics, fracture mechanics as well as blasting experiment. The results showed that t...The rock-breaking mechanism and effect of confined blasting were analysed by blasting and impact dynamic mechanics, fluid dynamic mechanics, fracture mechanics as well as blasting experiment. The results showed that the fracturing of surrounding rock in confined blasting condition is the result of coaction of rock pre-cracking by shock wave and stress wave and the continuing expanding crackenhancement of confined medium, and the model of crack development of borehole surrounding rock in confined blasting condition was established. This study acquired the damage range of surrounding rock under the action of shock wave and stress wave, as well as the crack development characteristics of surrounding rock after the wedge-in confined medium into the crack space. Deep-hole confined blasting experiment on large rock showed that the high-efficient utilisation of in-hole explosive was achieved and the safety of rock blasting operation was ensured. Safe static rock-breaking under the action of high-efficient explosive blasting was achieved as well as the unification of super dynamic load of explosive blasting and static rock-breaking of water medium.展开更多
基金Prpject(E052104/50705021)supported by the National Natural Science Foundation of ChinaProject(2006:01504489)supported by the Development Program for Outstanding Young Teachers in HIT
文摘The ultrasonic wedge bonding with d25 μm copper wire was achieved on Au/Ni plated Cu substrate at ambient temperature.Ultrasonic wedge bonding mechanism was investigated by using SEM/EDX,pull test,shear test and microhardness test.The results show that the thinning of the Au layer occurs directly below the center of the bonding tool with the bonding power increasing.The interdiffusion between copper wire and Au metallization during the wedge bonding is assumed negligible,and the wedge bonding is achieved by wear action induced by ultrasonic vibration.The ultrasonic power contributes to enhance the deformation of copper wire due to ultrasonic softening effect which is then followed by the strain hardening of the copper wedge bonding.
基金supported by the National Natural Science Foundation(Nos.51574220,51604262)the Foundation Research Project of Jiangsu Province(No.BK20160256)+1 种基金the Postdoctoral Science Foundation(No.2015M581896)the Postdoctoral Science Foundation Project of Jiangsu Province(No.1601212C)
文摘The rock-breaking mechanism and effect of confined blasting were analysed by blasting and impact dynamic mechanics, fluid dynamic mechanics, fracture mechanics as well as blasting experiment. The results showed that the fracturing of surrounding rock in confined blasting condition is the result of coaction of rock pre-cracking by shock wave and stress wave and the continuing expanding crackenhancement of confined medium, and the model of crack development of borehole surrounding rock in confined blasting condition was established. This study acquired the damage range of surrounding rock under the action of shock wave and stress wave, as well as the crack development characteristics of surrounding rock after the wedge-in confined medium into the crack space. Deep-hole confined blasting experiment on large rock showed that the high-efficient utilisation of in-hole explosive was achieved and the safety of rock blasting operation was ensured. Safe static rock-breaking under the action of high-efficient explosive blasting was achieved as well as the unification of super dynamic load of explosive blasting and static rock-breaking of water medium.