Mixed mode Ⅰ/Ⅱ fracture erperiments of LC4-CS aluminum alloy were conductedby using tension--shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracturemechanisms of thickness effect on mixed mode Ⅰ/Ⅱ fracture ...Mixed mode Ⅰ/Ⅱ fracture erperiments of LC4-CS aluminum alloy were conductedby using tension--shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracturemechanisms of thickness effect on mixed mode Ⅰ/Ⅱ fracture were first examined fromfracture surface morphology to correlate with the macroscopic fracture behavior andstress state. It is found that specimen thickness has a strong influence on mixed modefracture. As thickness varies from thin to thick the macroscopic fracture surfacesappear the characteristics of plane stress state (2mm, 4mm--thick specimen), three--dimensional stress state (8mm--thick specimens), and plane strain state (14mm--thickspecimens), respectively. The specimens of all kinds of thicknesses are typical of ten-sile type failure under mode Ⅰ loading condition and shear type failure under mode Ⅱloading condition. Two distinct features coexist on the fracture surfaces under mixedmode loading conditions, and the corresponding proportion varies with loading mix-ity. Void--growth processes are the failure mechanism in both predominately tensile-and shears--type fractures. The size and depth of dimples on the fracture surface varygreatly with thickness. Therefore, it is extraordinary necessary to take into accountthe thickness effect when a mixed mode fracture criterion is being established.展开更多
Hydrogen induced cracking(HIC)of 0.3% C,1% Cr,1% Mn,1% Si high strength steel has been studied under simple mode Ⅰ,mode Ⅱ and(Ⅰ+Ⅱ)mixed mode loading conditions.Af- ter being hydrogen-charged in IN H_2SO_4 solution...Hydrogen induced cracking(HIC)of 0.3% C,1% Cr,1% Mn,1% Si high strength steel has been studied under simple mode Ⅰ,mode Ⅱ and(Ⅰ+Ⅱ)mixed mode loading conditions.Af- ter being hydrogen-charged in IN H_2SO_4 solution,the material behaved hydrogen embrittlement in all the cases studied.The threshold K_(ⅡH)/K_(ⅡX) of HIC under mode Ⅱ load- ing was 0.27,which was nearly the same as that K(ⅠH)/K_(ⅠX)=0.29 under mode Ⅰ loading. While the thresholds of-HIC under(Ⅰ+Ⅱ)mixed mode loading were 0.36,0.41 and 0.37 cor- responding to the K_Ⅱ/K_Ⅰ ratio of 0.27,0.4 and O.81.The results show that simple mode Ⅰ or mode Ⅱ loading is more susceptible to hydrogen embrittlement than(Ⅰ+Ⅱ)mixed mode. For explaining the experimental results,the effects of triaxial stress as well as plastic deformation ahead of crack tip has been discussed.展开更多
Ⅰn recent years,the issue of aircraft icing has gained widespread recognition.The breaking and detachment of dynamic ice can pose a threat to flight safety.However,the shedding and fracture mechanisms of dynamic ice ...Ⅰn recent years,the issue of aircraft icing has gained widespread recognition.The breaking and detachment of dynamic ice can pose a threat to flight safety.However,the shedding and fracture mechanisms of dynamic ice are unclear and cannot meet the engineering needs of ice-shedding hazard assessment.Therefore,studying the fracture toughness of ice bodies has extremely important practical significance.To address this issue,this article uses a centrally cracked Brazilian disk(CCBD)specimen to measure the pure mode Ⅰ toughness and pure mode Ⅱ fracture toughness of freshwater ice at different loading rates.The mixed-mode(Ⅰ–Ⅱ)fracture characteristics of ice are discussed,and the experimental results are compared and analyzed with the theoretical values of the generalized maximum tangential stress(GMTS)criterion considering the influence of T-stress.The results indicated that as the loading rate increases,the pure mode Ⅰ toughness and pure mode Ⅱ fracture toughness of freshwater ice decrease,and the fracture toughness of freshwater ice is more sensitive to the loading rate.Ⅰn terms of fracture criteria,the theoretical value of the ratio of pure mode Ⅱ fracture toughness to pure mode Ⅰ fracture toughness based on the GMTS criterion is in good agreement with the experimental value,while the theoretical value based on the maximum tangential stress(MTS)criterion deviates significantly from the experimental value,indicating that the GMTS criterion considering the influence of T-stress can better predict the experimental results.展开更多
It is obtained in this paper that the fatigue threshold value of mode H was 1.9 times of that of mode Ⅰ in dual-phase steel(DPS),and the normal stress intensity factor range oJ mode Ⅱ branch crack tip was 2.2 times ...It is obtained in this paper that the fatigue threshold value of mode H was 1.9 times of that of mode Ⅰ in dual-phase steel(DPS),and the normal stress intensity factor range oJ mode Ⅱ branch crack tip was 2.2 times of that of mode Ⅰ.Above results illustrate that the resistance of mode Ⅱ crack growth was higher than that of mode Ⅰ,the former resulting from roughness-induced shear resistance,the latter,crack closure. The mode Ⅱ component can play two important roles in near-threshold fatigue crack growth:(1)increasing crack tip plasticity which accelerates the crack growth and(2)intro- ducing crack surface contact and rubbing to reduce the crack propagation rate.By means of crack closure,the quantity of shear resistance was easily solved in this paper.The friction shear stress strength factor range of mode Ⅱ,K_,is still much higher than the closure stress strength factor range of mode Ⅰ,K_(Ⅰ,cl).This illustrated that the roughness enlarged the second role and played a role of shielding crack tip from mode Ⅱ crack.展开更多
文摘Mixed mode Ⅰ/Ⅱ fracture erperiments of LC4-CS aluminum alloy were conductedby using tension--shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracturemechanisms of thickness effect on mixed mode Ⅰ/Ⅱ fracture were first examined fromfracture surface morphology to correlate with the macroscopic fracture behavior andstress state. It is found that specimen thickness has a strong influence on mixed modefracture. As thickness varies from thin to thick the macroscopic fracture surfacesappear the characteristics of plane stress state (2mm, 4mm--thick specimen), three--dimensional stress state (8mm--thick specimens), and plane strain state (14mm--thickspecimens), respectively. The specimens of all kinds of thicknesses are typical of ten-sile type failure under mode Ⅰ loading condition and shear type failure under mode Ⅱloading condition. Two distinct features coexist on the fracture surfaces under mixedmode loading conditions, and the corresponding proportion varies with loading mix-ity. Void--growth processes are the failure mechanism in both predominately tensile-and shears--type fractures. The size and depth of dimples on the fracture surface varygreatly with thickness. Therefore, it is extraordinary necessary to take into accountthe thickness effect when a mixed mode fracture criterion is being established.
文摘Hydrogen induced cracking(HIC)of 0.3% C,1% Cr,1% Mn,1% Si high strength steel has been studied under simple mode Ⅰ,mode Ⅱ and(Ⅰ+Ⅱ)mixed mode loading conditions.Af- ter being hydrogen-charged in IN H_2SO_4 solution,the material behaved hydrogen embrittlement in all the cases studied.The threshold K_(ⅡH)/K_(ⅡX) of HIC under mode Ⅱ load- ing was 0.27,which was nearly the same as that K(ⅠH)/K_(ⅠX)=0.29 under mode Ⅰ loading. While the thresholds of-HIC under(Ⅰ+Ⅱ)mixed mode loading were 0.36,0.41 and 0.37 cor- responding to the K_Ⅱ/K_Ⅰ ratio of 0.27,0.4 and O.81.The results show that simple mode Ⅰ or mode Ⅱ loading is more susceptible to hydrogen embrittlement than(Ⅰ+Ⅱ)mixed mode. For explaining the experimental results,the effects of triaxial stress as well as plastic deformation ahead of crack tip has been discussed.
基金supported by the National Natural Science Foundation of China(Nos.12132019 and 11872042)the Open Fund for Key Laboratory of Deep Underground Science and Engineering of Ministry of Education(No.DESEYU202301)+1 种基金the 2023 Open Project of Failure Mechanics and Engineering Disaster Prevention,Key Lab of Sichuan Province(No.FMEDP202306)the Natural Science Foundation of Sichuan Province(No.2023NSFSC0043).
文摘Ⅰn recent years,the issue of aircraft icing has gained widespread recognition.The breaking and detachment of dynamic ice can pose a threat to flight safety.However,the shedding and fracture mechanisms of dynamic ice are unclear and cannot meet the engineering needs of ice-shedding hazard assessment.Therefore,studying the fracture toughness of ice bodies has extremely important practical significance.To address this issue,this article uses a centrally cracked Brazilian disk(CCBD)specimen to measure the pure mode Ⅰ toughness and pure mode Ⅱ fracture toughness of freshwater ice at different loading rates.The mixed-mode(Ⅰ–Ⅱ)fracture characteristics of ice are discussed,and the experimental results are compared and analyzed with the theoretical values of the generalized maximum tangential stress(GMTS)criterion considering the influence of T-stress.The results indicated that as the loading rate increases,the pure mode Ⅰ toughness and pure mode Ⅱ fracture toughness of freshwater ice decrease,and the fracture toughness of freshwater ice is more sensitive to the loading rate.Ⅰn terms of fracture criteria,the theoretical value of the ratio of pure mode Ⅱ fracture toughness to pure mode Ⅰ fracture toughness based on the GMTS criterion is in good agreement with the experimental value,while the theoretical value based on the maximum tangential stress(MTS)criterion deviates significantly from the experimental value,indicating that the GMTS criterion considering the influence of T-stress can better predict the experimental results.
文摘It is obtained in this paper that the fatigue threshold value of mode H was 1.9 times of that of mode Ⅰ in dual-phase steel(DPS),and the normal stress intensity factor range oJ mode Ⅱ branch crack tip was 2.2 times of that of mode Ⅰ.Above results illustrate that the resistance of mode Ⅱ crack growth was higher than that of mode Ⅰ,the former resulting from roughness-induced shear resistance,the latter,crack closure. The mode Ⅱ component can play two important roles in near-threshold fatigue crack growth:(1)increasing crack tip plasticity which accelerates the crack growth and(2)intro- ducing crack surface contact and rubbing to reduce the crack propagation rate.By means of crack closure,the quantity of shear resistance was easily solved in this paper.The friction shear stress strength factor range of mode Ⅱ,K_,is still much higher than the closure stress strength factor range of mode Ⅰ,K_(Ⅰ,cl).This illustrated that the roughness enlarged the second role and played a role of shielding crack tip from mode Ⅱ crack.