To reveal the drop failure modes of the wafer level chip scale packages （WLCSPs） with Sn-3.0Ag-0.5Cu solder joints, board level drop tests were performed according to the JEDEC standard. Six failure modes were iden...To reveal the drop failure modes of the wafer level chip scale packages （WLCSPs） with Sn-3.0Ag-0.5Cu solder joints, board level drop tests were performed according to the JEDEC standard. Six failure modes were identified, i.e., short FR-4 cracks and complete FR-4 cracks at the printing circuit board （PCB） side, split between redistribution layer （RDL） and Cu under bump metallization （UBM）, RDL fracture, bulk cracks and partial bulk and intermetallic compound （IMC） cracks at the chip side. For the outmost solder joints, complete FR-4 cracks tended to occur, due to large deformation of PCB and low strength of FR-4 dielectric layer. The formation of complete FR-4 cracks largely absorbed the impact energy, resulting in the absence of other failure modes. For the inner solder joints, the absorption of impact energy by the short FR-4 cracks was limited, resulting in other failure modes at the chip side.展开更多
Through carefully reading and studying the emotional crisis of Holden in The catcher in the rye, the main character＇s anxiety, isolation, bewilderment in the crisis of existence and his efforts to identify himself in...Through carefully reading and studying the emotional crisis of Holden in The catcher in the rye, the main character＇s anxiety, isolation, bewilderment in the crisis of existence and his efforts to identify himself in the dilemma are interpreted. His experience exemplifies the plight experienced by the postwar generation and provides a good text from which one can study the American society and culture in 1950s.展开更多
基金Projects(51475072,51171036)supported by the National Natural Science Foundation of China
文摘To reveal the drop failure modes of the wafer level chip scale packages （WLCSPs） with Sn-3.0Ag-0.5Cu solder joints, board level drop tests were performed according to the JEDEC standard. Six failure modes were identified, i.e., short FR-4 cracks and complete FR-4 cracks at the printing circuit board （PCB） side, split between redistribution layer （RDL） and Cu under bump metallization （UBM）, RDL fracture, bulk cracks and partial bulk and intermetallic compound （IMC） cracks at the chip side. For the outmost solder joints, complete FR-4 cracks tended to occur, due to large deformation of PCB and low strength of FR-4 dielectric layer. The formation of complete FR-4 cracks largely absorbed the impact energy, resulting in the absence of other failure modes. For the inner solder joints, the absorption of impact energy by the short FR-4 cracks was limited, resulting in other failure modes at the chip side.
文摘Through carefully reading and studying the emotional crisis of Holden in The catcher in the rye, the main character＇s anxiety, isolation, bewilderment in the crisis of existence and his efforts to identify himself in the dilemma are interpreted. His experience exemplifies the plight experienced by the postwar generation and provides a good text from which one can study the American society and culture in 1950s.