The catalytic effects of single and mixed catalysts, i.e. single 3%Ca and 5%Na-BL（black liquor） catalysts and mixed 3%Ca＋5%Na-BL catalyst, on carbon conversion, gasification reaction rate constant and activation en...The catalytic effects of single and mixed catalysts, i.e. single 3%Ca and 5%Na-BL（black liquor） catalysts and mixed 3%Ca＋5%Na-BL catalyst, on carbon conversion, gasification reaction rate constant and activation energy, relative amount of harmful pollutant like sulphur containing gases have been investigated by thermogravimetry in steam gasification under temperature 750℃ to 950℃ at ambient pressure for three high-metarnorphous anthracites （Longyan, Fenghai and Youxia coals in Fujian Province）. The mixed catalyst of 3%Ca＋5%Na-BL increases greatly the carbon conversion and gasification rate constant by accelerating the gasification reaction C＋H2O→CO＋H2 due to presence of alkali surfacecompounds [COM], [CO2M] and exchanged calcium phenolate and calcium carboxylate （-COO）2. By adding CaCO3 into BL catalyst in gasification, in addition to improving the catalyst function and enhancing the carbon conversion, the effective desulphurization is also achieved, but the better operating temperature should be below 900℃. The homogenous and shrinking core models can be successfully employed to correlate the relations between the conversion and the gasification .time .and to estimate the reaction rate constant, The reaction acUvaUon energy and pre-exponential factor are estimated and the activation energy for mixed catalyst is in a range of 98.72-166.92 kJ·mol^-1, much less than 177.50-196.46 kJ·mol^-1 for non-catalytic steam gasification for three experimental coals.展开更多
CO2 gasification of Fuijian high-metamorphous anthracite with black liquor （BL） and/or mixture of BL and calcium stuff （BL＋Ca） as catalyst was studied by using a thermogravimetry under 750-950℃ at ambient pressu...CO2 gasification of Fuijian high-metamorphous anthracite with black liquor （BL） and/or mixture of BL and calcium stuff （BL＋Ca） as catalyst was studied by using a thermogravimetry under 750-950℃ at ambient pressure. When the coal was impregnated with an appropriate quantity of Ca and BL mixture, the catalytic activity of CO2 gasification was enhanced obviously. With a loading of 8%Na-BL＋2%Ca, the carbon conversion of three coal samples tested reaches up to 92.9%-99.3% at 950℃ within 30min. The continuous formation of alkali surface compounds such as （[-COM], [-CO2M]） and the presence of exchanged Ca, such as calcium phenolate and calcium carboxylates （COO）2Ca, contribute to the increase in catalytic efficiency, and using BL＋Ca is more efficient than that adding BL only, The homogeneous model and shrinking-core model were applied to correlate the data of conversion with time and to estimate the reaction rate constants under different temperature. The corresponding reaction activation energy （Ea） and pre-exponential factor of three anthracites were estimated. It is found that Ea is in the range from 73.6 to 121.4kJ·mol^-1 in the case of BL＋Ca, and 74.3 to 104.2kJ·mol^-1 when only BL was used as the catalyst, both of which are much less than that from 143.5 to 181.4kJ·mol^-1 if no catalyst used. It is clearly demonstrated that both of BL＋Ca mixture and BL could be the source of cheap and effective catalyst for coal gasification.展开更多
Adhesive for bamboo plywood prepared directly using lignin existing in the black liquor as a kind of material replacing phenol was proposed on the basis of the same structural properties of lignin and phenol. The resu...Adhesive for bamboo plywood prepared directly using lignin existing in the black liquor as a kind of material replacing phenol was proposed on the basis of the same structural properties of lignin and phenol. The results indicate that the reaction time of black liquor methylating is 30min, when the ratio of alkali to formaldehyde is controlled at approximately 0.20, decomposition rate of formaldehyde is the lowest and the effect of black liquor methylating is the best, the optimal molar ratio of phenol： formaldehyde to NaOH to H2O of preparing phenolic resin is 1.00 ： 1.50 ： 0.50 ： 9.00, and the suitable viscosity is 27 - 30 Pa· s. At different mass ratios of methylated black liquor to phenolic resin, all terms of performance of black liquor phenolic resin are excellent and satisfy the requirement. All terms of performance of bamboo plywood prepared using this technique are hetter than that of excellent bamboo plywood of national criteria. Using this technique, the cost is depressed by 28.69% without altering the traditional adhesive producing technique flow, and without using additional equipment.展开更多
基金Supported by the National Natural Science Foundation of China （20376014） and Fujian Science and Technology Council Grant （HG99-01 ）.
文摘The catalytic effects of single and mixed catalysts, i.e. single 3%Ca and 5%Na-BL（black liquor） catalysts and mixed 3%Ca＋5%Na-BL catalyst, on carbon conversion, gasification reaction rate constant and activation energy, relative amount of harmful pollutant like sulphur containing gases have been investigated by thermogravimetry in steam gasification under temperature 750℃ to 950℃ at ambient pressure for three high-metarnorphous anthracites （Longyan, Fenghai and Youxia coals in Fujian Province）. The mixed catalyst of 3%Ca＋5%Na-BL increases greatly the carbon conversion and gasification rate constant by accelerating the gasification reaction C＋H2O→CO＋H2 due to presence of alkali surfacecompounds [COM], [CO2M] and exchanged calcium phenolate and calcium carboxylate （-COO）2. By adding CaCO3 into BL catalyst in gasification, in addition to improving the catalyst function and enhancing the carbon conversion, the effective desulphurization is also achieved, but the better operating temperature should be below 900℃. The homogenous and shrinking core models can be successfully employed to correlate the relations between the conversion and the gasification .time .and to estimate the reaction rate constant, The reaction acUvaUon energy and pre-exponential factor are estimated and the activation energy for mixed catalyst is in a range of 98.72-166.92 kJ·mol^-1, much less than 177.50-196.46 kJ·mol^-1 for non-catalytic steam gasification for three experimental coals.
基金Supported by the National Natural Science Foundation of China （No.20376014） and Fujian Science and Technology Council Grant （HG99-01）.
文摘CO2 gasification of Fuijian high-metamorphous anthracite with black liquor （BL） and/or mixture of BL and calcium stuff （BL＋Ca） as catalyst was studied by using a thermogravimetry under 750-950℃ at ambient pressure. When the coal was impregnated with an appropriate quantity of Ca and BL mixture, the catalytic activity of CO2 gasification was enhanced obviously. With a loading of 8%Na-BL＋2%Ca, the carbon conversion of three coal samples tested reaches up to 92.9%-99.3% at 950℃ within 30min. The continuous formation of alkali surface compounds such as （[-COM], [-CO2M]） and the presence of exchanged Ca, such as calcium phenolate and calcium carboxylates （COO）2Ca, contribute to the increase in catalytic efficiency, and using BL＋Ca is more efficient than that adding BL only, The homogeneous model and shrinking-core model were applied to correlate the data of conversion with time and to estimate the reaction rate constants under different temperature. The corresponding reaction activation energy （Ea） and pre-exponential factor of three anthracites were estimated. It is found that Ea is in the range from 73.6 to 121.4kJ·mol^-1 in the case of BL＋Ca, and 74.3 to 104.2kJ·mol^-1 when only BL was used as the catalyst, both of which are much less than that from 143.5 to 181.4kJ·mol^-1 if no catalyst used. It is clearly demonstrated that both of BL＋Ca mixture and BL could be the source of cheap and effective catalyst for coal gasification.
文摘Adhesive for bamboo plywood prepared directly using lignin existing in the black liquor as a kind of material replacing phenol was proposed on the basis of the same structural properties of lignin and phenol. The results indicate that the reaction time of black liquor methylating is 30min, when the ratio of alkali to formaldehyde is controlled at approximately 0.20, decomposition rate of formaldehyde is the lowest and the effect of black liquor methylating is the best, the optimal molar ratio of phenol： formaldehyde to NaOH to H2O of preparing phenolic resin is 1.00 ： 1.50 ： 0.50 ： 9.00, and the suitable viscosity is 27 - 30 Pa· s. At different mass ratios of methylated black liquor to phenolic resin, all terms of performance of black liquor phenolic resin are excellent and satisfy the requirement. All terms of performance of bamboo plywood prepared using this technique are hetter than that of excellent bamboo plywood of national criteria. Using this technique, the cost is depressed by 28.69% without altering the traditional adhesive producing technique flow, and without using additional equipment.