TiO2/γ-Al2O3 supported In/Ag catalysts were prepared by impregnation method,and investigated for NO reduction with CO as the reducing agent under lean burn conditions.The microscopic structure and surface properties ...TiO2/γ-Al2O3 supported In/Ag catalysts were prepared by impregnation method,and investigated for NO reduction with CO as the reducing agent under lean burn conditions.The microscopic structure and surface properties of the catalysts were studied by N2 adsorption-desorption,X-ray diffraction,transmission electron microscopy,X-ray photoelectron spectroscopy,ultraviolet-visible spectroscopy,H2 temperature-programmed reduction and Fourier transform infrared spectroscopy.TiO2/γ-Al2O3 supported In/Ag is a good catalyst for the reduction of NO to N2.It displayed high dispersion,large amounts of surface active components and high NO adsorption capacity,which gave good catalytic performance and stability for the reduction of NO with CO under lean burn conditions.The silver species stabilized and improved the dispersion of the indium species.The introduction of TiO2 into the γ-Al2O3 support promoted NO adsorption and improved the dispersion of the indium species and silver species.展开更多
The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. Acco...The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.展开更多
A series of copper manganese oxides were prepared using a selective etching technique with various amounts of ammonia added during the co-precipitation process. The effect of the ammonia etching on the structure and c...A series of copper manganese oxides were prepared using a selective etching technique with various amounts of ammonia added during the co-precipitation process. The effect of the ammonia etching on the structure and catalytic properties of the copper manganese oxides was investigated using elemental analysis, nitrogen physisorption, X-ray powder diffraction, scanning and transmission electron microscopy, X-ray photoelectron spectroscopy, H2 temperature-programmed reduc- tion, and Oz temperature-programmed desorption combined with catalytic oxidation of CO. It was found that ammonia can selectively remove copper species from the copper manganese oxides, which correspondingly generates more defects in these oxides. An oxygen spillover from the man- ganese to the copper species was observed by H2 temperature-programmed desorption, indicating that ammonia etching enhanced the mobility of lattice oxygen species in these oxides. The Oz tem- perature-programmed desorption measurements further revealed that ammonia etching improved the ability of these oxides to release lattice oxygen. The improvement in redox properties of the copper manganese oxides following ammonia etching was associated with enhanced catalytic performance for CO oxidation.展开更多
Two homogeneous photoelectrocatalytic systems composed of simple polypyridyl Co complexes[Co(tpy)2](PF6)2and[Co(bpy)3](PF6)2as electrocatalysts and a Si wafer as the photoelectrode were used for combined photoelectroc...Two homogeneous photoelectrocatalytic systems composed of simple polypyridyl Co complexes[Co(tpy)2](PF6)2and[Co(bpy)3](PF6)2as electrocatalysts and a Si wafer as the photoelectrode were used for combined photoelectrochemical reduction of CO2to CO.A high photocurrent density of1.4mA/cm2was observed for the system with the[Co(tpy)2](PF6)2catalyst and a photovoltage of400mV was generated.Faradaic efficiencies of CO were optimized to83%and94%for the[Co(tpy)2](PF6)2and[Co(bpy)3](PF6)2complexes,respectively,in acetonitrile solution with10%methanol(volume fraction,same below)as a protic additive.Addition of2%water volume fraction induced a large amount of non‐specific H2evolution by the Si photoelectrode.展开更多
Nitrogen doping of activated carbon loading Fe2O3 was performed by annealing in ammonia, and the activity of the modified carbon for NO reduction was studied in the presence of oxygen. Results show that Fe2O3 enhances...Nitrogen doping of activated carbon loading Fe2O3 was performed by annealing in ammonia, and the activity of the modified carbon for NO reduction was studied in the presence of oxygen. Results show that Fe2O3 enhances the amount of surface oxygen complexes and facilitates nitrogen incorporation in the carbon, especially in the form of pyridinic nitrogen. The modified carbon shows excellent activity for NO reduction in the low temperature regime （〈500℃） because of the cooperative effect of Fe2O3 and the surface nitrogen species.展开更多
A series of reduction experiments of iron ore pellets with hydrogen,carbon monoxide and their mixture were carried out in a laboratory scale shaft furnace.The sticking behavior accompanying reduction of iron ore pelle...A series of reduction experiments of iron ore pellets with hydrogen,carbon monoxide and their mixture were carried out in a laboratory scale shaft furnace.The sticking behavior accompanying reduction of iron ore pellets was investigated.And morphology of the sticking interface forming during reduction was analyzed by SEM equipped with EDS.In order to evaluate the effects of the temperature and gas composition on sticking properties,reduction of iron ore pellets were conducted at 800-1000 ℃.The results show that the sticking strength of the pellets increases with temperature,however,decreases with hydrogen content in reducing gas.For an efficient shaft furnace operation in direct reduction(DR),relative prevention of sticking such as coating of pellets was also developed to solve sticking problem.The results show that CaO is a suitable material for the coating method.展开更多
基金supported by the National Science & Technology Pillar Program(2012BAF03B02)National Natural Science Foundation of China(21101085,U1162203)+3 种基金Natural Science Foundation of Liaoning Province(2015020196)Doctoral Fund of Shandong Province(BS2015HZ003)Fushun Science & Technology Program(FSKJHT 201423)Liaoning Excellent Talents Program in University(LJQ2012031)~~
文摘TiO2/γ-Al2O3 supported In/Ag catalysts were prepared by impregnation method,and investigated for NO reduction with CO as the reducing agent under lean burn conditions.The microscopic structure and surface properties of the catalysts were studied by N2 adsorption-desorption,X-ray diffraction,transmission electron microscopy,X-ray photoelectron spectroscopy,ultraviolet-visible spectroscopy,H2 temperature-programmed reduction and Fourier transform infrared spectroscopy.TiO2/γ-Al2O3 supported In/Ag is a good catalyst for the reduction of NO to N2.It displayed high dispersion,large amounts of surface active components and high NO adsorption capacity,which gave good catalytic performance and stability for the reduction of NO with CO under lean burn conditions.The silver species stabilized and improved the dispersion of the indium species.The introduction of TiO2 into the γ-Al2O3 support promoted NO adsorption and improved the dispersion of the indium species and silver species.
文摘The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.
基金supported by the National Basic Research Program of China (973 Program,2013CB934104)the China Postdoctoral Science Foundation(2014M560202)~~
文摘A series of copper manganese oxides were prepared using a selective etching technique with various amounts of ammonia added during the co-precipitation process. The effect of the ammonia etching on the structure and catalytic properties of the copper manganese oxides was investigated using elemental analysis, nitrogen physisorption, X-ray powder diffraction, scanning and transmission electron microscopy, X-ray photoelectron spectroscopy, H2 temperature-programmed reduc- tion, and Oz temperature-programmed desorption combined with catalytic oxidation of CO. It was found that ammonia can selectively remove copper species from the copper manganese oxides, which correspondingly generates more defects in these oxides. An oxygen spillover from the man- ganese to the copper species was observed by H2 temperature-programmed desorption, indicating that ammonia etching enhanced the mobility of lattice oxygen species in these oxides. The Oz tem- perature-programmed desorption measurements further revealed that ammonia etching improved the ability of these oxides to release lattice oxygen. The improvement in redox properties of the copper manganese oxides following ammonia etching was associated with enhanced catalytic performance for CO oxidation.
基金supported by the National Key R&D Program of China (2016YFB0600901)the Strategic Priority Research Program of the Chinese Academy of Sciences (XDB17030300)~~
文摘Two homogeneous photoelectrocatalytic systems composed of simple polypyridyl Co complexes[Co(tpy)2](PF6)2and[Co(bpy)3](PF6)2as electrocatalysts and a Si wafer as the photoelectrode were used for combined photoelectrochemical reduction of CO2to CO.A high photocurrent density of1.4mA/cm2was observed for the system with the[Co(tpy)2](PF6)2catalyst and a photovoltage of400mV was generated.Faradaic efficiencies of CO were optimized to83%and94%for the[Co(tpy)2](PF6)2and[Co(bpy)3](PF6)2complexes,respectively,in acetonitrile solution with10%methanol(volume fraction,same below)as a protic additive.Addition of2%water volume fraction induced a large amount of non‐specific H2evolution by the Si photoelectrode.
文摘Nitrogen doping of activated carbon loading Fe2O3 was performed by annealing in ammonia, and the activity of the modified carbon for NO reduction was studied in the presence of oxygen. Results show that Fe2O3 enhances the amount of surface oxygen complexes and facilitates nitrogen incorporation in the carbon, especially in the form of pyridinic nitrogen. The modified carbon shows excellent activity for NO reduction in the low temperature regime （〈500℃） because of the cooperative effect of Fe2O3 and the surface nitrogen species.
基金Project(50725416)supported by the National Natural Science Foundation for Distinguished Young Scholars of China
文摘A series of reduction experiments of iron ore pellets with hydrogen,carbon monoxide and their mixture were carried out in a laboratory scale shaft furnace.The sticking behavior accompanying reduction of iron ore pellets was investigated.And morphology of the sticking interface forming during reduction was analyzed by SEM equipped with EDS.In order to evaluate the effects of the temperature and gas composition on sticking properties,reduction of iron ore pellets were conducted at 800-1000 ℃.The results show that the sticking strength of the pellets increases with temperature,however,decreases with hydrogen content in reducing gas.For an efficient shaft furnace operation in direct reduction(DR),relative prevention of sticking such as coating of pellets was also developed to solve sticking problem.The results show that CaO is a suitable material for the coating method.