Four isothermal sections at 298.15K,308.15K,318.15K and 328.15K in system water-n-hexane-ethanol were measured by gas chromatograph method.The innerscaling method was used to determine the concentrations of n-hexane a...Four isothermal sections at 298.15K,308.15K,318.15K and 328.15K in system water-n-hexane-ethanol were measured by gas chromatograph method.The innerscaling method was used to determine the concentrations of n-hexane and ethanol in this ternary system.Ethy1 acetate was chosen as the sample of inner-scaling because of its separability and fit retainning time.Acetylacetone was chosen as diluent of the oil phase andn-butyl alcohol was chosen as diluent of the water phase.The experimental data of four isothermal sections at 298.15K,308.15K,318.15K adn 328.15K in system water-n-hexane-ethanol at normal pressure were given.Four schematic figures were also given.The character of these phase diagrams was analysed.They were compared with the phase diagram of system water-n-hexane-methanol.The possible causes of experimental error were discussed.The root mean square error of measurement is 1.47%.展开更多
An isothermal section of the Mg-Nd-Gd ternary system at 723 K was established by diffusion triple technique and electron probe microanalysis （EPMA）. Mg3Gd and Mg3Nd form a continuous solid solution （Gd,Nd）3Mg, and...An isothermal section of the Mg-Nd-Gd ternary system at 723 K was established by diffusion triple technique and electron probe microanalysis （EPMA）. Mg3Gd and Mg3Nd form a continuous solid solution （Gd,Nd）3Mg, and a continuous solid solution （Gd,Nd）Mg is also formed between MgGd and MgNd. Mg7Gd, Mg5Gd, Mg2Gd, Mg41Nd5, （Gd,Nd）3Mg and （Gd,Nd）Mg are found in the ternary system. In these intermetallic phases, Mg7Gd has been reported to be a metastable phase in previous literatures. The solubilities of Mg, Gd and Nd in all the phases were detected. Furthermore, four three-phase equilibria, α（Mg）＋Mg7Gd＋Mg41Nd5, Mg7Gd＋Mg5Gd＋Mg41Nd5, Mg5Gd＋Mg41Nd5＋（Gd,Nd）3Mg and （Gd,Nd）3Mg＋（Gd,Nd）Mg＋Mg2Gd, were identified in the isothermal section.展开更多
Phase diagrams of two isothermal sections of the Ni-Ti-Ta ternary system at 1000 and 1200℃in a full composition range were determined by X-ray diffraction and electron probe microanalysis.The experimental results ind...Phase diagrams of two isothermal sections of the Ni-Ti-Ta ternary system at 1000 and 1200℃in a full composition range were determined by X-ray diffraction and electron probe microanalysis.The experimental results indicated a ternary compoundτphase with low solid solubility and composition ranges of(16.3-22.4)at.%Ta,(15.9-24.1)at.%Ti and(58.5-60.0)at.%Ni at 1000℃.The two terminal solid solutions(bcc-(Ta)andβ-Ti)formed a continuous solid solution at 1000 and 1200℃.A certain amount of Ti can dissolve into Ni-Ta intermetallic compounds near the Ni-Ta side,with the highest value of 21.9 at.%observed in the Ni;Ta compound at 1000℃.展开更多
文摘Four isothermal sections at 298.15K,308.15K,318.15K and 328.15K in system water-n-hexane-ethanol were measured by gas chromatograph method.The innerscaling method was used to determine the concentrations of n-hexane and ethanol in this ternary system.Ethy1 acetate was chosen as the sample of inner-scaling because of its separability and fit retainning time.Acetylacetone was chosen as diluent of the oil phase andn-butyl alcohol was chosen as diluent of the water phase.The experimental data of four isothermal sections at 298.15K,308.15K,318.15K adn 328.15K in system water-n-hexane-ethanol at normal pressure were given.Four schematic figures were also given.The character of these phase diagrams was analysed.They were compared with the phase diagram of system water-n-hexane-methanol.The possible causes of experimental error were discussed.The root mean square error of measurement is 1.47%.
基金Projects(50731002,50971136)supported by the National Natural Science Foundation of China
文摘An isothermal section of the Mg-Nd-Gd ternary system at 723 K was established by diffusion triple technique and electron probe microanalysis （EPMA）. Mg3Gd and Mg3Nd form a continuous solid solution （Gd,Nd）3Mg, and a continuous solid solution （Gd,Nd）Mg is also formed between MgGd and MgNd. Mg7Gd, Mg5Gd, Mg2Gd, Mg41Nd5, （Gd,Nd）3Mg and （Gd,Nd）Mg are found in the ternary system. In these intermetallic phases, Mg7Gd has been reported to be a metastable phase in previous literatures. The solubilities of Mg, Gd and Nd in all the phases were detected. Furthermore, four three-phase equilibria, α（Mg）＋Mg7Gd＋Mg41Nd5, Mg7Gd＋Mg5Gd＋Mg41Nd5, Mg5Gd＋Mg41Nd5＋（Gd,Nd）3Mg and （Gd,Nd）3Mg＋（Gd,Nd）Mg＋Mg2Gd, were identified in the isothermal section.
基金financially supported by the National Natural Science Foundation of China(No.51831007)National Key R&D Program of China(No.2017YFB0702901)。
文摘Phase diagrams of two isothermal sections of the Ni-Ti-Ta ternary system at 1000 and 1200℃in a full composition range were determined by X-ray diffraction and electron probe microanalysis.The experimental results indicated a ternary compoundτphase with low solid solubility and composition ranges of(16.3-22.4)at.%Ta,(15.9-24.1)at.%Ti and(58.5-60.0)at.%Ni at 1000℃.The two terminal solid solutions(bcc-(Ta)andβ-Ti)formed a continuous solid solution at 1000 and 1200℃.A certain amount of Ti can dissolve into Ni-Ta intermetallic compounds near the Ni-Ta side,with the highest value of 21.9 at.%observed in the Ni;Ta compound at 1000℃.