A stable δ- and β-bismuth trioxide was prepared at room temperature by vacuum vapor-phase oxidation. The average crystal size of products was 14.6 nm (by XRD), the d(0.5) value was in the range from 62 nm to 69 nm, ...A stable δ- and β-bismuth trioxide was prepared at room temperature by vacuum vapor-phase oxidation. The average crystal size of products was 14.6 nm (by XRD), the d(0.5) value was in the range from 62 nm to 69 nm, and geometric standard deviation(GSD) was from 1.42 to 1.64. The results show that δ-Bi2O3 is formed when quenching rates is rapid and β-Bi2O3 is formed when it is slow. The size of grains increases with rising reaction temperature, flow rate of carrier gas, residual pressure of system and longer growing time of grains.展开更多
Ternary Ag/AgC l/BiO IO3 composite photocatalysts are prepared by a facile method. Enhanced visible-light absorption and charge carrier separation are achieved after the introduction of Ag/AgC l particles into BiO IO3...Ternary Ag/AgC l/BiO IO3 composite photocatalysts are prepared by a facile method. Enhanced visible-light absorption and charge carrier separation are achieved after the introduction of Ag/AgC l particles into BiO IO3 systems,as revealed by ultraviolet-visible diffuse-reflectance spectrometry,photocurrent response and electrochemical impedance spectroscopy. The Ag/AgC l/BiO IO3 composites are applied to the visible-light photocatalytic oxidization of NO in air and exhibit an enhanced activity for NO removal in comparison with Ag/AgC l and pure BiO IO3. A possible photocatalytic mechanism for Ag/AgC l/BiO IO3 is proposed,which is related to the surface plasmon resonance effects of Ag metal and the effective carrier separation ability of BiO IO3. This work provides insight into the design and preparation of BiO IO3-based materials with enhanced visible-light photocatalysis ability.展开更多
The combined use of the photoelectric and electro-optic properties of BSO crystal (Bi 12 SiO 20 ) leads to realize spatial light modulation.Under some condition,BSO crystal can become birefringent depending on...The combined use of the photoelectric and electro-optic properties of BSO crystal (Bi 12 SiO 20 ) leads to realize spatial light modulation.Under some condition,BSO crystal can become birefringent depending on a local illuminance.The relationship between the distributions of an illuminance and a birefringence will be discussed.This spatial light modulator can work in real-time. The experiment shows,in order to increase the sensitivity of BSO crystal,an electric field of 6 kV/cm at an atmosphere pressure of 15×10 5 Pa should be applied to BSO crystal.With BSO we have measured 3-dimensional deformation by means of real-time holography.展开更多
Reduction smelting of the bismuth oxide residue from pressure leaching of bismuth sulfide was investigated in the FeO-SiO_2-CaO ternary slag system.The results show that all the recovery ratios of Bi,Ag,Cu and Pb incr...Reduction smelting of the bismuth oxide residue from pressure leaching of bismuth sulfide was investigated in the FeO-SiO_2-CaO ternary slag system.The results show that all the recovery ratios of Bi,Ag,Cu and Pb increase with the increase of reductive coal proportion,reaction temperature and time,while too much reductive coal would help Fe enter metal phase;CaO/SiO_2and Fe O/SiO_2 of the chosen slag system should be 0.5-0.75 and 1.25-1.75,respectively,for the reason that the slag system has the optimum mobility and is beneficial for the recovery of metals.The corresponding optimum conditions are determined as follows:the added coal proportion is 7%of the leaching residue,CaO/SiO_2 mass ratio in the chosen slag system is 0.5 and FeO-SiO_2 is 1.5,the reaction temperature is 1300°C and the reaction time is 40 min.Under the above conditions,the recovery ratios of Bi,Ag,Cu and Pb are 99.6%,99.8%,97.0%and 97.3%,respectively.展开更多
基金Project(03SSY4056) supported by the Bureau of Science and Technology of Hunan Province, China Project(04C034) supported by the Bureau of Education of Hunan Province, China
文摘A stable δ- and β-bismuth trioxide was prepared at room temperature by vacuum vapor-phase oxidation. The average crystal size of products was 14.6 nm (by XRD), the d(0.5) value was in the range from 62 nm to 69 nm, and geometric standard deviation(GSD) was from 1.42 to 1.64. The results show that δ-Bi2O3 is formed when quenching rates is rapid and β-Bi2O3 is formed when it is slow. The size of grains increases with rising reaction temperature, flow rate of carrier gas, residual pressure of system and longer growing time of grains.
基金supported by the National Natural Science Foundation of China(5147807051108487)the Science and Technology Project from Chongqing Education Commission(KJ1400617)~~
文摘Ternary Ag/AgC l/BiO IO3 composite photocatalysts are prepared by a facile method. Enhanced visible-light absorption and charge carrier separation are achieved after the introduction of Ag/AgC l particles into BiO IO3 systems,as revealed by ultraviolet-visible diffuse-reflectance spectrometry,photocurrent response and electrochemical impedance spectroscopy. The Ag/AgC l/BiO IO3 composites are applied to the visible-light photocatalytic oxidization of NO in air and exhibit an enhanced activity for NO removal in comparison with Ag/AgC l and pure BiO IO3. A possible photocatalytic mechanism for Ag/AgC l/BiO IO3 is proposed,which is related to the surface plasmon resonance effects of Ag metal and the effective carrier separation ability of BiO IO3. This work provides insight into the design and preparation of BiO IO3-based materials with enhanced visible-light photocatalysis ability.
文摘The combined use of the photoelectric and electro-optic properties of BSO crystal (Bi 12 SiO 20 ) leads to realize spatial light modulation.Under some condition,BSO crystal can become birefringent depending on a local illuminance.The relationship between the distributions of an illuminance and a birefringence will be discussed.This spatial light modulator can work in real-time. The experiment shows,in order to increase the sensitivity of BSO crystal,an electric field of 6 kV/cm at an atmosphere pressure of 15×10 5 Pa should be applied to BSO crystal.With BSO we have measured 3-dimensional deformation by means of real-time holography.
基金Project(134414) supported by the Postdoctoral Funded Program of Central South University,China
文摘Reduction smelting of the bismuth oxide residue from pressure leaching of bismuth sulfide was investigated in the FeO-SiO_2-CaO ternary slag system.The results show that all the recovery ratios of Bi,Ag,Cu and Pb increase with the increase of reductive coal proportion,reaction temperature and time,while too much reductive coal would help Fe enter metal phase;CaO/SiO_2and Fe O/SiO_2 of the chosen slag system should be 0.5-0.75 and 1.25-1.75,respectively,for the reason that the slag system has the optimum mobility and is beneficial for the recovery of metals.The corresponding optimum conditions are determined as follows:the added coal proportion is 7%of the leaching residue,CaO/SiO_2 mass ratio in the chosen slag system is 0.5 and FeO-SiO_2 is 1.5,the reaction temperature is 1300°C and the reaction time is 40 min.Under the above conditions,the recovery ratios of Bi,Ag,Cu and Pb are 99.6%,99.8%,97.0%and 97.3%,respectively.