A three-dimensional （3-D） modified cellular automaton （MCA） method was developed for simulating the dendrite morphology of cubic system alloys. Two-dimensional （2-D） equations of growth velocities of the dendrit...A three-dimensional （3-D） modified cellular automaton （MCA） method was developed for simulating the dendrite morphology of cubic system alloys. Two-dimensional （2-D） equations of growth velocities of the dendrite tip, interface curvature and anisotropy of the surface energy were extended to 3-D system in the model. Therefore, the model was able to describe the morphology evolution of 3-D dendrites. Then, the model was applied to simulate the mechanism of spacing adjustment for 3-D columnar dendrite growth, and the competitive growth of columnar dendrites with different preferred growth orientations under constant temperature gradient and pulling velocity. Directional solidification experiments of NH4Cl-H2O transparent alloy were performed. It was found that the simulated results compared well with the experimental results. Therefore, the model was reliable for simulating the 3-D dendrite growth of cubic system alloys.展开更多
基金Projects (2005CB724105, 2011CB706801) supported by the National Basic Research Program of ChinaProjects (10477010, 51171089) supported by the National Natural Science Foundation of China+1 种基金Project (2007AA04Z141) supported by the High-Tech Research and Development Program of ChinaProjects (2009ZX04006-041-04, 2011ZX04014-052) supported by the Important National Science & Technology Specific
文摘A three-dimensional （3-D） modified cellular automaton （MCA） method was developed for simulating the dendrite morphology of cubic system alloys. Two-dimensional （2-D） equations of growth velocities of the dendrite tip, interface curvature and anisotropy of the surface energy were extended to 3-D system in the model. Therefore, the model was able to describe the morphology evolution of 3-D dendrites. Then, the model was applied to simulate the mechanism of spacing adjustment for 3-D columnar dendrite growth, and the competitive growth of columnar dendrites with different preferred growth orientations under constant temperature gradient and pulling velocity. Directional solidification experiments of NH4Cl-H2O transparent alloy were performed. It was found that the simulated results compared well with the experimental results. Therefore, the model was reliable for simulating the 3-D dendrite growth of cubic system alloys.