The Ag(Invar)composite powder prepared by ball milling was used to fabricate the Cu/Ag(Invar)composites.Microstructures and properties of the composites were studied after sintering and thermo-mechanical treatment.The...The Ag(Invar)composite powder prepared by ball milling was used to fabricate the Cu/Ag(Invar)composites.Microstructures and properties of the composites were studied after sintering and thermo-mechanical treatment.The results indicatethat during ball milling,micro-forging weld and work-hardening fracture result in that the average particle size of the Ag(Invar)powder increases rapidly at first,and then decreases sharply,finally tends to be constant.Compared with the Cu/Invar ones,thesinterability of the composites is greatly improved,resulting in that the pores in them are smaller in amount and size.After thethermo-mechanical treatment,the Cu/Ag(Invar)composites are nearly fully dense with the optimum phase composition and elementdistribution.More importantly,Cu and the Invar alloy in the composites distribute continuously in a three-dimensional(3D)networkstructure.Cu/Invar interface diffusion is effectively inhibited by the Ag barrier layer,leading to a great improvement of themechanical and thermal properties of the Cu/Ag(Invar)composites.展开更多
基金Project(2014DFA50860) supported by the International Science&Technology Cooperation Program of China
文摘The Ag(Invar)composite powder prepared by ball milling was used to fabricate the Cu/Ag(Invar)composites.Microstructures and properties of the composites were studied after sintering and thermo-mechanical treatment.The results indicatethat during ball milling,micro-forging weld and work-hardening fracture result in that the average particle size of the Ag(Invar)powder increases rapidly at first,and then decreases sharply,finally tends to be constant.Compared with the Cu/Invar ones,thesinterability of the composites is greatly improved,resulting in that the pores in them are smaller in amount and size.After thethermo-mechanical treatment,the Cu/Ag(Invar)composites are nearly fully dense with the optimum phase composition and elementdistribution.More importantly,Cu and the Invar alloy in the composites distribute continuously in a three-dimensional(3D)networkstructure.Cu/Invar interface diffusion is effectively inhibited by the Ag barrier layer,leading to a great improvement of themechanical and thermal properties of the Cu/Ag(Invar)composites.