Two water soluble acryl terpolymers containing polyvinyl alcohol, acrylamide/acrylic acid and vinyl sulphonic acid （VSA） were synthesized by free radical polymerization in aqueous medium. The morphological structure...Two water soluble acryl terpolymers containing polyvinyl alcohol, acrylamide/acrylic acid and vinyl sulphonic acid （VSA） were synthesized by free radical polymerization in aqueous medium. The morphological structure of the polymers were analysed using FTIR and 1H NMR, while the thermal properties were analysed by TGA and DSC. The inhibitive action of the terpolymers on corrosion of mid-steel in 1 mol. L- 1 HCI was studied using gravimetric, potentiodynamic polarisation and electrochemical impedance spectroscopy （EIS） at 303 K. Both the polymers provided inhibition efficiency around 90% which clearly demonstrate that the grafted poly- mers have effective corrosion inhibiting ability on MS corrosion.展开更多
A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature...A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature, functional monomers, titration time on performances of emulsion have been discussed in detail.展开更多
Fe3O4/P （NaUA-St-BA） core-shell composite micro spheres were in situ prepared by soapless polymerization of styrene and butyl acrylate, with Fe3O4magnetic colloidal particles coated with NaUA. The results of IR and ...Fe3O4/P （NaUA-St-BA） core-shell composite micro spheres were in situ prepared by soapless polymerization of styrene and butyl acrylate, with Fe3O4magnetic colloidal particles coated with NaUA. The results of IR and XRD analysis demonstrated that the desired polymer chains have been covalently bonded to the surface of Fe3O4 nano particles. The morphology analysis by TEM confirmed that the composite particles have the core-shell structure and a relatively uniform diameter of about 100nm. The magnetic properties of the obtained composite latex particles were measured by VSM and found that they exhibited super paramagnetic properties. Finally, the prepared magnetic composite particles latex is stable for several months.展开更多
Polymer-coated mesoporous carbon nanocomposites were prepared from the immobilization of acrylonitrile and acrylic acid copolymers with divinylbenzene as a crosslinker onto a mesoporous carbon framework.High surface a...Polymer-coated mesoporous carbon nanocomposites were prepared from the immobilization of acrylonitrile and acrylic acid copolymers with divinylbenzene as a crosslinker onto a mesoporous carbon framework.High surface areas were maintained after polymerization with accessible porosity.This functional nanocomposite was tested as an adsorbent for uranium from high salinity solutions.Uranium adsorption results have shown that the adsorption capacities are strongly influenced by the density of the amidoxime groups and the specific surface area.展开更多
基金Tamil Nadu State Council for Science and Technology (Tnscst/rfrs/vr/2013-14) for catalysing and financially supporting the research work under the RFRS scheme
文摘Two water soluble acryl terpolymers containing polyvinyl alcohol, acrylamide/acrylic acid and vinyl sulphonic acid （VSA） were synthesized by free radical polymerization in aqueous medium. The morphological structure of the polymers were analysed using FTIR and 1H NMR, while the thermal properties were analysed by TGA and DSC. The inhibitive action of the terpolymers on corrosion of mid-steel in 1 mol. L- 1 HCI was studied using gravimetric, potentiodynamic polarisation and electrochemical impedance spectroscopy （EIS） at 303 K. Both the polymers provided inhibition efficiency around 90% which clearly demonstrate that the grafted poly- mers have effective corrosion inhibiting ability on MS corrosion.
基金Ministry of Science and Technology of China for Major State Basic Research Projects (2002AA322020)
文摘A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature, functional monomers, titration time on performances of emulsion have been discussed in detail.
文摘Fe3O4/P （NaUA-St-BA） core-shell composite micro spheres were in situ prepared by soapless polymerization of styrene and butyl acrylate, with Fe3O4magnetic colloidal particles coated with NaUA. The results of IR and XRD analysis demonstrated that the desired polymer chains have been covalently bonded to the surface of Fe3O4 nano particles. The morphology analysis by TEM confirmed that the composite particles have the core-shell structure and a relatively uniform diameter of about 100nm. The magnetic properties of the obtained composite latex particles were measured by VSM and found that they exhibited super paramagnetic properties. Finally, the prepared magnetic composite particles latex is stable for several months.
基金sponsored by the US Department of EnergyOffice of Nuclear Energy+2 种基金under contract DE-AC05-00OR22725 with Oak Ridge National Laboratorymanaged by UT-BattelleLLC
文摘Polymer-coated mesoporous carbon nanocomposites were prepared from the immobilization of acrylonitrile and acrylic acid copolymers with divinylbenzene as a crosslinker onto a mesoporous carbon framework.High surface areas were maintained after polymerization with accessible porosity.This functional nanocomposite was tested as an adsorbent for uranium from high salinity solutions.Uranium adsorption results have shown that the adsorption capacities are strongly influenced by the density of the amidoxime groups and the specific surface area.