Copolymer of maleic acid and acrylic acid （PMA-100）, combining with polyvinyl butyral （PVB） ultrafiltration membrane was used for the removal of Mn（II） from waste water by complexation-ultrafiltration. The carbo...Copolymer of maleic acid and acrylic acid （PMA-100）, combining with polyvinyl butyral （PVB） ultrafiltration membrane was used for the removal of Mn（II） from waste water by complexation-ultrafiltration. The carboxylic group content of PMA-100 and the rate of complexation reaction were measured. Effects of the mass ratio of PMA-100 to Mn（II） （n）, pH, background electrolyte, etc on the rejection rate （R） and permeate flux （J） were investigated. The results show that carboxylic group content of PMA-100 is 9.5 mmol/g. The complexation of Mn（II） with PMA-100 is rapid and completed within 5 min at pH 6.0. Both R and J increase with pH increasing in the range of 2.5-7.0, and R increases with the increase of n at pH 6.0 while J is little affected. The background electrolyte leads to the decrease of R, and CaCl2 has much greater effect on R than NaCl at the same ionic strength.展开更多
基金Project (21176264) supported by the National Natural Science Foundation of ChinaProject (11JJ2010) supported by Hunan Provincial Natural Science Foundation of ChinaProject (LC13076) supported by Undergraduate Innovation Foundation of Central South University,China
文摘Copolymer of maleic acid and acrylic acid （PMA-100）, combining with polyvinyl butyral （PVB） ultrafiltration membrane was used for the removal of Mn（II） from waste water by complexation-ultrafiltration. The carboxylic group content of PMA-100 and the rate of complexation reaction were measured. Effects of the mass ratio of PMA-100 to Mn（II） （n）, pH, background electrolyte, etc on the rejection rate （R） and permeate flux （J） were investigated. The results show that carboxylic group content of PMA-100 is 9.5 mmol/g. The complexation of Mn（II） with PMA-100 is rapid and completed within 5 min at pH 6.0. Both R and J increase with pH increasing in the range of 2.5-7.0, and R increases with the increase of n at pH 6.0 while J is little affected. The background electrolyte leads to the decrease of R, and CaCl2 has much greater effect on R than NaCl at the same ionic strength.