Different-sized hollow SiO2 spheres of 249–1348 nm in diameter were successfully prepared by using Na2SiO3 as the precursor and using polystyrene and polystyrene-methyl acrylic acid latexes as the templates. The diam...Different-sized hollow SiO2 spheres of 249–1348 nm in diameter were successfully prepared by using Na2SiO3 as the precursor and using polystyrene and polystyrene-methyl acrylic acid latexes as the templates. The diameter and shell thickness of the hollow SiO2 spheres increase with increasing the latex template diameter at a given mass ratio of SiO2 to latex template. The diameter and shell thickness of the hollow SiO2 spheres also increase with increasing the mass ratios of SiO2 to latex template. The presence of carboxylic acid groups on the surfaces of polystyrene-methyl acrylic acid latex templates favors the formation of dense and uniform SiO2 shells. The hollow SiO2 sphere is constructed by mesoporous shell with large specific surface area. When glyphosate is used as a release model chemical, glyphosate release rate is tuned by varying the shell thickness.展开更多
Acetyl crosslinked polystyrene (EPS) and crosslinked bromoacetyl polystyrene (BEPS)beads were synthesized by Fridel-Crafts acetylation of polystyrene (PS) and bromination of EPS respectively. FTIR, XPS, and TG-TDG wer...Acetyl crosslinked polystyrene (EPS) and crosslinked bromoacetyl polystyrene (BEPS)beads were synthesized by Fridel-Crafts acetylation of polystyrene (PS) and bromination of EPS respectively. FTIR, XPS, and TG-TDG were employed to characterize their structures. The results revealed there are two types of bromine in the BEPS molecule. One is in the main chain of polystyrene and the other is in the acetyl. The results of TG-DTG showed that the rates of loss weight of PS, EPS, and BEPS were 92.7%, 92.2%, and 81.3% among the 300 ℃～500 ℃; 7.3%, 7.8%, and 18. 7% in 594 ℃, 660 ℃, and 584.8 ℃, respectively.展开更多
It was generally considered that contamination of the gel type polystyrenestrong basic anion exchange resin by organic matter in natural water is the result ofion exchange and Van der waal's adsorption on it. On t...It was generally considered that contamination of the gel type polystyrenestrong basic anion exchange resin by organic matter in natural water is the result ofion exchange and Van der waal's adsorption on it. On the basis of laboratory and industrial experiments, this paper confirmed that the interreaction between organicmatter and resin polymer matrix is primarily controled by a Van der waal's adsorption.展开更多
基金Projects (11KJB530002, CX10B-259Z) supported by Research Funds from Jiangsu Provincial Department of Education, ChinaProject (10zxfk35) supported by Sichuan Province Nonmetallic Composites and Functional Materials Key Laboratory Project, China
文摘Different-sized hollow SiO2 spheres of 249–1348 nm in diameter were successfully prepared by using Na2SiO3 as the precursor and using polystyrene and polystyrene-methyl acrylic acid latexes as the templates. The diameter and shell thickness of the hollow SiO2 spheres increase with increasing the latex template diameter at a given mass ratio of SiO2 to latex template. The diameter and shell thickness of the hollow SiO2 spheres also increase with increasing the mass ratios of SiO2 to latex template. The presence of carboxylic acid groups on the surfaces of polystyrene-methyl acrylic acid latex templates favors the formation of dense and uniform SiO2 shells. The hollow SiO2 sphere is constructed by mesoporous shell with large specific surface area. When glyphosate is used as a release model chemical, glyphosate release rate is tuned by varying the shell thickness.
基金National Natural Science Foundation of China (No.29906008) and Nature Science Foundation of Shandong Province (No.Q99B15).
文摘Acetyl crosslinked polystyrene (EPS) and crosslinked bromoacetyl polystyrene (BEPS)beads were synthesized by Fridel-Crafts acetylation of polystyrene (PS) and bromination of EPS respectively. FTIR, XPS, and TG-TDG were employed to characterize their structures. The results revealed there are two types of bromine in the BEPS molecule. One is in the main chain of polystyrene and the other is in the acetyl. The results of TG-DTG showed that the rates of loss weight of PS, EPS, and BEPS were 92.7%, 92.2%, and 81.3% among the 300 ℃～500 ℃; 7.3%, 7.8%, and 18. 7% in 594 ℃, 660 ℃, and 584.8 ℃, respectively.
文摘It was generally considered that contamination of the gel type polystyrenestrong basic anion exchange resin by organic matter in natural water is the result ofion exchange and Van der waal's adsorption on it. On the basis of laboratory and industrial experiments, this paper confirmed that the interreaction between organicmatter and resin polymer matrix is primarily controled by a Van der waal's adsorption.