Combinations of graphene(Gr)and carbon black(C)were employed as binary carbon supports to fabricate Pd‐based electrocatalysts via one‐pot co‐reduction with Pd2+.The electrocatalytic performance of the resulting Pd...Combinations of graphene(Gr)and carbon black(C)were employed as binary carbon supports to fabricate Pd‐based electrocatalysts via one‐pot co‐reduction with Pd2+.The electrocatalytic performance of the resulting Pd/Gr‐C catalysts during the electrooxidation of formic acid was assessed.A Pd/Gr0.3C0.7(Gr oxide:C=3:7,based on the precursor mass ratio)electrocatalyst exhibited better catalytic performance than both Pd/C and Pd/Gr catalysts.The current density generated by the Pd/Gr0.3C0.7catalyst was as high as102.14mA mgPd?1,a value that is approximately3times that obtained from the Pd/C(34.40mA mgPd?1)and2.6times that of the Pd/Gr material(38.50mA mgPd?1).The anodic peak potential of the Pd/Gr0.3C0.7was120mV more negative than that of the Pd/C and70mV more negative than that of the Pd/Gr.Scanning electron microscopy images indicated that the spherical C particles accumulated on the wrinkled graphene surfaces to form C cluster/Gr hybrids having three‐dimensional nanostructures.X‐ray photoelectron spectroscopy data confirmed the interaction between the Pd metal and the binary Gr‐C support.The Pd/Gr0.3C0.7also exhibited high stability,and so is a promising candidate for the fabrication of anodes for direct formic acid fuel cells.This work demonstrates a simple and cost‐effective method for improving the performance of Pd‐based electrocatalysts,which should have potential industrial applications.展开更多
基金supported by the Natural Science Foundation of Shandong Province(ZR2016BM31)the Science and Technology Foundation of Jinan City(201311035)~~
文摘Combinations of graphene(Gr)and carbon black(C)were employed as binary carbon supports to fabricate Pd‐based electrocatalysts via one‐pot co‐reduction with Pd2+.The electrocatalytic performance of the resulting Pd/Gr‐C catalysts during the electrooxidation of formic acid was assessed.A Pd/Gr0.3C0.7(Gr oxide:C=3:7,based on the precursor mass ratio)electrocatalyst exhibited better catalytic performance than both Pd/C and Pd/Gr catalysts.The current density generated by the Pd/Gr0.3C0.7catalyst was as high as102.14mA mgPd?1,a value that is approximately3times that obtained from the Pd/C(34.40mA mgPd?1)and2.6times that of the Pd/Gr material(38.50mA mgPd?1).The anodic peak potential of the Pd/Gr0.3C0.7was120mV more negative than that of the Pd/C and70mV more negative than that of the Pd/Gr.Scanning electron microscopy images indicated that the spherical C particles accumulated on the wrinkled graphene surfaces to form C cluster/Gr hybrids having three‐dimensional nanostructures.X‐ray photoelectron spectroscopy data confirmed the interaction between the Pd metal and the binary Gr‐C support.The Pd/Gr0.3C0.7also exhibited high stability,and so is a promising candidate for the fabrication of anodes for direct formic acid fuel cells.This work demonstrates a simple and cost‐effective method for improving the performance of Pd‐based electrocatalysts,which should have potential industrial applications.