For the clean and economical production of chromium compounds, it is crucial to remove aluminates from chromate alkali solutions and utilize aluminum-containing compounds. In this work, carbonization was used to remov...For the clean and economical production of chromium compounds, it is crucial to remove aluminates from chromate alkali solutions and utilize aluminum-containing compounds. In this work, carbonization was used to remove aluminates from a synthetic chromate leaching solution containing a high K2O/Al2O3 mole ratio. The influence of reaction temperature, carbonization time, flow rate of carbon dioxide, and seed ratio on the precipitation of Al was investigated. The optimal output was obtained under the following experimental conditions： a reaction temperature of 50 °C, a carbonization time of 100 min, a carbon dioxide flow rate of 0.1 L/min, and a seed ratio of 1.0. Gibbsite was obtained following carbonization. The structure and morphology of the gibbsite were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and laser particle size analyzer. The particle size distribution and morphology of the gibbsite were significantly influenced by the experimental conditions. The gibbsite had a mean particle size （d50） of 16.72μm. The thermal decomposition of the gibbsite was analyzed by XRD and the decomposition path was determined. The obtained coarseα-Al2O3 precipitate, which contains 0.08% Cr2O3 and 0.10% K2O, was suitable for subsequent utilization.展开更多
基金Project(51125018)supported by the National Science Foundation for Distinguished Young Scholars of ChinaProject(2011AA060704)supported by the National High-tech Research and Development Program of ChinaProjects(51204153,21406246)supported by the National Natural Science Foundation of China
文摘For the clean and economical production of chromium compounds, it is crucial to remove aluminates from chromate alkali solutions and utilize aluminum-containing compounds. In this work, carbonization was used to remove aluminates from a synthetic chromate leaching solution containing a high K2O/Al2O3 mole ratio. The influence of reaction temperature, carbonization time, flow rate of carbon dioxide, and seed ratio on the precipitation of Al was investigated. The optimal output was obtained under the following experimental conditions： a reaction temperature of 50 °C, a carbonization time of 100 min, a carbon dioxide flow rate of 0.1 L/min, and a seed ratio of 1.0. Gibbsite was obtained following carbonization. The structure and morphology of the gibbsite were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and laser particle size analyzer. The particle size distribution and morphology of the gibbsite were significantly influenced by the experimental conditions. The gibbsite had a mean particle size （d50） of 16.72μm. The thermal decomposition of the gibbsite was analyzed by XRD and the decomposition path was determined. The obtained coarseα-Al2O3 precipitate, which contains 0.08% Cr2O3 and 0.10% K2O, was suitable for subsequent utilization.