A dynamic material model of Mg-4.51Al-1.19Zn-0.5Mn-0.5Ca(AZ41,mass fraction,%)magnesium alloy was put forward.The results show that the dynamic material model can characterize the deformation behavior and microstructu...A dynamic material model of Mg-4.51Al-1.19Zn-0.5Mn-0.5Ca(AZ41,mass fraction,%)magnesium alloy was put forward.The results show that the dynamic material model can characterize the deformation behavior and microstructure evolution and describe the relations among flow stress,strain,strain rates and deformation temperatures.Statistical analysis shows the validity of the proposed model.The model predicts that lower deformation temperature and higher strain rate cause the sharp strain hardening. Meanwhile,the flow stress curve turns into a steady state at high temperature and lower strain rate.The moderate temperature of 350 ℃and strain rate of 0.01 s-1 are appropriate to this alloy.展开更多
Isothermal compression tests are applied to study the deformation mechanisms of TC11 titanium alloy with lamellar structure under the deformation temperature range of 890-995 oC and strain rate range of 0.01-10 s-1.Ac...Isothermal compression tests are applied to study the deformation mechanisms of TC11 titanium alloy with lamellar structure under the deformation temperature range of 890-995 oC and strain rate range of 0.01-10 s-1.According to the flow stress data obtained by compression tests,the deformation activations are calculated based on kinetics analysis of high temperature deformation,which are then used for deformation mechanism analysis combined with microstructure investigation.The results show that deformation mechanisms vary with deformation conditions:at low strain rate range,the deformation mechanism is mainly dislocation slip;at low temperature and high strain rate range,twinning is the main mechanism;at high temperature and high strain rate range,the deformation is mainly controlled by diffusion of β phase.展开更多
The impact of a rigid body(protected structure) together with cushion material(cellular metal foam) on hard ground from a fixed height was investigated.An analytical one-degree-of-freedom colliding model(ODF-CM) was e...The impact of a rigid body(protected structure) together with cushion material(cellular metal foam) on hard ground from a fixed height was investigated.An analytical one-degree-of-freedom colliding model(ODF-CM) was established to analyze the protection ability and energy absorption by the foam under low velocity impact conditions.For validation,drop hammer experiments were carried out for high porosity closed-cell aluminum foam specimens subjected to low velocity impact loading.The dynamic deformation behavior of the specimen was observed and the velocity attenuation of the drop hammer was measured.The results demonstrated that the aluminum foam had excellent energy absorption capabilities,with its dynamic compressive behavior similar to that obtained under quasi-static loading conditions.Finite element method(FEM) was subsequently employed to obtain stress distributions in the foam specimen.As the propagating period of stress in the specimen was far less than the duration of attenuation,the evolution of the stress was similar to that under quasi-static loading conditions and no obvious stress wave effect was observed,which agreed with the experimental observation.Finally,the predicted velocity attenuation by the ODF-CM was compared with both the experimental measurements and FEM simulation,and good agreements were achieved when the stress distribution was considered to be uniform and the "quasi-static" compressive properties are employed.展开更多
Uniaxial tensile testing at strain rates ranging from 10-3 to 10-1 s-1 was carried out to study the rate-dependent me-chanical behavior for poly(ethylene terephthalate) (PET) used in the packaging industry. The experi...Uniaxial tensile testing at strain rates ranging from 10-3 to 10-1 s-1 was carried out to study the rate-dependent me-chanical behavior for poly(ethylene terephthalate) (PET) used in the packaging industry. The experimental results show that a rate-dependent plastic behavior exists for PET material. The value of the yield strength was found to increase with the increasing strain rate. A new constitutive model based on the improved Cowper-Symonds rate-dependent constitutive model is proposed to describe the mechanical behavior of PET material in the strain rate ranging from 10-3 to 10-1 s-1, providing more accurate material data for the subsequent simulation analysis of drop test and dynamic buckling. The predictions obtained using the proposed model are compared with experimental results of the improved Cowper-Symonds model. The simulating results of the proposed model agree well with the experimental data. For a low strain rate, the predictions of this model are more precise than those obtained using the improved Cowper-Symonds model. This confirms that the new constitutive model is suitable for describing the me-chanical behavior of PET material at a low strain rate and modeling impact problem.展开更多
基金Project(12JCYBJC32100)supported by Tianjin Research Program of Application Foundation and Advanced Technologyin part by Grants-in-Aid from the Japan Society for the Promotion of Science(JSPS)
基金Project(Y2008F27)supported by the Natural Science Foundation of Shandong Province,China
文摘A dynamic material model of Mg-4.51Al-1.19Zn-0.5Mn-0.5Ca(AZ41,mass fraction,%)magnesium alloy was put forward.The results show that the dynamic material model can characterize the deformation behavior and microstructure evolution and describe the relations among flow stress,strain,strain rates and deformation temperatures.Statistical analysis shows the validity of the proposed model.The model predicts that lower deformation temperature and higher strain rate cause the sharp strain hardening. Meanwhile,the flow stress curve turns into a steady state at high temperature and lower strain rate.The moderate temperature of 350 ℃and strain rate of 0.01 s-1 are appropriate to this alloy.
文摘Isothermal compression tests are applied to study the deformation mechanisms of TC11 titanium alloy with lamellar structure under the deformation temperature range of 890-995 oC and strain rate range of 0.01-10 s-1.According to the flow stress data obtained by compression tests,the deformation activations are calculated based on kinetics analysis of high temperature deformation,which are then used for deformation mechanism analysis combined with microstructure investigation.The results show that deformation mechanisms vary with deformation conditions:at low strain rate range,the deformation mechanism is mainly dislocation slip;at low temperature and high strain rate range,twinning is the main mechanism;at high temperature and high strain rate range,the deformation is mainly controlled by diffusion of β phase.
基金supported by the National Basic Research Program of China ("973" Project)(Grant No. 2011CB610305)the National "111" Project of China (Grant No. B06024)the National Natural Science Foundation of China (Grant Nos. 10825210,11072188)
文摘The impact of a rigid body(protected structure) together with cushion material(cellular metal foam) on hard ground from a fixed height was investigated.An analytical one-degree-of-freedom colliding model(ODF-CM) was established to analyze the protection ability and energy absorption by the foam under low velocity impact conditions.For validation,drop hammer experiments were carried out for high porosity closed-cell aluminum foam specimens subjected to low velocity impact loading.The dynamic deformation behavior of the specimen was observed and the velocity attenuation of the drop hammer was measured.The results demonstrated that the aluminum foam had excellent energy absorption capabilities,with its dynamic compressive behavior similar to that obtained under quasi-static loading conditions.Finite element method(FEM) was subsequently employed to obtain stress distributions in the foam specimen.As the propagating period of stress in the specimen was far less than the duration of attenuation,the evolution of the stress was similar to that under quasi-static loading conditions and no obvious stress wave effect was observed,which agreed with the experimental observation.Finally,the predicted velocity attenuation by the ODF-CM was compared with both the experimental measurements and FEM simulation,and good agreements were achieved when the stress distribution was considered to be uniform and the "quasi-static" compressive properties are employed.
基金Project (No 2008C11005) supported by the Key Science and Technology Program of Zhejiang Province, China
文摘Uniaxial tensile testing at strain rates ranging from 10-3 to 10-1 s-1 was carried out to study the rate-dependent me-chanical behavior for poly(ethylene terephthalate) (PET) used in the packaging industry. The experimental results show that a rate-dependent plastic behavior exists for PET material. The value of the yield strength was found to increase with the increasing strain rate. A new constitutive model based on the improved Cowper-Symonds rate-dependent constitutive model is proposed to describe the mechanical behavior of PET material in the strain rate ranging from 10-3 to 10-1 s-1, providing more accurate material data for the subsequent simulation analysis of drop test and dynamic buckling. The predictions obtained using the proposed model are compared with experimental results of the improved Cowper-Symonds model. The simulating results of the proposed model agree well with the experimental data. For a low strain rate, the predictions of this model are more precise than those obtained using the improved Cowper-Symonds model. This confirms that the new constitutive model is suitable for describing the me-chanical behavior of PET material at a low strain rate and modeling impact problem.