Experiments on the partitioning of Cu between different granitic silicate melts and the respective coexisting aqueous fluids have been performed under conditions of 850 ℃, 100 MPa and oxygen fugacity （fO2） buffered...Experiments on the partitioning of Cu between different granitic silicate melts and the respective coexisting aqueous fluids have been performed under conditions of 850 ℃, 100 MPa and oxygen fugacity （fO2） buffered at approaching Ni-NiO （NNO）. Partition coefficients of Cu （Dcu = Cfluid/Cmelt） were varied with different alumina/alkali mole ratios [Al2O3/（Na2O ＋ K2O）, abbreviated as Al/ Alk], Na/K mole ratios, and SiO2 mole contents. The DCu increased from 1.28 ± 0.01 to 22.18 ±0.22 with the increase of Al/Alk mole ratios （ranging from 0.64 to 1.20） and Na/K mole ratios （ranging from 0.58 to 2.56）. The experimental results also showed that Dcu was positively correlated with the HCl concentration of the starting fluid. The Dcu was independent of the SiO2 mole content in the range of SiO2 content considered. No Dcu value was less than 1 in our experiments at 850 ℃ and 100 MPa, indicating that Cu preferred to enter the fluid phase rather than the coexisting melt phase under most conditions in the melt-fluid system, and thus a significant amount of Cu could be transported in the fluid phase in the magmatichydrothermal environment. The results indicated that Cu favored partitioning into the aqueous fluid rather than the melt phase if there was a high Na/K ratio, Na-rich, peraluminous granitic melt coexisting with the high Cl^- fluid.展开更多
文摘Experiments on the partitioning of Cu between different granitic silicate melts and the respective coexisting aqueous fluids have been performed under conditions of 850 ℃, 100 MPa and oxygen fugacity （fO2） buffered at approaching Ni-NiO （NNO）. Partition coefficients of Cu （Dcu = Cfluid/Cmelt） were varied with different alumina/alkali mole ratios [Al2O3/（Na2O ＋ K2O）, abbreviated as Al/ Alk], Na/K mole ratios, and SiO2 mole contents. The DCu increased from 1.28 ± 0.01 to 22.18 ±0.22 with the increase of Al/Alk mole ratios （ranging from 0.64 to 1.20） and Na/K mole ratios （ranging from 0.58 to 2.56）. The experimental results also showed that Dcu was positively correlated with the HCl concentration of the starting fluid. The Dcu was independent of the SiO2 mole content in the range of SiO2 content considered. No Dcu value was less than 1 in our experiments at 850 ℃ and 100 MPa, indicating that Cu preferred to enter the fluid phase rather than the coexisting melt phase under most conditions in the melt-fluid system, and thus a significant amount of Cu could be transported in the fluid phase in the magmatichydrothermal environment. The results indicated that Cu favored partitioning into the aqueous fluid rather than the melt phase if there was a high Na/K ratio, Na-rich, peraluminous granitic melt coexisting with the high Cl^- fluid.