The effects of isothermal holding time on the semisolid microstructure of Mg-9Al-1Si(mass fraction,%)alloy were investigated.The research results indicate that the Mg-9Al-1Si alloy with non-dendritic microstructure ca...The effects of isothermal holding time on the semisolid microstructure of Mg-9Al-1Si(mass fraction,%)alloy were investigated.The research results indicate that the Mg-9Al-1Si alloy with non-dendritic microstructure can be produced by the semi-solid isothermal heat treatment.With holding time varying from 5 to 30 min,the volume fraction of liquid is gradually enlarged from 29.3%to 38.6%,the morphology ofα-Mg grains changes from initial dendritic shape to spherical types and their average sizes increases from 41.1 to 56.1μm.In addition,during the isothermal heat treatment,the eutectic Mg2Si phase changes from the initial Chinese script shape to granule and/or polygon shape in Mg-9Al-1Si alloy.The modification of Mg2Si phase is possibly attributed to a shift of the eutectic composition of the liquid in semi-solid slurries,towards lower silicon contents with increasing Al content due to a redistribution of Al during isothermal heat treatment.展开更多
基金Project(HEUFT05038)supported by the Basic Research Foundation of Harbin Engineering University,ChinaProject(2009AA03Z423)supported by the National High-Tech Research and Development Program of China
文摘The effects of isothermal holding time on the semisolid microstructure of Mg-9Al-1Si(mass fraction,%)alloy were investigated.The research results indicate that the Mg-9Al-1Si alloy with non-dendritic microstructure can be produced by the semi-solid isothermal heat treatment.With holding time varying from 5 to 30 min,the volume fraction of liquid is gradually enlarged from 29.3%to 38.6%,the morphology ofα-Mg grains changes from initial dendritic shape to spherical types and their average sizes increases from 41.1 to 56.1μm.In addition,during the isothermal heat treatment,the eutectic Mg2Si phase changes from the initial Chinese script shape to granule and/or polygon shape in Mg-9Al-1Si alloy.The modification of Mg2Si phase is possibly attributed to a shift of the eutectic composition of the liquid in semi-solid slurries,towards lower silicon contents with increasing Al content due to a redistribution of Al during isothermal heat treatment.