Formamidinium lead bromide(FAPbBr_(3))nanocrystals(NCs)have been considered to be a good optoelectronic material due to their pure green emission,excellent stability and superior carrier transport characteristics.Howe...Formamidinium lead bromide(FAPbBr_(3))nanocrystals(NCs)have been considered to be a good optoelectronic material due to their pure green emission,excellent stability and superior carrier transport characteristics.However,two-photon pumped amplified spontaneous emission(ASE)and the corresponding nonlinear optical properties of FAPbBr_(3) NCs are scarcely revealed.Herein,we synthesized colloidal FAPbBr_(3) NCs with different sizes by changing the molar ratio of FABr/PbBr_(2) in the precursor solution,using ligand assisted precipitation(LARP)technology at room temperature.Photoluminescence(PL)and time resolved photoluminescence(TRPL)spectroscopy were measured to characterize their ASE properties.And their nonlinear optical properties were studied through the Zscan technique and the two-photon excited fluorescence method.The stimulated emission properties including oneand two-photon pumped ASE have been realized from FAPbBr_(3) NCs.With large two-photon absorption coefficient(0.27 cm/GW)and high non-linear absorption cross-section(7.52×10^(5) GM),ASE with threshold as low as 9.8μJ/cm^(2) and 487μJ/cm^(2) have been obtained from colloidal FAPbBr_(3) NCs using one-and two-photon excitations.These results indicate that as a new possible green-emitting frequency-upconversion material with low thresholds,FAPbBr_(3) NCs hold great potential in the development of high-performance two-photon pump lasers.展开更多
高性能微消光涤纶是针对制造工业缝纫线而开发的,原料上使用大有光增黏聚酯切片进行生产,工艺上由原来的"四组热辊"、"三步拉伸"改为"两组热辊"、"一步拉伸"的生产方式,并优化了工艺参数,生产...高性能微消光涤纶是针对制造工业缝纫线而开发的,原料上使用大有光增黏聚酯切片进行生产,工艺上由原来的"四组热辊"、"三步拉伸"改为"两组热辊"、"一步拉伸"的生产方式,并优化了工艺参数,生产出强度达到4.8 c N/dtex的涤纶长丝,且大大降低了生产成本。展开更多
文摘Formamidinium lead bromide(FAPbBr_(3))nanocrystals(NCs)have been considered to be a good optoelectronic material due to their pure green emission,excellent stability and superior carrier transport characteristics.However,two-photon pumped amplified spontaneous emission(ASE)and the corresponding nonlinear optical properties of FAPbBr_(3) NCs are scarcely revealed.Herein,we synthesized colloidal FAPbBr_(3) NCs with different sizes by changing the molar ratio of FABr/PbBr_(2) in the precursor solution,using ligand assisted precipitation(LARP)technology at room temperature.Photoluminescence(PL)and time resolved photoluminescence(TRPL)spectroscopy were measured to characterize their ASE properties.And their nonlinear optical properties were studied through the Zscan technique and the two-photon excited fluorescence method.The stimulated emission properties including oneand two-photon pumped ASE have been realized from FAPbBr_(3) NCs.With large two-photon absorption coefficient(0.27 cm/GW)and high non-linear absorption cross-section(7.52×10^(5) GM),ASE with threshold as low as 9.8μJ/cm^(2) and 487μJ/cm^(2) have been obtained from colloidal FAPbBr_(3) NCs using one-and two-photon excitations.These results indicate that as a new possible green-emitting frequency-upconversion material with low thresholds,FAPbBr_(3) NCs hold great potential in the development of high-performance two-photon pump lasers.