Thin transparent oxide conducting films(TCOFs)of titanium and gallium substituted zinc oxide(TGZO)were fabricated via radio frequency(RF)magnetron sputtering technique.The effects of RF power on electrical,linear and ...Thin transparent oxide conducting films(TCOFs)of titanium and gallium substituted zinc oxide(TGZO)were fabricated via radio frequency(RF)magnetron sputtering technique.The effects of RF power on electrical,linear and nonlinear optical characteristics were investigated by Hall tester,Ultraviolet(UV)-visible spectrophotometer and optical characterization method.The results indicate that RF power significantly influences the electrical and optical properties of the deposited films.As RF power raises,the resistivity and Urbach energy fall initially and then rise,while the figure of merit,mean visible transmittance and optical bandgap show the reverse variation trend.At RF power of 190 W,the TGZO sample exhibits the highest electro-optical properties,with the maximum figure of merit(1.14×10^(4)Ω-1∙cm^(-1)),mean visible transmittance(86.9%)and optical bandgap(3.50 eV),the minimum resistivity(6.26×10^(-4)Ω∙cm)and Urbach energy(174.23 meV).In addition,the optical constants of the deposited films were determined by the optical spectrum fitting method,and the RF power dependence of nonlinear optical properties was studied.It is observed that all the thin films exhibit normal dispersion characteristics in the visible region,and the nonlinear optical parameters are greatly affected by the RF power in the ultraviolet region.展开更多
The fluorine-containing organic polymer was synthesized from 3, 3＇, 4, 4＇-Bisphenyltetracarboxylic （BPDA）, and 2,2-Bis （3-amino-4-hydroxyyphenyl） hexafluoropropane （6FHP）. It is a first-step preparation of a p...The fluorine-containing organic polymer was synthesized from 3, 3＇, 4, 4＇-Bisphenyltetracarboxylic （BPDA）, and 2,2-Bis （3-amino-4-hydroxyyphenyl） hexafluoropropane （6FHP）. It is a first-step preparation of a preimided hydroxy-containing polyimide, followed by the covalent bonding of an active chromophore, dispersed red 19 （DR19）, onto the backbone of the polyimide via the Mitsunobu reaction. The nonlinear optical （NLO） containing polyimide was synthesized. The differential scanning calorimeter （DSC）and thermal gravimetric analysis （TGA） exhibited Tg and the temperature Tg at which 5 % mass losses occurring of polymer were 248 and 309 ℃, respectively. A reflective electro-optic （EO） modulator using this polymer was fabricated. The optical nonlinearities were determined to be d33 = 5. 209×10^-9 esu （poling voltage of 3.6 kV, 205 ℃） and d33 =7. 418×10^-9esu （poling voltage of 3. 8 kV, 210 ℃） by the second harmonic generation method in in-situ condition at a fundamental wavelength of 1 064 nm. The EO coefficients 733 of the polymer layer in the EO modulator were determined to be 2. 182 pm/V （poling voltage of 3.6 kV, 205 ℃） and 3. 107 pm/V （poling voltage of 3.8 kV, 210 ℃） at 1064 nm by an attenuated-total-reflection （ATR） method.展开更多
文摘Thin transparent oxide conducting films(TCOFs)of titanium and gallium substituted zinc oxide(TGZO)were fabricated via radio frequency(RF)magnetron sputtering technique.The effects of RF power on electrical,linear and nonlinear optical characteristics were investigated by Hall tester,Ultraviolet(UV)-visible spectrophotometer and optical characterization method.The results indicate that RF power significantly influences the electrical and optical properties of the deposited films.As RF power raises,the resistivity and Urbach energy fall initially and then rise,while the figure of merit,mean visible transmittance and optical bandgap show the reverse variation trend.At RF power of 190 W,the TGZO sample exhibits the highest electro-optical properties,with the maximum figure of merit(1.14×10^(4)Ω-1∙cm^(-1)),mean visible transmittance(86.9%)and optical bandgap(3.50 eV),the minimum resistivity(6.26×10^(-4)Ω∙cm)and Urbach energy(174.23 meV).In addition,the optical constants of the deposited films were determined by the optical spectrum fitting method,and the RF power dependence of nonlinear optical properties was studied.It is observed that all the thin films exhibit normal dispersion characteristics in the visible region,and the nonlinear optical parameters are greatly affected by the RF power in the ultraviolet region.
基金Jiangsu Planned Projects for Postdoctoral ResearchFunds(No0602037B)the Natural Science Foundation of Higher Edu-cation Institutions of Jiangsu Province (No05KJB150016)+1 种基金the Nation-al Natural Science Foundation of China (No50377005)the Fund ofJiangsu University (No06JDG015)
文摘The fluorine-containing organic polymer was synthesized from 3, 3＇, 4, 4＇-Bisphenyltetracarboxylic （BPDA）, and 2,2-Bis （3-amino-4-hydroxyyphenyl） hexafluoropropane （6FHP）. It is a first-step preparation of a preimided hydroxy-containing polyimide, followed by the covalent bonding of an active chromophore, dispersed red 19 （DR19）, onto the backbone of the polyimide via the Mitsunobu reaction. The nonlinear optical （NLO） containing polyimide was synthesized. The differential scanning calorimeter （DSC）and thermal gravimetric analysis （TGA） exhibited Tg and the temperature Tg at which 5 % mass losses occurring of polymer were 248 and 309 ℃, respectively. A reflective electro-optic （EO） modulator using this polymer was fabricated. The optical nonlinearities were determined to be d33 = 5. 209×10^-9 esu （poling voltage of 3.6 kV, 205 ℃） and d33 =7. 418×10^-9esu （poling voltage of 3. 8 kV, 210 ℃） by the second harmonic generation method in in-situ condition at a fundamental wavelength of 1 064 nm. The EO coefficients 733 of the polymer layer in the EO modulator were determined to be 2. 182 pm/V （poling voltage of 3.6 kV, 205 ℃） and 3. 107 pm/V （poling voltage of 3.8 kV, 210 ℃） at 1064 nm by an attenuated-total-reflection （ATR） method.