全氟庚烷端基聚丙烯酸的制备及其水溶液的表面张力

Five samples of perfluoroheptyl end capped polyacrylic acid ( F P A A) having ahigh surface activity were prepared by free radicalpolymerization ofacrylicacid . Theinitiatorwas perfluorooctanoyl peroxide which produced the free radicalof heptyl at 45 ℃. The yieldsof F P A A were in the range of 10 % to 25 % . The weight average molecular weights were2 62 ×104 to 7 99 ×104 and the polydispersity indexes were 1 97 to 5 64 ,depending on theconcentration of the initiator in the monomer. The surface tension was about 15m N/m at30 ℃forthe aqueous solution of F P A Awith the weight average molecular weight2 62 ×104in the concentration of about 0 01g/ m L. The molecular areas of F P A A at the air waterinterface under the condition ofcritical micelle concentration were 3 2 to 4 6n m2 ,which areobviously larger than the area per molecule of perfluorooctanoic acid (2 14nm 2) and muchsmaller than that of ordinary polyacrylic acid (83 4nm 2) . It means that the polymermoleculesin the surface adsorbed layer form the brush structure because of the special effectof the perfluoroalkyl groups at the chain ends .

全氟庚烷作为纸张脱酸载体的安全有效性研究

近现代纸质文献脱酸过程中所使用的溶剂需要谨慎、科学。总览既有的脱酸用溶剂体系,氟碳溶剂被视为良好的脱酸用溶剂。人工模拟常用的脱酸过程,使用全氟庚烷作为纸张脱酸用溶剂,并对酸化纸张进行处理,并将处理前后纸张在(105±2)℃条件下进行干热老化。考察处理前后纸张的酸度情况、机械性能、颜色变化等,从而确定全氟庚烷作为脱酸载体在近现代纸质文献脱酸过程中的使用安全性。利用全氟庚烷-氢氧化镁体系对酸化的纸质文献进行脱酸处理。经处理后,纸张的pH值和碱储量有很好的提升,可见全氟庚烷作为脱酸载体可用于文献脱酸。

全氟庚烷对木材表面环氧生漆性能的影响

通过测试附着力、涂膜硬度、涂膜光泽度、涂膜色差和涂膜耐水性能等,研究了全氟庚烷的添加量对天然生漆性能的影响。研究结果表明全氟庚烷的添加量对天然生漆的干燥时间和附着力没有明显影响,当全氟庚烷的添加量在2%以下时,天然生漆涂膜的硬度为2H;当添加量为4%时,涂膜光泽度提升最多,达到17.3%。另一方面,全氟庚烷的添加量在3%时,涂膜的耐水性最差。当全氟庚烷含量为2%时,天然生漆综合性能最佳。

丝织物的大气压等离子体液相沉积处理

为提高丝织物表面的拒水、拒油性能,较好地控制沉积涂层的质量,将等离子体与液态沉积液结合,采用介质阻挡放电装置,利用高频高压电源在大气压下通入惰性气体氦(He)产生辉光放电等离子体,通过超声喷嘴将液相单体雾化并喷射入等离子体区域,使之在处理物表面上进行等离子体沉积聚合。应用此工艺对丝织物处理,将全氟庚烷单体经过超声雾化,注入大气压辉光放电区域中,实现了在丝织物表面沉积拒水性涂层。通过SEM观察和ATR-FTIR以及接触角测量,分析处理前后纤维表面形态和结构的变化,得出在不同工艺参数下丝织物表面的全氟庚烷沉积率变化规律。结果表明,纤维表面成功沉积致密膜层,织物表面水接触角增大,拒水性能得到极大的改善。