Slurry processing experiments were performed with AlSi7Mg0.6 to identify the globularization mechanisms.The melt sample water quenched slightly above the liquidus point is predominantly dendritic while that cooled int...Slurry processing experiments were performed with AlSi7Mg0.6 to identify the globularization mechanisms.The melt sample water quenched slightly above the liquidus point is predominantly dendritic while that cooled into the semi-solid temperature range internally via stirring the melt with a rotating cylindrical block of the alloy itself becomes fully globular.The globules are much smaller when internal cooling and stirring are employed longer to achieve higher solid fractions before casting.Coarse dendrite fragments of various sizes are revealed,in the case of stirring after an initial fraction of solid is first formed without the benefit of additional internal cooling.展开更多
This paper studies the robust H∞ disturbance attenuation with internal stability for uncertain nonlinear control systems. By adding one power integrator technique, this paper designs a explicit smooth robust dynamic ...This paper studies the robust H∞ disturbance attenuation with internal stability for uncertain nonlinear control systems. By adding one power integrator technique, this paper designs a explicit smooth robust dynamic feedback law while rejecting the disturbance to any specified degree of accuracy. Further, the example and simulation results show the effectiveness of the proposed schemes.展开更多
基金the State Planning Organization of Turkey for the financial support
文摘Slurry processing experiments were performed with AlSi7Mg0.6 to identify the globularization mechanisms.The melt sample water quenched slightly above the liquidus point is predominantly dendritic while that cooled into the semi-solid temperature range internally via stirring the melt with a rotating cylindrical block of the alloy itself becomes fully globular.The globules are much smaller when internal cooling and stirring are employed longer to achieve higher solid fractions before casting.Coarse dendrite fragments of various sizes are revealed,in the case of stirring after an initial fraction of solid is first formed without the benefit of additional internal cooling.
基金The research is supported by the Natural Science Foundation of Henan Province under Grant No. 2007120005.
文摘This paper studies the robust H∞ disturbance attenuation with internal stability for uncertain nonlinear control systems. By adding one power integrator technique, this paper designs a explicit smooth robust dynamic feedback law while rejecting the disturbance to any specified degree of accuracy. Further, the example and simulation results show the effectiveness of the proposed schemes.