A three-dimensional finite-element model of slab continuous casting mold was conducted to clarify the effect of cooling structure on thermal behavior of copper plates. The results show that temperature distribution of...A three-dimensional finite-element model of slab continuous casting mold was conducted to clarify the effect of cooling structure on thermal behavior of copper plates. The results show that temperature distribution of hot surface is mainly governed by cooling structure and heat-transfer conditions. For hot surface centricity, maximum surface temperature promotions are 30 ℃and 15 ℃ with thickness increments of copper plates of 5 mm and nickel layers of 1 ram, respectively. The surface temperature without nickel layers is depressed by 10 ℃ when the depth increment of water slots is 2 mm and that with nickel layers adjacent to and away from mold outlet is depressed by 7℃ and 5 ℃, respectively. The specific trend of temperature distribution of transverse sections of copper plates is nearly free of cooling structure, but temperature is changed and its law is similar to the corresponding surface temperature.展开更多
AlN films with preferred c-axis orientation are deposited on Si substrates using the radio frequency(RF) magnetron sputtering method.The post-processing is carried out under the cooling conditions including high vacuu...AlN films with preferred c-axis orientation are deposited on Si substrates using the radio frequency(RF) magnetron sputtering method.The post-processing is carried out under the cooling conditions including high vacuum,low vacuum under deposition gas ambient and low vacuum under dynamic N2 ambient.Structures and morphologies of the films are analyzed by X-ray diffraction(XRD) and atomic force microscopy(AFM).The hardness and Young's modulus are investigated by the nanoindenter.The experimental results indicate that the(100) and(110) peak intensities decrease in the XRD spectra and the root-mean-square of roughness(Rrms) of the film decreases gradually with the increase of the cooling rate.The maximum values of the hardness and Young modulus are obtained by cooling in low vacuum under deposition gas ambient.The reason for orientation variation of the films is explained from the perspective of the Al-N bond formation.展开更多
基金Project(51004031) supported by the National Natural Science Foundation of ChinaProject(50925415) supported by the National Outstanding Young Scientist Foundation of China+1 种基金Project(20100042120012) supported by the Special Research Fund for Doctoral Programs of Ministry of Education of ChinaProject(N090402022) supported by the Fundamental Research Funds for the Central Universities of China
文摘A three-dimensional finite-element model of slab continuous casting mold was conducted to clarify the effect of cooling structure on thermal behavior of copper plates. The results show that temperature distribution of hot surface is mainly governed by cooling structure and heat-transfer conditions. For hot surface centricity, maximum surface temperature promotions are 30 ℃and 15 ℃ with thickness increments of copper plates of 5 mm and nickel layers of 1 ram, respectively. The surface temperature without nickel layers is depressed by 10 ℃ when the depth increment of water slots is 2 mm and that with nickel layers adjacent to and away from mold outlet is depressed by 7℃ and 5 ℃, respectively. The specific trend of temperature distribution of transverse sections of copper plates is nearly free of cooling structure, but temperature is changed and its law is similar to the corresponding surface temperature.
基金supported by the National Natural Science Foundation of China (No.50972105)Tianjin Natural Science Foundation (Nos.09JCZDJC16500,08JCZDJC22700 and 10SYSYJC27700)
文摘AlN films with preferred c-axis orientation are deposited on Si substrates using the radio frequency(RF) magnetron sputtering method.The post-processing is carried out under the cooling conditions including high vacuum,low vacuum under deposition gas ambient and low vacuum under dynamic N2 ambient.Structures and morphologies of the films are analyzed by X-ray diffraction(XRD) and atomic force microscopy(AFM).The hardness and Young's modulus are investigated by the nanoindenter.The experimental results indicate that the(100) and(110) peak intensities decrease in the XRD spectra and the root-mean-square of roughness(Rrms) of the film decreases gradually with the increase of the cooling rate.The maximum values of the hardness and Young modulus are obtained by cooling in low vacuum under deposition gas ambient.The reason for orientation variation of the films is explained from the perspective of the Al-N bond formation.