The influences of rolling reduction and aluminum sheet initial thickness(AIT)on the thickness fluctuation of aluminum layer(TFA)of embedded aluminum?steel composite sheet produced by cold roll bonding were investigate...The influences of rolling reduction and aluminum sheet initial thickness(AIT)on the thickness fluctuation of aluminum layer(TFA)of embedded aluminum?steel composite sheet produced by cold roll bonding were investigated,the formation mechanism of TFA was analyzed and method to improve the thickness uniformity of the aluminum layer was proposed.The results showed that when the reduction increased,TFA increased gradually.When the reduction was lower than40%,AIT had negligible effect on the TFA,while TFA increased with the decrease of AIT when the reduction was higher than40%.The non-uniformities of the steel surface deformation and the interfacial bonding extent caused by the work-hardened steel surface layer,were the main reasons for the formation of TFA.Adopting an appropriate surface treatment can help to decrease the hardening extent of the steel surface for improving the deformation uniformity during cold roll bonding process,which effectively improved the aluminum thickness uniformity of the embedded aluminum/steel composite sheets.展开更多
基金Project(2013AA031301)supported by National High-tech Research and Development Program of ChinaProject(51104016)supported by National Natural Science Foundation of ChinaProject(BM2014006)supported by Jiangsu Key Laboratory for Clad Materials,China
文摘The influences of rolling reduction and aluminum sheet initial thickness(AIT)on the thickness fluctuation of aluminum layer(TFA)of embedded aluminum?steel composite sheet produced by cold roll bonding were investigated,the formation mechanism of TFA was analyzed and method to improve the thickness uniformity of the aluminum layer was proposed.The results showed that when the reduction increased,TFA increased gradually.When the reduction was lower than40%,AIT had negligible effect on the TFA,while TFA increased with the decrease of AIT when the reduction was higher than40%.The non-uniformities of the steel surface deformation and the interfacial bonding extent caused by the work-hardened steel surface layer,were the main reasons for the formation of TFA.Adopting an appropriate surface treatment can help to decrease the hardening extent of the steel surface for improving the deformation uniformity during cold roll bonding process,which effectively improved the aluminum thickness uniformity of the embedded aluminum/steel composite sheets.