The effect of cold rolling reduction(50%-90%)on the grain structures of solutionized 1445 Al-Li alloy sheet at525-575 ℃ was investigated through electron backscatter diffraction(EBSD).Although the solutionization tem...The effect of cold rolling reduction(50%-90%)on the grain structures of solutionized 1445 Al-Li alloy sheet at525-575 ℃ was investigated through electron backscatter diffraction(EBSD).Although the solutionization temperature is elevated to 575 ℃,the sheet is not completely recrystallized.The main recrystallization model is subgrain coalescence and growth,and the non-recrystallization is due to the formed nano-sized Al3(Sc,Zr)dispersoids,which pin the grain boundaries,subgrain boundaries and dislocations.With increasing the cold rolling reduction,the fraction and size of the recrystallized grains in the sheet solutionized at525 ℃ are decreased,but the fraction of the subgrains is increased,leading to a decrease in the fraction of the deformed structures.Meanwhile,the number fraction of high-angle boundaries(HABs)is increased.Due to the decreased fraction of the deformed structures and increased fraction of the HABs,the T8-aged 1445 Al-Li alloy sheet displays a decrease trend in the strength and heterogeneity with increasing the cold rolling reduction.At higher solutionization temperature of 575 ℃,the fraction of the recrystallized grains and their size are obviously increased.展开更多
文摘The effect of cold rolling reduction(50%-90%)on the grain structures of solutionized 1445 Al-Li alloy sheet at525-575 ℃ was investigated through electron backscatter diffraction(EBSD).Although the solutionization temperature is elevated to 575 ℃,the sheet is not completely recrystallized.The main recrystallization model is subgrain coalescence and growth,and the non-recrystallization is due to the formed nano-sized Al3(Sc,Zr)dispersoids,which pin the grain boundaries,subgrain boundaries and dislocations.With increasing the cold rolling reduction,the fraction and size of the recrystallized grains in the sheet solutionized at525 ℃ are decreased,but the fraction of the subgrains is increased,leading to a decrease in the fraction of the deformed structures.Meanwhile,the number fraction of high-angle boundaries(HABs)is increased.Due to the decreased fraction of the deformed structures and increased fraction of the HABs,the T8-aged 1445 Al-Li alloy sheet displays a decrease trend in the strength and heterogeneity with increasing the cold rolling reduction.At higher solutionization temperature of 575 ℃,the fraction of the recrystallized grains and their size are obviously increased.