Based on hot metal pretreatment （HMPT）-basic oxygen furnace （BOF）-Rheinstahl Heraeus （RH）-compact strip production （CSP） process, parameters controlling on cold rolling deep drawing substrate SPHE were investi...Based on hot metal pretreatment （HMPT）-basic oxygen furnace （BOF）-Rheinstahl Heraeus （RH）-compact strip production （CSP） process, parameters controlling on cold rolling deep drawing substrate SPHE were investigated during smelting and rolling process by composition design and technology control. The influence of parameters on chemical compositions, mechanical properties and microstructure was revealed by scanning electron microscope （SEM）. The results show that, 1） main chemical components in SPHE are w（C）_〈40×10^-6, w（Si）_〈 0.01%, w（S）_〈0.009%, w（N）〈20×10^-6, w（O）〈_ 25×10^-6; 2） main mechanical properties of the SPHE are Crs=274 MPa, 00=334 MPa, A=48.9%; 3） main performances of deep drawing quality （DDQ） grade steel produced by SPHE are as follows, transversely crs=167 MPa, 00=298 MPa, n=0.219, r=2.46; vertically σs=166 MPa, 00=298 MPa, n=0.226, r=2.39; in 45° direction σ=171 MPa, 00=308 MPa, n=0.214, t=2.26; 4） microstrueture of DDQ is ferrite, average grain size is Grade 7.5, and inclusion size is 3-10μm.展开更多
基金Project(50971135) supported by the National Natural Science Foundation of China
文摘Based on hot metal pretreatment （HMPT）-basic oxygen furnace （BOF）-Rheinstahl Heraeus （RH）-compact strip production （CSP） process, parameters controlling on cold rolling deep drawing substrate SPHE were investigated during smelting and rolling process by composition design and technology control. The influence of parameters on chemical compositions, mechanical properties and microstructure was revealed by scanning electron microscope （SEM）. The results show that, 1） main chemical components in SPHE are w（C）_〈40×10^-6, w（Si）_〈 0.01%, w（S）_〈0.009%, w（N）〈20×10^-6, w（O）〈_ 25×10^-6; 2） main mechanical properties of the SPHE are Crs=274 MPa, 00=334 MPa, A=48.9%; 3） main performances of deep drawing quality （DDQ） grade steel produced by SPHE are as follows, transversely crs=167 MPa, 00=298 MPa, n=0.219, r=2.46; vertically σs=166 MPa, 00=298 MPa, n=0.226, r=2.39; in 45° direction σ=171 MPa, 00=308 MPa, n=0.214, t=2.26; 4） microstrueture of DDQ is ferrite, average grain size is Grade 7.5, and inclusion size is 3-10μm.