A Pb-0.08Ca-2Sn alloy was subjected to rolling at room temperature to different final thicknesses.Annealing treatments at temperature ranging from 80 to 120 °C led to recrystallization of the samples as shown by ...A Pb-0.08Ca-2Sn alloy was subjected to rolling at room temperature to different final thicknesses.Annealing treatments at temperature ranging from 80 to 120 °C led to recrystallization of the samples as shown by resistivity and micro-hardness measurements.The deformation texture determined through X-ray diffraction is qualitatively the Brass type.The measured Lankford anisotropy parameter R and its evolution are close to the determined one using a self consistent approach.The R value evolution with angle to rolling direction shows the presence of planar anisotropy and poor drawability.The recrystallization in annealing at 80-120 °C is achieved within time period up to 3×104 s.The recrystallization texture is a retained deformation texture with an emerging Cube component.展开更多
The Al-Zn-Mg-Cu alloy strip can be successfully fabricated by twin roll casting. In order to determine the effect of thickness reduction and heat treatment temperature on the recrystallization behavior, the strips wer...The Al-Zn-Mg-Cu alloy strip can be successfully fabricated by twin roll casting. In order to determine the effect of thickness reduction and heat treatment temperature on the recrystallization behavior, the strips were rolled and subsequently heat treated under various conditions. As a result, a fine grained microstructure （average grain size -13 μm, average grain aspect ratio -1.7） and high mechanical properties （UTS ≥360 MPa, δ ≥20%） were obtained by cold rolling with thickness reduction of 60% and heat treatment at 500 ℃ for 1 h. Also, the effect of the microstructure on mechanical properties of the Al-Zn-Mg-Cu alloy strip was discussed. Consequently, the low cost and high strength Al-Zn-Mg-Cu alloy sheet can be fabricated by twin roll casting by proper thermo-mechanical processes.展开更多
The microstructures and mechanical properties of Mg-8Li and Mg-8Li-2Al-2RE alloy sheets were evaluated after cold rolling.Both alloys contain α-phase and β-phase which consists of a solid solution of Mg in BCC Li.Th...The microstructures and mechanical properties of Mg-8Li and Mg-8Li-2Al-2RE alloy sheets were evaluated after cold rolling.Both alloys contain α-phase and β-phase which consists of a solid solution of Mg in BCC Li.The proportion ofβ-phase in both alloys is approximately 60%.Theα-phase andβ-phase are elongated approximately parallel to the rolling direction and there is no sign of recrystallization even after being annealed at 200℃for 1 h.The yield strength of Mg-8Li-2Al-2RE sheets is about 165 MPa with elongation of 35%along rolling direction,while the yield strength is about 187 MPa with elongation of 21%along the direction titled 45ü to rolling direction.Theα-phase in both alloys exhibits basal texture,and the intensity of basal texture in Mg-8Li is larger than that in Mg-8Li-2Al-2RE.However,theβ-phase shows(100)texture,and the intensity of(100)texture in Mg-8Li is twice of that in Mg-8Li-2Al-2RE.It could be attributed to the existence of RE-containing particles in Mg-8Li-2Al-2RE.展开更多
文摘A Pb-0.08Ca-2Sn alloy was subjected to rolling at room temperature to different final thicknesses.Annealing treatments at temperature ranging from 80 to 120 °C led to recrystallization of the samples as shown by resistivity and micro-hardness measurements.The deformation texture determined through X-ray diffraction is qualitatively the Brass type.The measured Lankford anisotropy parameter R and its evolution are close to the determined one using a self consistent approach.The R value evolution with angle to rolling direction shows the presence of planar anisotropy and poor drawability.The recrystallization in annealing at 80-120 °C is achieved within time period up to 3×104 s.The recrystallization texture is a retained deformation texture with an emerging Cube component.
基金supported by a grant from the Korea Institute of Materials Science (Project No. PNK 3250)
文摘The Al-Zn-Mg-Cu alloy strip can be successfully fabricated by twin roll casting. In order to determine the effect of thickness reduction and heat treatment temperature on the recrystallization behavior, the strips were rolled and subsequently heat treated under various conditions. As a result, a fine grained microstructure （average grain size -13 μm, average grain aspect ratio -1.7） and high mechanical properties （UTS ≥360 MPa, δ ≥20%） were obtained by cold rolling with thickness reduction of 60% and heat treatment at 500 ℃ for 1 h. Also, the effect of the microstructure on mechanical properties of the Al-Zn-Mg-Cu alloy strip was discussed. Consequently, the low cost and high strength Al-Zn-Mg-Cu alloy sheet can be fabricated by twin roll casting by proper thermo-mechanical processes.
基金Project(2007CB613704)supported by the National Basic Research Program of ChinaProject(50874100)supported by the National Natural Science Foundation of China
文摘The microstructures and mechanical properties of Mg-8Li and Mg-8Li-2Al-2RE alloy sheets were evaluated after cold rolling.Both alloys contain α-phase and β-phase which consists of a solid solution of Mg in BCC Li.The proportion ofβ-phase in both alloys is approximately 60%.Theα-phase andβ-phase are elongated approximately parallel to the rolling direction and there is no sign of recrystallization even after being annealed at 200℃for 1 h.The yield strength of Mg-8Li-2Al-2RE sheets is about 165 MPa with elongation of 35%along rolling direction,while the yield strength is about 187 MPa with elongation of 21%along the direction titled 45ü to rolling direction.Theα-phase in both alloys exhibits basal texture,and the intensity of basal texture in Mg-8Li is larger than that in Mg-8Li-2Al-2RE.However,theβ-phase shows(100)texture,and the intensity of(100)texture in Mg-8Li is twice of that in Mg-8Li-2Al-2RE.It could be attributed to the existence of RE-containing particles in Mg-8Li-2Al-2RE.