A type of biomedical magnesium alloy Mg-3Zn-1Y-0.6Zr-0.5Ca was cast and extruded at three extrusion temperatures of 270, 300 and 330 °C. The microstructure and mechanical properties of the cast and extruded alloy...A type of biomedical magnesium alloy Mg-3Zn-1Y-0.6Zr-0.5Ca was cast and extruded at three extrusion temperatures of 270, 300 and 330 °C. The microstructure and mechanical properties of the cast and extruded alloys, tailored at different extrusion parameters, were investigated using tensile tests, optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, X-ray diffractometry, transmission electron microscopy and electron backscattered diffraction. Optimum comprehensive mechanical properties are achieved in the alloy extruded at 270 °C, the ultimate tensile strength and the elongation reach 315 MPa and 26%, respectively, which is deemed to be associated with the grain refinement, weak basal texture and second phases strengthening. After hot extrusion, extensive dynamic recrystallization is found in the Mg-3Zn-1Y-0.6Zr-0.5Ca alloy. Continuous Mg3YZn6 phase bands are gradually broken into discontinuous chain-like or dot-like structures, and the grains distribute more uniformly. The as-extruded Mg-3Zn-1Y-0.6Zr-0.5Ca alloy exhibits a weak texture with (0001) basal planes parallel to the extrusion direction.展开更多
基金Projects(51574175,51474153) supported by the National Natural Science Foundation of China
文摘A type of biomedical magnesium alloy Mg-3Zn-1Y-0.6Zr-0.5Ca was cast and extruded at three extrusion temperatures of 270, 300 and 330 °C. The microstructure and mechanical properties of the cast and extruded alloys, tailored at different extrusion parameters, were investigated using tensile tests, optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, X-ray diffractometry, transmission electron microscopy and electron backscattered diffraction. Optimum comprehensive mechanical properties are achieved in the alloy extruded at 270 °C, the ultimate tensile strength and the elongation reach 315 MPa and 26%, respectively, which is deemed to be associated with the grain refinement, weak basal texture and second phases strengthening. After hot extrusion, extensive dynamic recrystallization is found in the Mg-3Zn-1Y-0.6Zr-0.5Ca alloy. Continuous Mg3YZn6 phase bands are gradually broken into discontinuous chain-like or dot-like structures, and the grains distribute more uniformly. The as-extruded Mg-3Zn-1Y-0.6Zr-0.5Ca alloy exhibits a weak texture with (0001) basal planes parallel to the extrusion direction.