Two kinds of high strength-damping aluminum alloys （LZ7） were fabricated by rapid solidification and powder metallurgy （RS-PM） process. One material was extruded to profile aluminum directly and the other was extr...Two kinds of high strength-damping aluminum alloys （LZ7） were fabricated by rapid solidification and powder metallurgy （RS-PM） process. One material was extruded to profile aluminum directly and the other was extruded to bar and then rolled to sheet. The damping capacity over a temperature range of 25-300 ℃was studied with damping mechanical thermal analyzer （DMTA） and the microstructures were investigated by optical microscopy （OM）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The experimental results show that the damping capacity increases with the test temperature elevating. Internal friction value of rolled sheet aluminum is up to 11.5×10^-2 and that of profile aluminum is as high as 6.0×10^-2 and 7.5×10^-2 at 300 ℃, respectively. Microstructure analysis shows the shape of precipitation phase of rolled alloy is more regular and the distribution is more homogeneous than that of profile alloy. Meanwhile, the interface between particulate and matrix of rolled sheet alloy is looser than that of profile alloy. Maybe the differences at interface can explain why damping capacity of rolled sheet alloy is higher than that of profile alloys at high temperature （above 120 ℃）.展开更多
Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive ...Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive mined-out gobs, enormous ore body under roadway and low recovery ratio of Yongshaba Mine, Kaiyang Phosphor Mine Group, Guizhou Province, China. An appropriate backfill system and craflwork were designed, using shattering milling method to crush gypsum, double-axles mixing and strong activation mixing way to mix slurry, cemented slurry and mullock backfill alternately process. The results show that gypsum is fit for backfilling afterwards by adding fly ash, though it is not an ideal aggregate for fine granule and coagulate retardation. The suggested dosage （the mass ratio of cement to fly ash to gypsum） is 1：1：6-1：1：8 with mass fraction of solid materials 60%-63%. Slurry is transported in suspend state with non-plastic strength, and then in concretion state after backfilling. The application to mine shows the technology is feasible, and gypsum utilization ratio is up to 100%. Transportation and backfill effect is very good for paste-like slurry and drenching cemented slurry into mullock, and the compressive strength and recovery ratio are 2.0 MPa and 82.6%, respectively, with the maximum subsidence of surface only 1.307 mm. Furthermore, the investment of system is about 7 × 10^6 yuan （RMB）, only 1/10 of that of traditional paste backfill system.展开更多
Selective laser melting(SLM)technology is the prevailing method of manufacturing components with complex geometries.However,the cost of the additive manufacturing(AM)fine powder is relatively high,which significantly ...Selective laser melting(SLM)technology is the prevailing method of manufacturing components with complex geometries.However,the cost of the additive manufacturing(AM)fine powder is relatively high,which significantly limits the development of the SLM.In this study,the 316L fine powder and coarse powder with a mass ratio of 80:20,70:30 and 60:40 were mixed using a ball milling and the samples with a relative density greater than 97%were prepared by SLM.The results show that the intricate temperature gradients and surface tension gradients in SLM will produce Marangoni flow,forming a typical molten pool morphology,cellular and strip subgrain structures.And as the proportion of coarse powder increases,the scanning track morphology changes from smooth to undulating;the morphology of the molten pool and subgrain structure are weakened.Meanwhile,the unmelted particles appear on the surface of the SLM sample.On the premise of an introducing appropriate amount of large particle size powder(20%),the SLM samples still have good mechanical properties(662 MPa,47%).展开更多
The Al-Ni-Y alloy powder was prepared by rapid solidification technology of inert gas atomization. The diameter of amorphous powder is less than 12 μm. The effects of atomization gas on cooling velocity, morphology,...The Al-Ni-Y alloy powder was prepared by rapid solidification technology of inert gas atomization. The diameter of amorphous powder is less than 12 μm. The effects of atomization gas on cooling velocity, morphology, microstructure and microhardness of powder and fine powder ratio were investigated.The results show that the morphology, microstructure and microhardness of powder and fine powder ratio are affected by cooling velocity changed through atomization gas. The cooling velocity of inert gas atomization is more than 1×10~4 K/s. The larger the cooling velocity, the finer the powder, and the smoother the surface of powder; the smaller the diameter of powder, the larger the microhardness of powder.展开更多
This work is an experimental approach based on the method of experimental plans to determine a specific formulation of a resin concrete. In this study, an unsaturated polyester resin （thermosetting resin） was used w...This work is an experimental approach based on the method of experimental plans to determine a specific formulation of a resin concrete. In this study, an unsaturated polyester resin （thermosetting resin） was used with two types of mineral fillers （dune sand and crushed sand）, and with the addition of a marble powder to ensure the continuity of the particle size mixing granular. The lack of the methods for developing this kind of composite materials, had led us to perform an initial experimental approach to define the experimental field, that is to say determine the mass proportions of the various compounds of mixture of our study. In the second approach, we have established and implemented fully experimental plans with three factors namely： factor （1）： sand, factor （2）： resin, factor （3）： marble powder. Test results being the density of polymer concrete and the mechanical resistances. Finally, multi-parameters regression allowed us to determine predictive mathematical models for the different responses of the study. Tests results showed that at three days we got a tensile strength of about 16 MPa with a resin concrete density of 1.9 g/cm3. This shows the advantages of this material.展开更多
基金Project (50971012) supported by the National Natural Science Foundation of China
文摘Two kinds of high strength-damping aluminum alloys （LZ7） were fabricated by rapid solidification and powder metallurgy （RS-PM） process. One material was extruded to profile aluminum directly and the other was extruded to bar and then rolled to sheet. The damping capacity over a temperature range of 25-300 ℃was studied with damping mechanical thermal analyzer （DMTA） and the microstructures were investigated by optical microscopy （OM）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The experimental results show that the damping capacity increases with the test temperature elevating. Internal friction value of rolled sheet aluminum is up to 11.5×10^-2 and that of profile aluminum is as high as 6.0×10^-2 and 7.5×10^-2 at 300 ℃, respectively. Microstructure analysis shows the shape of precipitation phase of rolled alloy is more regular and the distribution is more homogeneous than that of profile alloy. Meanwhile, the interface between particulate and matrix of rolled sheet alloy is looser than that of profile alloy. Maybe the differences at interface can explain why damping capacity of rolled sheet alloy is higher than that of profile alloys at high temperature （above 120 ℃）.
基金Project(2006BAB02A03)supported by the National Key Technology Research and Development ProgramProject(08MX16)supported by Mittal Scientific and Technological Innovation Projects of Central South University during 2008
文摘Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive mined-out gobs, enormous ore body under roadway and low recovery ratio of Yongshaba Mine, Kaiyang Phosphor Mine Group, Guizhou Province, China. An appropriate backfill system and craflwork were designed, using shattering milling method to crush gypsum, double-axles mixing and strong activation mixing way to mix slurry, cemented slurry and mullock backfill alternately process. The results show that gypsum is fit for backfilling afterwards by adding fly ash, though it is not an ideal aggregate for fine granule and coagulate retardation. The suggested dosage （the mass ratio of cement to fly ash to gypsum） is 1：1：6-1：1：8 with mass fraction of solid materials 60%-63%. Slurry is transported in suspend state with non-plastic strength, and then in concretion state after backfilling. The application to mine shows the technology is feasible, and gypsum utilization ratio is up to 100%. Transportation and backfill effect is very good for paste-like slurry and drenching cemented slurry into mullock, and the compressive strength and recovery ratio are 2.0 MPa and 82.6%, respectively, with the maximum subsidence of surface only 1.307 mm. Furthermore, the investment of system is about 7 × 10^6 yuan （RMB）, only 1/10 of that of traditional paste backfill system.
基金Projects(51671152,51304153,51504191,51874225)supported by the National Natural Science Foundation of ChinaProject(14JK512)supported by the Natural Science Foundation of Shaanxi Educational Committee,China+1 种基金Project(18JC019)supported by Shaanxi Provincial Department of Education Industrialization Project,ChinaProject(14JK1512)supported by Shaanxi Provincial Department of Education Natural Science Special Project,China
文摘Selective laser melting(SLM)technology is the prevailing method of manufacturing components with complex geometries.However,the cost of the additive manufacturing(AM)fine powder is relatively high,which significantly limits the development of the SLM.In this study,the 316L fine powder and coarse powder with a mass ratio of 80:20,70:30 and 60:40 were mixed using a ball milling and the samples with a relative density greater than 97%were prepared by SLM.The results show that the intricate temperature gradients and surface tension gradients in SLM will produce Marangoni flow,forming a typical molten pool morphology,cellular and strip subgrain structures.And as the proportion of coarse powder increases,the scanning track morphology changes from smooth to undulating;the morphology of the molten pool and subgrain structure are weakened.Meanwhile,the unmelted particles appear on the surface of the SLM sample.On the premise of an introducing appropriate amount of large particle size powder(20%),the SLM samples still have good mechanical properties(662 MPa,47%).
文摘The Al-Ni-Y alloy powder was prepared by rapid solidification technology of inert gas atomization. The diameter of amorphous powder is less than 12 μm. The effects of atomization gas on cooling velocity, morphology, microstructure and microhardness of powder and fine powder ratio were investigated.The results show that the morphology, microstructure and microhardness of powder and fine powder ratio are affected by cooling velocity changed through atomization gas. The cooling velocity of inert gas atomization is more than 1×10~4 K/s. The larger the cooling velocity, the finer the powder, and the smoother the surface of powder; the smaller the diameter of powder, the larger the microhardness of powder.
文摘This work is an experimental approach based on the method of experimental plans to determine a specific formulation of a resin concrete. In this study, an unsaturated polyester resin （thermosetting resin） was used with two types of mineral fillers （dune sand and crushed sand）, and with the addition of a marble powder to ensure the continuity of the particle size mixing granular. The lack of the methods for developing this kind of composite materials, had led us to perform an initial experimental approach to define the experimental field, that is to say determine the mass proportions of the various compounds of mixture of our study. In the second approach, we have established and implemented fully experimental plans with three factors namely： factor （1）： sand, factor （2）： resin, factor （3）： marble powder. Test results being the density of polymer concrete and the mechanical resistances. Finally, multi-parameters regression allowed us to determine predictive mathematical models for the different responses of the study. Tests results showed that at three days we got a tensile strength of about 16 MPa with a resin concrete density of 1.9 g/cm3. This shows the advantages of this material.