In order to remove the low turbidity present in surface water, a novel metal-polysilicate coagulant was used to treat the raw water taken from Tanjiang River in Guangdong Province. This study on the effects of Al/Fe ...In order to remove the low turbidity present in surface water, a novel metal-polysilicate coagulant was used to treat the raw water taken from Tanjiang River in Guangdong Province. This study on the effects of Al/Fe molar ratio on the performance of a complex compound formed by polysilicic acid, aluminium and ferric salt (PAFS) showed that PAFS with Al/Fe ratio of 10:3 seemed to have the best coagulation performance in removing turbidity and color. Experimental results showed that under the conditions of polymerization time of 15 d, sedimentation time of 12 min, and pH of 6?8, PAFS with Al/Fe molar ratio of 10:3 had the best coagulation efficiency and lowest residual Al concentration. The turbid- ity decreased from 23.8 NTU to 3.23 NTU and the residual Al concentration was only 0.165 mg/L in the product water. It could be speculated that colloidal impurities and particulate Al were removed by adsorption bridging and electrical neu- tralization of long chain inorganic polymer coagulants.展开更多
Chitosan derived from crab shells, was used to prepare the graft polymer in aqueous solution with acrylamide （AM） and methacrylatoethyl trimethyl ammonium chloride （DMC） as raw materials and ceric ammonium nitrate...Chitosan derived from crab shells, was used to prepare the graft polymer in aqueous solution with acrylamide （AM） and methacrylatoethyl trimethyl ammonium chloride （DMC） as raw materials and ceric ammonium nitrate （CAN） as initiator. The flocculation ability of the resulting polymer （PCAD） was studied in waste water treatment experiments. Its properties were determined on the basis of the transmittance of waste water after flocculation. The effects of ehitosan and DMC content on PCAD＇s flocculation ability were studied. Floeculation experiments were also undertaken under various pH conditions. According to the experimental data, the flocculation ability could be improved when chitosan content decreased in the raw material, but the monomer conversion would decrease obviously. When the ehitosan＇s content was more than 65%, AM and DMC groups were less on each chitosan molecule. So PCAD＇s flocculation ability was poor. Similarly, high content of DMC would result in low monomer conversion and high flocculation ability. PCAD molecules with more DMC group had more positive charges. It was favorable to flocculation. However, monomer conversion would decrease with the increase of DMC content. The suitable conditions were that chitosan and DMC contents were 65% and 15-20%, respectively. The experiment data showed that PCAD had good flocculation ability under weak acidic condition. Its ability would be weakened by strong acidic or alkaline condition. The flocculation efficiency was the best at pH of 5.5 when PCAD＇s dosage was 8mg-Lk Compared with cationic polymer （the copolymer of AM and DMC, PAD）, PCAD showed better flocculation ability under acid and neutral conditions, but worse ability under alkaline condition.展开更多
The biopolymer flocculant （named PS-2） producing by Pseudomonas fluorescens was investigated. The PS-2 had high efficiency with small dosage, when dealing with kaolin suspension, formed larger floc, with big sedimen...The biopolymer flocculant （named PS-2） producing by Pseudomonas fluorescens was investigated. The PS-2 had high efficiency with small dosage, when dealing with kaolin suspension, formed larger floc, with big sedimentation rate, over a wide range of temperatures. Distributing of flocculating activity test showed that the biopolymer flocculant was an extracellular product. The composition analysis of purified biopolymer flocculant showed that it composed mainly of polysaccharide and nucleic acid. The content of polysaccharide was 86. 7%, which determined by using phenol-vitriol method, and the content of nucleic acid was 7.8%, which determined by UV absorption method. The biopolymer flocculant as a powder form showed much better stability than that as a supernatant. The character of biopolymer flocculant was stable even it was heated to 100℃ when it in acidic condition. The optimal conditions to flocculate kaolin suspension were as follows： pH 8-12, flocculant dosage lmL/L, and Ca^2＋ as the optimal cation.展开更多
基金Project (No. E9825) supported by the Natural Science Foundation of Heilongjiang Province,China
文摘In order to remove the low turbidity present in surface water, a novel metal-polysilicate coagulant was used to treat the raw water taken from Tanjiang River in Guangdong Province. This study on the effects of Al/Fe molar ratio on the performance of a complex compound formed by polysilicic acid, aluminium and ferric salt (PAFS) showed that PAFS with Al/Fe ratio of 10:3 seemed to have the best coagulation performance in removing turbidity and color. Experimental results showed that under the conditions of polymerization time of 15 d, sedimentation time of 12 min, and pH of 6?8, PAFS with Al/Fe molar ratio of 10:3 had the best coagulation efficiency and lowest residual Al concentration. The turbid- ity decreased from 23.8 NTU to 3.23 NTU and the residual Al concentration was only 0.165 mg/L in the product water. It could be speculated that colloidal impurities and particulate Al were removed by adsorption bridging and electrical neu- tralization of long chain inorganic polymer coagulants.
基金supported by Young Scientist Foundation (2008BS09001) from the Department of Science and Technology of Shandong Province
文摘Chitosan derived from crab shells, was used to prepare the graft polymer in aqueous solution with acrylamide （AM） and methacrylatoethyl trimethyl ammonium chloride （DMC） as raw materials and ceric ammonium nitrate （CAN） as initiator. The flocculation ability of the resulting polymer （PCAD） was studied in waste water treatment experiments. Its properties were determined on the basis of the transmittance of waste water after flocculation. The effects of ehitosan and DMC content on PCAD＇s flocculation ability were studied. Floeculation experiments were also undertaken under various pH conditions. According to the experimental data, the flocculation ability could be improved when chitosan content decreased in the raw material, but the monomer conversion would decrease obviously. When the ehitosan＇s content was more than 65%, AM and DMC groups were less on each chitosan molecule. So PCAD＇s flocculation ability was poor. Similarly, high content of DMC would result in low monomer conversion and high flocculation ability. PCAD molecules with more DMC group had more positive charges. It was favorable to flocculation. However, monomer conversion would decrease with the increase of DMC content. The suitable conditions were that chitosan and DMC contents were 65% and 15-20%, respectively. The experiment data showed that PCAD had good flocculation ability under weak acidic condition. Its ability would be weakened by strong acidic or alkaline condition. The flocculation efficiency was the best at pH of 5.5 when PCAD＇s dosage was 8mg-Lk Compared with cationic polymer （the copolymer of AM and DMC, PAD）, PCAD showed better flocculation ability under acid and neutral conditions, but worse ability under alkaline condition.
文摘The biopolymer flocculant （named PS-2） producing by Pseudomonas fluorescens was investigated. The PS-2 had high efficiency with small dosage, when dealing with kaolin suspension, formed larger floc, with big sedimentation rate, over a wide range of temperatures. Distributing of flocculating activity test showed that the biopolymer flocculant was an extracellular product. The composition analysis of purified biopolymer flocculant showed that it composed mainly of polysaccharide and nucleic acid. The content of polysaccharide was 86. 7%, which determined by using phenol-vitriol method, and the content of nucleic acid was 7.8%, which determined by UV absorption method. The biopolymer flocculant as a powder form showed much better stability than that as a supernatant. The character of biopolymer flocculant was stable even it was heated to 100℃ when it in acidic condition. The optimal conditions to flocculate kaolin suspension were as follows： pH 8-12, flocculant dosage lmL/L, and Ca^2＋ as the optimal cation.