In order to reduce the agglomeration of nanographene and improve its dispersibility,six silane coupling agents were used to modify the surface of the nanographene particles.Visual inspection,Fourier-transform infrared...In order to reduce the agglomeration of nanographene and improve its dispersibility,six silane coupling agents were used to modify the surface of the nanographene particles.Visual inspection,Fourier-transform infrared spectroscopy,transmission electron microscopy,Raman spectroscopy,and X-ray diffraction were employed to evaluate the dispersion properties of the resulting graphene in an aqueous solution of silane coupling agents.Results show that all six types of silane coupling agents are efficient in promoting the dispersion of graphene in aqueous solutions,and no obvious sedimentation of the graphene dispersion solution is observed after a stationary storage period of 30 d.Taking 3-aminopropyltriethoxysilane(KH-550)as an example,after the graphene is dispersed in the KH-550 aqueous solution,the carboxyl group on the surface of the graphene reacts with the KH-550 amino group to form an amide bond,and KH-550 is successfully grafted onto the graphene surface.Polar functional groups ionize in water,creating an electrostatic repulsion effect,or hydrophilic functional groups form hydrogen bonds with water molecules,which is believed to improve the dispersion stability of graphene.The dispersed graphene is curled and contains many folds.Each fold has about three or four layers,with an interlayer spacing of about 0.65 nm.The dispersed graphene also has a complete lattice and a reduced number of defects.Nanographene disperses well in silane coupling agent aqueous solutions and can,therefore,be used to prepare cement-based composites.展开更多
A silver nanoparticle(Ag NP) with good monodispersity was produced by a convenient method for reducing of Ag NO3 with N, N-dimethylacetamide in the presence of polyvinyl pyrrolidone(PVP) as the surface modification ag...A silver nanoparticle(Ag NP) with good monodispersity was produced by a convenient method for reducing of Ag NO3 with N, N-dimethylacetamide in the presence of polyvinyl pyrrolidone(PVP) as the surface modification agent. The shape and size of the Ag NP with reaction time were taken as variables. The surface plasmon band transition was monitored with reaction mixture time at different temperatures. The Ag NP crystallinity increases with the reaction time, and the reduction efficiency is very low when Ag NP solution is dealt at room temperature even after two days, while it is greatly improved at 160 °C only for 25 min. Ag NP modified by the as-synthesized PVP has a face-centered cubic crystalline structure, in which Ag NP could develop into a spherical morphology with a very narrow size distribution of 2-11 nm. The preparation provides a new reducing agent to form Ag NP with simpler operation and shorter time.展开更多
基金The National Key R&D Program of China(No.2018YFC0406701)the National Natural Science Foundation of China(No.51778133,51739008).
文摘In order to reduce the agglomeration of nanographene and improve its dispersibility,six silane coupling agents were used to modify the surface of the nanographene particles.Visual inspection,Fourier-transform infrared spectroscopy,transmission electron microscopy,Raman spectroscopy,and X-ray diffraction were employed to evaluate the dispersion properties of the resulting graphene in an aqueous solution of silane coupling agents.Results show that all six types of silane coupling agents are efficient in promoting the dispersion of graphene in aqueous solutions,and no obvious sedimentation of the graphene dispersion solution is observed after a stationary storage period of 30 d.Taking 3-aminopropyltriethoxysilane(KH-550)as an example,after the graphene is dispersed in the KH-550 aqueous solution,the carboxyl group on the surface of the graphene reacts with the KH-550 amino group to form an amide bond,and KH-550 is successfully grafted onto the graphene surface.Polar functional groups ionize in water,creating an electrostatic repulsion effect,or hydrophilic functional groups form hydrogen bonds with water molecules,which is believed to improve the dispersion stability of graphene.The dispersed graphene is curled and contains many folds.Each fold has about three or four layers,with an interlayer spacing of about 0.65 nm.The dispersed graphene also has a complete lattice and a reduced number of defects.Nanographene disperses well in silane coupling agent aqueous solutions and can,therefore,be used to prepare cement-based composites.
基金Project(126223)supported by Postdoctoral Fund of Central South University,ChinaProject(13JJ4102)supported by the Natural Science Foundation of Hunan Province,ChinaProject(14A025)supported by the Research Foundation of Education Bureau of Hunan Province,China
文摘A silver nanoparticle(Ag NP) with good monodispersity was produced by a convenient method for reducing of Ag NO3 with N, N-dimethylacetamide in the presence of polyvinyl pyrrolidone(PVP) as the surface modification agent. The shape and size of the Ag NP with reaction time were taken as variables. The surface plasmon band transition was monitored with reaction mixture time at different temperatures. The Ag NP crystallinity increases with the reaction time, and the reduction efficiency is very low when Ag NP solution is dealt at room temperature even after two days, while it is greatly improved at 160 °C only for 25 min. Ag NP modified by the as-synthesized PVP has a face-centered cubic crystalline structure, in which Ag NP could develop into a spherical morphology with a very narrow size distribution of 2-11 nm. The preparation provides a new reducing agent to form Ag NP with simpler operation and shorter time.