Nanoporous copper with nano-scale pore size was synthesized by dealloying Mn-Cu precursor alloy using a free corrosion method. The effects of heat treatment of Mn-Cu precursors on alloy phase, morphology and compositi...Nanoporous copper with nano-scale pore size was synthesized by dealloying Mn-Cu precursor alloy using a free corrosion method. The effects of heat treatment of Mn-Cu precursors on alloy phase, morphology and composition of the resultant nanoporous copper were investigated. It is revealed that the compositions distribute homogeneously in the bulk Mn-Cu precursors, which consequently results in a more fully dealloying for forming nanoporous copper. The alloy phase changes from Cuo.a9Mno.51 and Cuo.21Mno.79 of non-thermally treated precursor to Cuo.33Mn0.67 of heat treated alloy. The residual Mn content in nanoporous copper is decreased from 12.97% to 2.04% （molar fraction） made from the precursor without and with 95 h heat treatment. The typical pore shape of nanoporous copper prepared by dealloying the precursor without the heat treatment is divided into two different zones： the uniform bi-continuous structure zone and the blurry or no pore structure zone. Nanoporous copper is of a uniform sponge-like morphology made from the heat-treated precursor, and the average ligament diameter is 40 nm, far smaller than that from the non-thermally treated precursor, in which the average ligament diameter is estimated to be about 70 nm.展开更多
In order to continuously simulate multi-pass plate rolling process,a 3-D elastic hollow-roll model was proposed and an auto mesh-refining module with data passing was developed and integrated with FE software,Marc.The...In order to continuously simulate multi-pass plate rolling process,a 3-D elastic hollow-roll model was proposed and an auto mesh-refining module with data passing was developed and integrated with FE software,Marc.The hollow-roll model has equivalent stiffness of bending resistance and deformation to the real solid and much less meshes,so the computational time is greatly reduced.Based on these,the factors influencing plate profile,such as the roll-bending force,initial crown,thermal crown and heat transfer during rolling and inter-pass cooling can be taken into account in the simulation.The auto mesh-refining module with data passing can automatically refine and re-number elements and transfer the nodal and elemental results to the new meshes.Furthermore,the 3-D modeling routine is parametrically developed and can be run independently of Marc pre-processing program.A seven-pass industrial hot rolling process was continuously simulated to validate the accuracy of model.By comparison of the calculated results with the industrial measured data,the rolling force,temperature and plate profile are in good accordance with the measured ones.展开更多
Transparent,smooth and dense zinc tin oxide (ZTO) thin films have been successfully produced by using a new precursor solution,zinc acetate and tin(II) 2-ethylhexanoate mixed with 2-ethanolamine in methoxyethanol.The ...Transparent,smooth and dense zinc tin oxide (ZTO) thin films have been successfully produced by using a new precursor solution,zinc acetate and tin(II) 2-ethylhexanoate mixed with 2-ethanolamine in methoxyethanol.The ZTO films have been prepared by spin-coating,followed by thermal treatment in oxygen atmosphere.The morphology,composition,crystallinity and band gap energy (Eg) of the ZTO thin films have been characterized by Atomic Force Microscopy (AFM),Atomic Emission Spectrometry (AES),X-ray Diffraction (XRD) and UV-vis spectrophotometry.The conductivity of ZTO is about 9.8×10-9 S/cm,as estimated from the current-voltage (I-V) curve.The effect of the thermal treatment process on the morphology of ZTO thin films is also discussed.展开更多
基金Project(10804101) supported by the National Natural Science Foundation of ChinaProject(9140C6805021008) supported by the State Key Development Program for Basic Research of ChinaProject(2007B08007) supported by the Science and Technology Development Foundation of Chinese Academy of Engineering Physics
文摘Nanoporous copper with nano-scale pore size was synthesized by dealloying Mn-Cu precursor alloy using a free corrosion method. The effects of heat treatment of Mn-Cu precursors on alloy phase, morphology and composition of the resultant nanoporous copper were investigated. It is revealed that the compositions distribute homogeneously in the bulk Mn-Cu precursors, which consequently results in a more fully dealloying for forming nanoporous copper. The alloy phase changes from Cuo.a9Mno.51 and Cuo.21Mno.79 of non-thermally treated precursor to Cuo.33Mn0.67 of heat treated alloy. The residual Mn content in nanoporous copper is decreased from 12.97% to 2.04% （molar fraction） made from the precursor without and with 95 h heat treatment. The typical pore shape of nanoporous copper prepared by dealloying the precursor without the heat treatment is divided into two different zones： the uniform bi-continuous structure zone and the blurry or no pore structure zone. Nanoporous copper is of a uniform sponge-like morphology made from the heat-treated precursor, and the average ligament diameter is 40 nm, far smaller than that from the non-thermally treated precursor, in which the average ligament diameter is estimated to be about 70 nm.
基金Project(20050248007) supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China
文摘In order to continuously simulate multi-pass plate rolling process,a 3-D elastic hollow-roll model was proposed and an auto mesh-refining module with data passing was developed and integrated with FE software,Marc.The hollow-roll model has equivalent stiffness of bending resistance and deformation to the real solid and much less meshes,so the computational time is greatly reduced.Based on these,the factors influencing plate profile,such as the roll-bending force,initial crown,thermal crown and heat transfer during rolling and inter-pass cooling can be taken into account in the simulation.The auto mesh-refining module with data passing can automatically refine and re-number elements and transfer the nodal and elemental results to the new meshes.Furthermore,the 3-D modeling routine is parametrically developed and can be run independently of Marc pre-processing program.A seven-pass industrial hot rolling process was continuously simulated to validate the accuracy of model.By comparison of the calculated results with the industrial measured data,the rolling force,temperature and plate profile are in good accordance with the measured ones.
基金supported by the National Natural Science Foundation of China (50990060)
文摘Transparent,smooth and dense zinc tin oxide (ZTO) thin films have been successfully produced by using a new precursor solution,zinc acetate and tin(II) 2-ethylhexanoate mixed with 2-ethanolamine in methoxyethanol.The ZTO films have been prepared by spin-coating,followed by thermal treatment in oxygen atmosphere.The morphology,composition,crystallinity and band gap energy (Eg) of the ZTO thin films have been characterized by Atomic Force Microscopy (AFM),Atomic Emission Spectrometry (AES),X-ray Diffraction (XRD) and UV-vis spectrophotometry.The conductivity of ZTO is about 9.8×10-9 S/cm,as estimated from the current-voltage (I-V) curve.The effect of the thermal treatment process on the morphology of ZTO thin films is also discussed.