Deformation of the bulk metallic glasses (BMGs) and the creation and propagation of the shear bands are closely interconnected.Shearing force was loaded on Zr 41.2 Ti 13.8 Cu 12.5 Ni 10.0 Be 22.5 (Vit.1) BMGs by cutti...Deformation of the bulk metallic glasses (BMGs) and the creation and propagation of the shear bands are closely interconnected.Shearing force was loaded on Zr 41.2 Ti 13.8 Cu 12.5 Ni 10.0 Be 22.5 (Vit.1) BMGs by cutting during the turning of the BMG rod.The temperature rise of alloy on the shear bands was calculated and the result showed that it could reach the temperature of the super-cooled liquid zone or exceed the melting point.The temperature rise caused viscous fluid flow and brought about the deformation of BMGs.This suggested that the deformation of BMGs was derived,at least to some extent,from the adiabatic shear temperature rise.展开更多
基金supported by the National Basic Research Program of China (Grant No. 2010CB731600)the National Natural Science Foundation of China (Grant Nos. 50731005,50821001 and 51171163)+1 种基金the Doctoral Fund of Ministry of Education of China (Grant No. 20101333110004)the Nature Science Foundation of Hebei (Grant No. E2010001176)
文摘Deformation of the bulk metallic glasses (BMGs) and the creation and propagation of the shear bands are closely interconnected.Shearing force was loaded on Zr 41.2 Ti 13.8 Cu 12.5 Ni 10.0 Be 22.5 (Vit.1) BMGs by cutting during the turning of the BMG rod.The temperature rise of alloy on the shear bands was calculated and the result showed that it could reach the temperature of the super-cooled liquid zone or exceed the melting point.The temperature rise caused viscous fluid flow and brought about the deformation of BMGs.This suggested that the deformation of BMGs was derived,at least to some extent,from the adiabatic shear temperature rise.