An interesting phenomenon of cooling-rate induced brittleness in Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass （BMG） was reported. It was found that the as-cast BMG specimens exhibited a brittle-ductile transition w...An interesting phenomenon of cooling-rate induced brittleness in Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass （BMG） was reported. It was found that the as-cast BMG specimens exhibited a brittle-ductile transition when the larger specimens were machined into smaller specimens through removing the cast-softening surface layer by layer. After compression tests, the as-machined small specimens, owing to the absence of the cast-softening surface, displayed highly dense and intersecting shear bands, and extensive plastic deformation. This is in contrast to the catastrophic failure and low deformability in the as-cast large specimens. More free volume was detected in the smaller as-fractured specimens, by differential scanning calorimetry, which may be attributed to the occurrence of strain softening and increased plasticity. Compared with the relatively smooth fracture surface in the smaller specimens, the larger specimens showed more diverse features on the fracture surface due to their graded structures.展开更多
The original descriptive model of shear stress and shear displacement only reflects the stress deformation characteristics of plastic structural plane.The index model was revised and piecewise index model was built to...The original descriptive model of shear stress and shear displacement only reflects the stress deformation characteristics of plastic structural plane.The index model was revised and piecewise index model was built to describe the stress deformation characteristics of plastic structural plane and brittle structural plane.The relation of stress and strain to the failure mode of structural plane considering the effect of its shape was investigated,and a model which could reflect the relation between undulate angle and shear strength was built.The result indicates that structural plane presents nonlinear characteristics,specifically,the value of undulate angle,as well as corresponding shear strength,becomes larger as the normal stress decreases.展开更多
基金Project(2012M511401)supported by China Postdoctoral Science FoundationProject(12JJ5018)supported by Hunan Provincial Natural Science Foundation of China+1 种基金Project(2012RS4006)supported by Hunan Provincial Science and Technology Plan of ChinaProject(CSUZC2012028)supported by the Open-End Fund for the Valuable and Precision Instruments of Central South University,China
文摘An interesting phenomenon of cooling-rate induced brittleness in Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass （BMG） was reported. It was found that the as-cast BMG specimens exhibited a brittle-ductile transition when the larger specimens were machined into smaller specimens through removing the cast-softening surface layer by layer. After compression tests, the as-machined small specimens, owing to the absence of the cast-softening surface, displayed highly dense and intersecting shear bands, and extensive plastic deformation. This is in contrast to the catastrophic failure and low deformability in the as-cast large specimens. More free volume was detected in the smaller as-fractured specimens, by differential scanning calorimetry, which may be attributed to the occurrence of strain softening and increased plasticity. Compared with the relatively smooth fracture surface in the smaller specimens, the larger specimens showed more diverse features on the fracture surface due to their graded structures.
基金Project(50878212) supported by National Natural Science Foundation of ChinaProject(1298011-2) supported by the Funding of Scientific Research and Technology Development Projects of Guangxi Province,China+2 种基金Project(12JJ6052) supported by Natural Science Foundation of Hunan Province,ChinaProject(kfj120402) supported Open Fund of Key Laboratory of Special Environment Road Engineering of Hunan Province(Changsha University of Science&Technology),ChinaProject(13C1010) supported by the Research Foundation of Education Bureau of Hunan Province,China
文摘The original descriptive model of shear stress and shear displacement only reflects the stress deformation characteristics of plastic structural plane.The index model was revised and piecewise index model was built to describe the stress deformation characteristics of plastic structural plane and brittle structural plane.The relation of stress and strain to the failure mode of structural plane considering the effect of its shape was investigated,and a model which could reflect the relation between undulate angle and shear strength was built.The result indicates that structural plane presents nonlinear characteristics,specifically,the value of undulate angle,as well as corresponding shear strength,becomes larger as the normal stress decreases.