Evaluation on nitrogen removal of step-feed anoxic/oxic activated sludge process at the standpoint of reaction kinetics and process kinetics was conducted. Theoretical biological nitrogen removal efficiency was deduce...Evaluation on nitrogen removal of step-feed anoxic/oxic activated sludge process at the standpoint of reaction kinetics and process kinetics was conducted. Theoretical biological nitrogen removal efficiency was deduced based on the mass balance of nitrate in the last stage. The comparison of pre-denitrification process and step feed process in the aspects of nitrogen removal efficiency, volume of reactor and building investment was studied, and the results indicated that step-feed anoxic/oxic activated sludge process was superior to pre-denitrification process in these aspects.展开更多
The paper presents the results of wear and metallography tests of tool steel grades: ASTM A681, Chl2M and CH12FS per COST, AMS 6437E i BS X46Crl3, all surface hardened by the Carbo process (carburizing) and by the NiC...The paper presents the results of wear and metallography tests of tool steel grades: ASTM A681, Chl2M and CH12FS per COST, AMS 6437E i BS X46Crl3, all surface hardened by the Carbo process (carburizing) and by the NiCar process (nitrocarburizing). The thermo-chemical treatment was conducted in powder pack for a duration of 6 h (carburizing) and for 4 h in the case of nitrocarburizing. Factors investigated were: morphology, depth and microhardness of the cases obtained, their microstructure, as well as phase composition. Wear tests were conducted by the three cylinder-cone method. Wear velocity was 0.58 m/s, unit load was 50 MPa and 400Mpa, wear path was 3470 m. Oil SAE30 was applied at the rate of 30 drops per minute.展开更多
文摘Evaluation on nitrogen removal of step-feed anoxic/oxic activated sludge process at the standpoint of reaction kinetics and process kinetics was conducted. Theoretical biological nitrogen removal efficiency was deduced based on the mass balance of nitrate in the last stage. The comparison of pre-denitrification process and step feed process in the aspects of nitrogen removal efficiency, volume of reactor and building investment was studied, and the results indicated that step-feed anoxic/oxic activated sludge process was superior to pre-denitrification process in these aspects.
文摘The paper presents the results of wear and metallography tests of tool steel grades: ASTM A681, Chl2M and CH12FS per COST, AMS 6437E i BS X46Crl3, all surface hardened by the Carbo process (carburizing) and by the NiCar process (nitrocarburizing). The thermo-chemical treatment was conducted in powder pack for a duration of 6 h (carburizing) and for 4 h in the case of nitrocarburizing. Factors investigated were: morphology, depth and microhardness of the cases obtained, their microstructure, as well as phase composition. Wear tests were conducted by the three cylinder-cone method. Wear velocity was 0.58 m/s, unit load was 50 MPa and 400Mpa, wear path was 3470 m. Oil SAE30 was applied at the rate of 30 drops per minute.