Mg2FeH6 doped with and without Ti and its alloys (TiMn2, TiAl) were prepared combing ball milling and heat treatment. The effects of these additives on the dehydrogenation performance of Mg2FeH6 were studied systemati...Mg2FeH6 doped with and without Ti and its alloys (TiMn2, TiAl) were prepared combing ball milling and heat treatment. The effects of these additives on the dehydrogenation performance of Mg2FeH6 were studied systematically. The results show that all additives have favor influence on improving the hydrogen desorption property of Mg2FeH6. Especially, TiMn2 exhibits prominent effect on enhancing the dehydrogenation kinetics of Mg2FeH6. Moreover, the activation energy of TiMn2-doped Mg2FeH6 calculated by Kissinger equation is 94.87 kJ/mol, which is 28 kJ/mol lower than that of the undoped Mg2FeH6. The cycling tests suggest that the improved dehydrogenation kinetics of Mg2FeH6 doped by TiMn2 can maintain in the second cycle.展开更多
Mg-x(Ti0.9 Zr0.2 Mn1.5 Cr0.3)(x=20%,30%,40%) (mass fraction) composite powders were prepared by reactive ball milling with hydrogen and their hydrogen storage properties and microstructure were investigated by XRD,SEM...Mg-x(Ti0.9 Zr0.2 Mn1.5 Cr0.3)(x=20%,30%,40%) (mass fraction) composite powders were prepared by reactive ball milling with hydrogen and their hydrogen storage properties and microstructure were investigated by XRD,SEM and pressure-composition-temperature measurement.The results show that the composites have 3.83%-5.07%hydrogen capacity at 553 K and good hydrogenation kinetics,even at room temperature.Among them,the milled Mg-30%(Ti0.9Zr0.2Mn1.5Cr0.3)composite has the highest hydrogenation kinetics as it can quickly absorb 2.1%hydrogen at 373 K,3.5%in 2 000 s at 473 K,even 3.26%in 60 s at 553 K under 3 MPa hydrogen pressure.The improved hydrogenation properties come from the catalytic effect of Ti0.9 Zr0.2 Mn1.5 Cr0.3 particles dispersed uniformly on the surface of Mg particles.展开更多
基金Project(2010CB631300)supported by the National Basic Research Program of ChinaProject(2012AA051503)supported by the National High Technology Research&Development Program of China+1 种基金Projects(51001090,51171173)supported by the National Natural Science Foundation of ChinaProject(IRT13037)supported by the Program for Innovative Research Team in University of Ministry of Education of China
文摘Mg2FeH6 doped with and without Ti and its alloys (TiMn2, TiAl) were prepared combing ball milling and heat treatment. The effects of these additives on the dehydrogenation performance of Mg2FeH6 were studied systematically. The results show that all additives have favor influence on improving the hydrogen desorption property of Mg2FeH6. Especially, TiMn2 exhibits prominent effect on enhancing the dehydrogenation kinetics of Mg2FeH6. Moreover, the activation energy of TiMn2-doped Mg2FeH6 calculated by Kissinger equation is 94.87 kJ/mol, which is 28 kJ/mol lower than that of the undoped Mg2FeH6. The cycling tests suggest that the improved dehydrogenation kinetics of Mg2FeH6 doped by TiMn2 can maintain in the second cycle.
基金Projects(20833009,20873148,U0734005) supported by the National Natural Science Foundation of ChinaProject(2010CB631303) supported by the National Basic Research Program of China+2 种基金Project(2009A11GX052) supported by Dalian Science and Technology Foundation,ChinaProject(KFJJ10-1Z) supported by the State Key Laboratory of Explosion Science and Technology,Beijing Institute of Technology,ChinaProject(Y4090507) supported by the Zhejiang Basic Research Program of China
文摘Mg-x(Ti0.9 Zr0.2 Mn1.5 Cr0.3)(x=20%,30%,40%) (mass fraction) composite powders were prepared by reactive ball milling with hydrogen and their hydrogen storage properties and microstructure were investigated by XRD,SEM and pressure-composition-temperature measurement.The results show that the composites have 3.83%-5.07%hydrogen capacity at 553 K and good hydrogenation kinetics,even at room temperature.Among them,the milled Mg-30%(Ti0.9Zr0.2Mn1.5Cr0.3)composite has the highest hydrogenation kinetics as it can quickly absorb 2.1%hydrogen at 373 K,3.5%in 2 000 s at 473 K,even 3.26%in 60 s at 553 K under 3 MPa hydrogen pressure.The improved hydrogenation properties come from the catalytic effect of Ti0.9 Zr0.2 Mn1.5 Cr0.3 particles dispersed uniformly on the surface of Mg particles.