LiNi1/3Co1/3Mn1/3O2 was coated with uniform nano-sized AlF3 layer by chemical precipitation method to improve its rate capability.The samples were characterized by X-ray diffractometry (XRD),transmission electron micr...LiNi1/3Co1/3Mn1/3O2 was coated with uniform nano-sized AlF3 layer by chemical precipitation method to improve its rate capability.The samples were characterized by X-ray diffractometry (XRD),transmission electron microscopy (TEM),energy dispersive spectroscopy (EDS),charge-discharge cycling,cyclic voltammetry (CV),and electrochemical impedance spectroscopy (EIS).Uniform coated layer with a thickness of about 3 nm was observed on the surface of LiNi1/3Co1/3Mn1/3O2 particle by TEM.At 0.5C and 2C rates,1.5% (mass fraction) AlF3-coated LiNi1/3Co1/3Mn1/3O2/Li in 2.8-4.3 V versus Li/Li+ after 80 cycles showed less than 3% of capacity fading,while those of the bare one were 16.5% and 45.9%,respectively.At 5C rate,the capacity retention of the coated sample after 50 cycles maintained 91.4% of the initial discharge capacity,while that of the bare one decreased to 52.6%.EIS result showed that a little change of charge transfer resistance of the coated sample resulting from uniform thin AlF3 layer was proposed as the main reason why its rate capability was improved obviously.CV result further indicated a greater reversibility for the electrode processes and better electrochemical performance of AlF3-coated layer.展开更多
基金Project(50542004) supported by the National Natural Science Foundation of ChinaProject(1960-71131100017) supported by Graduate Degree Thesis Innovation Foundation of Central South University,China
文摘LiNi1/3Co1/3Mn1/3O2 was coated with uniform nano-sized AlF3 layer by chemical precipitation method to improve its rate capability.The samples were characterized by X-ray diffractometry (XRD),transmission electron microscopy (TEM),energy dispersive spectroscopy (EDS),charge-discharge cycling,cyclic voltammetry (CV),and electrochemical impedance spectroscopy (EIS).Uniform coated layer with a thickness of about 3 nm was observed on the surface of LiNi1/3Co1/3Mn1/3O2 particle by TEM.At 0.5C and 2C rates,1.5% (mass fraction) AlF3-coated LiNi1/3Co1/3Mn1/3O2/Li in 2.8-4.3 V versus Li/Li+ after 80 cycles showed less than 3% of capacity fading,while those of the bare one were 16.5% and 45.9%,respectively.At 5C rate,the capacity retention of the coated sample after 50 cycles maintained 91.4% of the initial discharge capacity,while that of the bare one decreased to 52.6%.EIS result showed that a little change of charge transfer resistance of the coated sample resulting from uniform thin AlF3 layer was proposed as the main reason why its rate capability was improved obviously.CV result further indicated a greater reversibility for the electrode processes and better electrochemical performance of AlF3-coated layer.