A wear resistant TiB-TiC reinforced TiNi-Ti2Ni intermetallic matrix composite coating（TiB-TiC/TiNi-Ti2Ni） was prepared on Ti-6.5Al-2Zr-1Mo-1V titanium alloy by the laser cladding process using Ti＋Ni＋B4C powder ble...A wear resistant TiB-TiC reinforced TiNi-Ti2Ni intermetallic matrix composite coating（TiB-TiC/TiNi-Ti2Ni） was prepared on Ti-6.5Al-2Zr-1Mo-1V titanium alloy by the laser cladding process using Ti＋Ni＋B4C powder blends as the precursor materials.Microstructure and worn surface morphologies of the coating were characterized by optical microscopy（OM）,scan electron microscopy（SEM）,X-ray diffraction（XRD）,energy dispersive X-ray analysis（EDS） and atomic force microscopy（AFM）.Wear resistance of the coating was evaluated under dry sliding wear test condition at room temperature.The results indicate that the laser clad coating has a unique microstructure composed of flower-like TiB-TiC eutectic ceramics uniformly distributed in the TiNi-Ti2Ni dual-phase intermetallic matrix.The coating exhibits an excellent wear resistance because of combined action of hard TiB-TiC eutectic ceramic reinforcements and ductile TiNi-Ti2Ni dual-phase intermetallic matrix.展开更多
Mg Al-layered double hydroxides（LDH） coatings were fabricated by the in-situ hydrothermal treatment method on the AA5005 aluminum alloy.The characteristics of the coatings were investigated by XRD,FT-IR,SEM and EDS....Mg Al-layered double hydroxides（LDH） coatings were fabricated by the in-situ hydrothermal treatment method on the AA5005 aluminum alloy.The characteristics of the coatings were investigated by XRD,FT-IR,SEM and EDS.The effect of the p H value of the solution on the formation of the LDH coatings was studied.The optimum p H value of the solution was 10.0.The corrosion resistance of the LDH coatings was studied using potentiodynamic polarization tests and electrochemical impedance spectrum（EIS）.The results demonstrate that the LDH coatings,characterized by platelets vertically to the substrate surface possess excellent corrosion resistance.The influence of the hydrothermal crystallization time on the corrosion resistance was evaluated.Prolonging the crystallization time can increase the corrosion resistance of the obtained LDH coatings.The anticorrosion mechanism of the LDH coatings was discussed.展开更多
The aim was to research fresh-keeping effects of natamycin on cold-pre- served grape. Red globe grapes were processed with compound coating liquid of chitosan with mass fraction at 1% and natamycin with mass fractions...The aim was to research fresh-keeping effects of natamycin on cold-pre- served grape. Red globe grapes were processed with compound coating liquid of chitosan with mass fraction at 1% and natamycin with mass fractions at 0.20% （T1）, 0.40% （T2） and 0.60% （T3）, respectively. Grapes processed with water （CK3） and 1% chitosan （CK2） were taken as control groups. Rotten rate, seed shattering rate, mass loss rate, respiratory intensity and related physiological quality in test and control groups were compared. The results indicated that respiratory intensity, mass loss rate, rotten rate and seed shattering rate in CK1 were all higher than those in CK2. In addition, T1, T2 and T3 were lower in the indices than CK1 and CK2, but still kept at a high level in fruit hardness. Furthermore, mass fractions of Vc and titratable acid declined more slowly in T1, T2 and T3, compared with CK1 and CK2. Natamycin better preserved grapes and prolonged storage period. In general, natamycin with mass fraction at 0.4% proved best in fresh-keeping.展开更多
Using titanium wires （99.5%, 200 μm in diameter） as a reactive source, an Al-based composite coating reinforced by titanium tri-aluminide （A13Ti） particles was fabricated by infiltration plus in-situ methods. Acc...Using titanium wires （99.5%, 200 μm in diameter） as a reactive source, an Al-based composite coating reinforced by titanium tri-aluminide （A13Ti） particles was fabricated by infiltration plus in-situ methods. According to the differential thermal analysis （DTA） curve, the reactive temperature between Ti wires and A1 matrix can be determined at 890 ℃. The obtained composite coatings were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and microhardness and wear test. The experimental results show that when holding period is 20 min at 890℃, the titanium wires react completely to in-situ synthesize Al3Ti particles, which presents blocky and strip-like states. The microhardness of in-situ synthesized Al3Ti particles is about 4.5 times that of the Al-matrix. Under the condition of dry sliding at 10 N load, compared with the unreinforced Al matrix, the composite coating fabricated with 20 min offers unique wear resistance behavior, and its wear mechanism is that the adhesive wear and abrasive wear coexist.展开更多
An experimental study has been carried out to investigate the influence of heat treatment at 300 ℃,450 ℃,550 ℃,650 ℃ and 800 ℃ on the microstructure and sliding wear behavior of Fe Al/WC intermetallic composite c...An experimental study has been carried out to investigate the influence of heat treatment at 300 ℃,450 ℃,550 ℃,650 ℃ and 800 ℃ on the microstructure and sliding wear behavior of Fe Al/WC intermetallic composite coatings produced by high velocity arc spraying (HVAS) and cored wires. The result shows, the main phases in both as sprayed and heat treated Fe Al/WC composite coatings are iron aluminide intermetallics (Fe 3Al+FeAl) and α as well as a little oxide (Al 2O 3) and carbides (WC, W 2C, Fe 2W 2C and Fe 6W 6C). After heat treated at 450-650 ℃, dispersion strengthening of Fe 2W 2C and Fe 6W 6C will lead to a rise in microhardness of the coatings. The microhardness is likely to be the most important factor which influences the sliding wear behavior of the coatings. Increasing the microhardness through heat treatment will improve the sliding wear resistance of the Fe Al/WC composite coatings.展开更多
基金Project (11R21414700) supported by Shanghai Postdoctoral Sustentation Fund, ChinaProject (20110490715) supported by the National Science Foundation for Post-doctoral Scientists of China+2 种基金Projects (50974088, 51004070) supported by the National Natural Science Foundation of ChinaProject (10QA1403400) supported by Shanghai Rising-Star ProgramProject (10540500900) supported by the Shanghai Municipal Education Commission
基金Project (2010CB731705) supported by the National Basic Research Program of China
文摘A wear resistant TiB-TiC reinforced TiNi-Ti2Ni intermetallic matrix composite coating（TiB-TiC/TiNi-Ti2Ni） was prepared on Ti-6.5Al-2Zr-1Mo-1V titanium alloy by the laser cladding process using Ti＋Ni＋B4C powder blends as the precursor materials.Microstructure and worn surface morphologies of the coating were characterized by optical microscopy（OM）,scan electron microscopy（SEM）,X-ray diffraction（XRD）,energy dispersive X-ray analysis（EDS） and atomic force microscopy（AFM）.Wear resistance of the coating was evaluated under dry sliding wear test condition at room temperature.The results indicate that the laser clad coating has a unique microstructure composed of flower-like TiB-TiC eutectic ceramics uniformly distributed in the TiNi-Ti2Ni dual-phase intermetallic matrix.The coating exhibits an excellent wear resistance because of combined action of hard TiB-TiC eutectic ceramic reinforcements and ductile TiNi-Ti2Ni dual-phase intermetallic matrix.
基金Project(20133718120003)supported by the Doctoral Program Foundation of State Education Ministry,ChinaProject(BS2013CL009)supported by the Scientific Research Foundation of Shandong for Outstanding Young Scientist,China+1 种基金Projects(13-1-4-217-jch,13-1-4-188-jch)supported by the Applied Basic Research Foundation of Qingdao,ChinaProject(2014TDJH104)supported by the SDUST Research Fund,China
文摘Mg Al-layered double hydroxides（LDH） coatings were fabricated by the in-situ hydrothermal treatment method on the AA5005 aluminum alloy.The characteristics of the coatings were investigated by XRD,FT-IR,SEM and EDS.The effect of the p H value of the solution on the formation of the LDH coatings was studied.The optimum p H value of the solution was 10.0.The corrosion resistance of the LDH coatings was studied using potentiodynamic polarization tests and electrochemical impedance spectrum（EIS）.The results demonstrate that the LDH coatings,characterized by platelets vertically to the substrate surface possess excellent corrosion resistance.The influence of the hydrothermal crystallization time on the corrosion resistance was evaluated.Prolonging the crystallization time can increase the corrosion resistance of the obtained LDH coatings.The anticorrosion mechanism of the LDH coatings was discussed.
文摘The aim was to research fresh-keeping effects of natamycin on cold-pre- served grape. Red globe grapes were processed with compound coating liquid of chitosan with mass fraction at 1% and natamycin with mass fractions at 0.20% （T1）, 0.40% （T2） and 0.60% （T3）, respectively. Grapes processed with water （CK3） and 1% chitosan （CK2） were taken as control groups. Rotten rate, seed shattering rate, mass loss rate, respiratory intensity and related physiological quality in test and control groups were compared. The results indicated that respiratory intensity, mass loss rate, rotten rate and seed shattering rate in CK1 were all higher than those in CK2. In addition, T1, T2 and T3 were lower in the indices than CK1 and CK2, but still kept at a high level in fruit hardness. Furthermore, mass fractions of Vc and titratable acid declined more slowly in T1, T2 and T3, compared with CK1 and CK2. Natamycin better preserved grapes and prolonged storage period. In general, natamycin with mass fraction at 0.4% proved best in fresh-keeping.
基金Project (11JK0799) supported by Scientific Research Program Funded by Shaanxi Provincial Education Department,ChinaProject (KTCQ1-17) supported by Scientific and Technological Innovation and Co-ordination Funded by Science and Technology Department of Shaanxi Province,China
文摘Using titanium wires （99.5%, 200 μm in diameter） as a reactive source, an Al-based composite coating reinforced by titanium tri-aluminide （A13Ti） particles was fabricated by infiltration plus in-situ methods. According to the differential thermal analysis （DTA） curve, the reactive temperature between Ti wires and A1 matrix can be determined at 890 ℃. The obtained composite coatings were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and microhardness and wear test. The experimental results show that when holding period is 20 min at 890℃, the titanium wires react completely to in-situ synthesize Al3Ti particles, which presents blocky and strip-like states. The microhardness of in-situ synthesized Al3Ti particles is about 4.5 times that of the Al-matrix. Under the condition of dry sliding at 10 N load, compared with the unreinforced Al matrix, the composite coating fabricated with 20 min offers unique wear resistance behavior, and its wear mechanism is that the adhesive wear and abrasive wear coexist.
文摘An experimental study has been carried out to investigate the influence of heat treatment at 300 ℃,450 ℃,550 ℃,650 ℃ and 800 ℃ on the microstructure and sliding wear behavior of Fe Al/WC intermetallic composite coatings produced by high velocity arc spraying (HVAS) and cored wires. The result shows, the main phases in both as sprayed and heat treated Fe Al/WC composite coatings are iron aluminide intermetallics (Fe 3Al+FeAl) and α as well as a little oxide (Al 2O 3) and carbides (WC, W 2C, Fe 2W 2C and Fe 6W 6C). After heat treated at 450-650 ℃, dispersion strengthening of Fe 2W 2C and Fe 6W 6C will lead to a rise in microhardness of the coatings. The microhardness is likely to be the most important factor which influences the sliding wear behavior of the coatings. Increasing the microhardness through heat treatment will improve the sliding wear resistance of the Fe Al/WC composite coatings.