The hexagonal to orthorhombic(HO)transformation fromβ-Ni_(3)Sn_(2)(hexagonal)phase toα'-Ni_(3)Sn_(2)(orthorhombic)phase was confirmed in directionally solidified Sn−Ni peritectic alloys.It is shown that the reme...The hexagonal to orthorhombic(HO)transformation fromβ-Ni_(3)Sn_(2)(hexagonal)phase toα'-Ni_(3)Sn_(2)(orthorhombic)phase was confirmed in directionally solidified Sn−Ni peritectic alloys.It is shown that the remelting/resolidification process which is caused by both the temperature gradient zone melting(TGZM)and Gibbs−Thomson(G−T)effects can take place on secondary dendrites.Besides,the intersection angle between the primary dendrite stem and secondary branch(θ)is found to increase fromπ/3 toπ/2 as the solidification proceeds.This is the morphological feature of the HO transformation,which can change the diffusion distance of the remelting/resolidification process.Thus,a diffusion-based analytical model is established to describe this process through the specific surface area(S_(V))of dendrites.The theoretical prediction demonstrates that the remelting/resolidification process is restricted when the HO transformation occurs during peritectic solidification.In addition,the slope of the prediction curves is changed,indicating the variation of the local remelting/resolidification rates.展开更多
基金the support from the Natural Science Foundation of China(No.51871118)Open Project of Key Laboratory for Magnetism and Magnetic Materials of the Ministry of Education,Lanzhou University,China(No.LZUMMM2021005)+1 种基金the Science and Technology Project of Lanzhou City,China(No.2019-1-30)State Key Laboratory of Special Rare Metal Materials,China(No.SKL2020K003)。
文摘The hexagonal to orthorhombic(HO)transformation fromβ-Ni_(3)Sn_(2)(hexagonal)phase toα'-Ni_(3)Sn_(2)(orthorhombic)phase was confirmed in directionally solidified Sn−Ni peritectic alloys.It is shown that the remelting/resolidification process which is caused by both the temperature gradient zone melting(TGZM)and Gibbs−Thomson(G−T)effects can take place on secondary dendrites.Besides,the intersection angle between the primary dendrite stem and secondary branch(θ)is found to increase fromπ/3 toπ/2 as the solidification proceeds.This is the morphological feature of the HO transformation,which can change the diffusion distance of the remelting/resolidification process.Thus,a diffusion-based analytical model is established to describe this process through the specific surface area(S_(V))of dendrites.The theoretical prediction demonstrates that the remelting/resolidification process is restricted when the HO transformation occurs during peritectic solidification.In addition,the slope of the prediction curves is changed,indicating the variation of the local remelting/resolidification rates.