采用 AFM,XRD和 XPS等对 Ni Ti表面离子束合成 Ti O2 /Ta2 O5复合薄膜的表面微观形貌、微结构和表面化学组成进行了表征。同时研究了膜层的力学性能、抗模拟体液腐蚀性和抗凝血性。结果表明 ,适当组成的 Ti O2 /Ta2 O5复合薄膜能显著提...采用 AFM,XRD和 XPS等对 Ni Ti表面离子束合成 Ti O2 /Ta2 O5复合薄膜的表面微观形貌、微结构和表面化学组成进行了表征。同时研究了膜层的力学性能、抗模拟体液腐蚀性和抗凝血性。结果表明 ,适当组成的 Ti O2 /Ta2 O5复合薄膜能显著提高 Ni展开更多
Dissimilar metal joining between NiTi shape memory alloy（SMA） and stainless steel was conducted.A cluster of NiTi SMA wires were first joined with tungsten inert gas（TIG） welding process,then the NiTi SMA TIG weld...Dissimilar metal joining between NiTi shape memory alloy（SMA） and stainless steel was conducted.A cluster of NiTi SMA wires were first joined with tungsten inert gas（TIG） welding process,then the NiTi SMA TIG weld was welded to a stainless steel pipe with laser spot welding process.The microstructure of the welds was examined with an optical microscope and the elemental distribution in the welds was measured by electron probe microanalysis（EPMA）.The results show that TiC compounds dispersively distribute in the NiTi SMA TIG weld.However,the amount of TiC compounds greatly decreases around the fusion boundary of the laser spot weld between the NiTi SMA and stainless steel.Mutual diffusion between NiTi shape memory alloy and stainless steel happen within a short distance near the fusion boundary,and intermetallic compounds such as Ni3Ti＋（Fe,Ni）Ti appear around the fusion boundary.展开更多
基金Project(50974046/E041607) supported by the National Natural Science Foundation of China
文摘Dissimilar metal joining between NiTi shape memory alloy（SMA） and stainless steel was conducted.A cluster of NiTi SMA wires were first joined with tungsten inert gas（TIG） welding process,then the NiTi SMA TIG weld was welded to a stainless steel pipe with laser spot welding process.The microstructure of the welds was examined with an optical microscope and the elemental distribution in the welds was measured by electron probe microanalysis（EPMA）.The results show that TiC compounds dispersively distribute in the NiTi SMA TIG weld.However,the amount of TiC compounds greatly decreases around the fusion boundary of the laser spot weld between the NiTi SMA and stainless steel.Mutual diffusion between NiTi shape memory alloy and stainless steel happen within a short distance near the fusion boundary,and intermetallic compounds such as Ni3Ti＋（Fe,Ni）Ti appear around the fusion boundary.