The compression test on rock-like specimens with prefabricated closed multi-fissures made by pulling out the embedded metal inserts in the precured period was done on the servo control uniaxial loading instrument. The...The compression test on rock-like specimens with prefabricated closed multi-fissures made by pulling out the embedded metal inserts in the precured period was done on the servo control uniaxial loading instrument. The influence of fissure inclination angle and distribution density on the failure characteristics of fissure bodies was researched. It was found that, the fissure inclination angle was the major influencing factor on the failure modes of fissure bodies. The different developmental states of micro-cracks would appear on specimens under different fissure inclination angles. However, the influence of fissure distribution density on the failure mode of fissure bodies was achieved by influencing the transfixion pattern of fissures. It was shown by the sliding crack model that, the effective shear, which drove the relative sliding of the fissure, was a function of fissure inclination angle and friction coefficient of the fissure surface. The strain-softening model of fissure bodies was established based on the mechanical parameters that were obtained by the test of rock-like materials under the same experimental condition. And the reliability of experimental results was identified by using this model.展开更多
To describe the deformation and strength characteristics of the corroded rock-like specimens containing a single crack under uniaxial compression,a damage constitutive model combining hydro-chemical damage with coupli...To describe the deformation and strength characteristics of the corroded rock-like specimens containing a single crack under uniaxial compression,a damage constitutive model combining hydro-chemical damage with coupling damage of micro-flaws and macro-cracks is proposed.Firstly,based on phenomenological theory,the damage variable of the rock-like specimens subjected to water environment erosion and chemical corrosion is obtained.Secondly,a coupled damage variable for cracked rock-like specimens is derived based on the Lemaitre strain equivalence hypothesis,which combines the Weibull statistical damage model for micro-flaws and the fracture mechanics model for a macro single crack.Then,considering the residual strength characteristics of the rock-like materials,the damage variable is modified by introducing the correction coefficient,and the damage constitutive model of the corroded rock-like specimens with a single crack under uniaxial compression is established.The model is verified by comparing the experimental stress−strain curves,and the results are in good agreement with those provided in the literature.Finally,the correction coefficient of the damage variable proposed in this paper is discussed.The damage constitutive model developed in this paper provides an effective method to describe the stress−strain relationship and residual strength characteristics of the corroded rock-like specimens with a single crack under uniaxial compression.展开更多
Uniaxial tensile tests and scanning electron microscopy(SEM)experiments were carried out on the porous FeAl intermetallics(porosities of 41.1%,44.2%and 49.3%,pore size of 15−30μm)prepared by our research group to stu...Uniaxial tensile tests and scanning electron microscopy(SEM)experiments were carried out on the porous FeAl intermetallics(porosities of 41.1%,44.2%and 49.3%,pore size of 15−30μm)prepared by our research group to study the macroscopic mechanical properties and microscopic failure mechanism.The results show that the tensileσ−εcurves of the porous FeAl with different porosities can be divided into four stages:elasticity,yielding,strengthening and failure,without necking phenomenon.The elastic modulus,ultimate strength and elongation decrease with the increase of porosity and the elongation is much lower than 5%.A macroscopic brittle fracture appears,and the microscopic fracture mechanism is mainly intergranular fracture,depending on the Al content in the dense FeAl intermetallics.In addition,the stochastic porous model(SPM)with random pore structure size and distribution is established by designing a self-compiling generation program in FORTRAN language.Combined with the secondary development platform of finite element software ANSYS,the effective elastic moduli of the porous FeAl can be determined by elastic analysis of SPM and they are close to the experimental values,which can verify the validity of the established SPM for analyzing the elastic properties of the porous material.展开更多
基金Project (10972238) supported by the National Natural Science Foundation of ChinaProject supported by the Open-End Fund of the Valuable and Precision Instruments of Central South University
文摘The compression test on rock-like specimens with prefabricated closed multi-fissures made by pulling out the embedded metal inserts in the precured period was done on the servo control uniaxial loading instrument. The influence of fissure inclination angle and distribution density on the failure characteristics of fissure bodies was researched. It was found that, the fissure inclination angle was the major influencing factor on the failure modes of fissure bodies. The different developmental states of micro-cracks would appear on specimens under different fissure inclination angles. However, the influence of fissure distribution density on the failure mode of fissure bodies was achieved by influencing the transfixion pattern of fissures. It was shown by the sliding crack model that, the effective shear, which drove the relative sliding of the fissure, was a function of fissure inclination angle and friction coefficient of the fissure surface. The strain-softening model of fissure bodies was established based on the mechanical parameters that were obtained by the test of rock-like materials under the same experimental condition. And the reliability of experimental results was identified by using this model.
基金Project(FRF-IDRY-20-013)supported by the Fundamental Research Funds for the Central Universities,ChinaProjects(51974014,52074020)supported by the National Natural Science Foundation of China。
文摘To describe the deformation and strength characteristics of the corroded rock-like specimens containing a single crack under uniaxial compression,a damage constitutive model combining hydro-chemical damage with coupling damage of micro-flaws and macro-cracks is proposed.Firstly,based on phenomenological theory,the damage variable of the rock-like specimens subjected to water environment erosion and chemical corrosion is obtained.Secondly,a coupled damage variable for cracked rock-like specimens is derived based on the Lemaitre strain equivalence hypothesis,which combines the Weibull statistical damage model for micro-flaws and the fracture mechanics model for a macro single crack.Then,considering the residual strength characteristics of the rock-like materials,the damage variable is modified by introducing the correction coefficient,and the damage constitutive model of the corroded rock-like specimens with a single crack under uniaxial compression is established.The model is verified by comparing the experimental stress−strain curves,and the results are in good agreement with those provided in the literature.Finally,the correction coefficient of the damage variable proposed in this paper is discussed.The damage constitutive model developed in this paper provides an effective method to describe the stress−strain relationship and residual strength characteristics of the corroded rock-like specimens with a single crack under uniaxial compression.
基金Project(11502307)supported by the National Natural Science Foundation of ChinaProject(2016JJ3187)supported by the Natural Science Foundation of Hunan Province,ChinaProject(50825102)supported by the National Natural Science Funds for Distinguished Young Scholar of China。
文摘Uniaxial tensile tests and scanning electron microscopy(SEM)experiments were carried out on the porous FeAl intermetallics(porosities of 41.1%,44.2%and 49.3%,pore size of 15−30μm)prepared by our research group to study the macroscopic mechanical properties and microscopic failure mechanism.The results show that the tensileσ−εcurves of the porous FeAl with different porosities can be divided into four stages:elasticity,yielding,strengthening and failure,without necking phenomenon.The elastic modulus,ultimate strength and elongation decrease with the increase of porosity and the elongation is much lower than 5%.A macroscopic brittle fracture appears,and the microscopic fracture mechanism is mainly intergranular fracture,depending on the Al content in the dense FeAl intermetallics.In addition,the stochastic porous model(SPM)with random pore structure size and distribution is established by designing a self-compiling generation program in FORTRAN language.Combined with the secondary development platform of finite element software ANSYS,the effective elastic moduli of the porous FeAl can be determined by elastic analysis of SPM and they are close to the experimental values,which can verify the validity of the established SPM for analyzing the elastic properties of the porous material.