压铸镁合金表面晶粒不均匀性的模拟研究

以AM50镁合金为研究对象,通过实验数据建立压铸件表面晶粒形核及生长模型,利用计算机模拟程序分析了不同压铸工艺对镁合金铸件表面不均匀性、中心压室预结晶含量及最终微观组织的影响。

Vacuum assisted high-pressure die casting of AZ91D magnesium alloy at different slow shot speeds

The effects of vacuum assistance on the microstructure and mechanical properties of high-pressure die cast AZ91 D alloy at different slow shot speeds were evaluated. Plate-shaped castings of AZ91 D alloy were carried out on a TOYO BD-350V5 cold chamber die casting machine incorporated with a self-improved TOYO vacuum system. It was found that the vacuum pressure in the die cavity at the beginning of mold filling increases with the increase of slow shot speed, following a cubic polynomial curve, resulting in a decline in the porosity-reduction ability of vacuum assistance with the increase of slow shot speed. The externally solidified crystal（ESC） contents in conventional and vacuum die castings behave similar against the slow shot speed. The tensile properties of vacuum die castings were strongly influenced by the ESC content at relative low slow shot speeds. With the increase of slow shot speed, the influence of the gas porosity level in vacuum die castings would get prominent.

Effects of shot speed and biscuit thickness on externaly solidified crystals of high-pressure diet cast AM60B magnesium alloy

Standard mechanical test bars with a diameter of 6.4 mm and a gauge length of 50 mm were processed, and the microstructures of die cast AM60B alloy under different die casting process parameters were observed. The influences of the slow shot speed, the fast shot speed and the biscuit thickness on the externally solidified crystals （ESCs） were investigated. With the increase of the biscuit thickness, the number of the ESCs in the cast samples decreases. Under a low slow shot speed, larg ESCs are found in the cast structure and a high fast shot speed results in more spherical ESCs. The relationships between ESCs and process parameters were also discussed.

Effect of multi-step slow shot speed on microstructure of vacuum die cast AZ91D magnesium alloy

Two multi-step （two-step and three-step） slow shot speeds were used in the vacuum die casting process of AZ91D magnesium alloy. The vacuum pressure variation in the die cavity before mold filling was monitored by using a pressure sensor. The microstructures of the produced castings were analyzed with optical microscope and image analysis software. The experimental results demonstrate that, the vacuum pressure in the die cavity at the beginning of mold filling is significantly reduced by using three-step slow shot speed, resulting in a low gas porosity level in the produced castings. At an appropriate multi-step slow shot speed, the dwell time of the liquid metal in the shot sleeve before mold filling can be reduced and the flow of the liquid metal in the shot sleeve at the later stage of the slow shot process can be restrained, which cause a low externally solidified crystal content in the produced castings.

Effect of different processing parameters on interfacial heat-transfer behavior in high-pressure die-casting process

Vacuum die casting can reduce the'air entrapment'phenomenon during casting process.Based on the temperature measurements at metal-die interface with different processing parameters,such as slow shot speed(VL),high shot speed(VH),pouring temperature(Tp)and initial die temperature(Tm),inverse method was developed to determine the interfacial heat transfer coefficient(IHTC).The results indicate that a closer contact between the casting and die could be achieved when the vacuum system is used.It is found that the vacuum could strongly increase the values of IHTC and decrease the grain size in castings.The IHTC could have a higher peak value with increasing the Tp from680to720℃or the VL from0.1to0.4m/s.In addition,the influence of the VH and Tm on IHTC could be negligible.