Distinguished from commonly used Fe2O3 and Fe3O4,a three-dimensional multilevel macromicro-mesoporous structure of FeC2O4/graphene composite has been prepared as binderfree electrode for supercapacitors.The as-prepare...Distinguished from commonly used Fe2O3 and Fe3O4,a three-dimensional multilevel macromicro-mesoporous structure of FeC2O4/graphene composite has been prepared as binderfree electrode for supercapacitors.The as-prepared materials are composed of macroporous graphene and microporous/mesoporous ferrous oxalate.Generally,the decomposition voltage of water is 1.23 V and the practical voltage window limit is about 2 V for asymmetric supercapacitors in aqueous electrolytes.When FeC2O4/rGO hydrogel was used as the negative electrode and a pure rGO hydrogel was used as the positive electrode,the asymmetrical supercapacitor voltage window raised to 1.7 V in KOH(1.0 mol/L)electrolyte and reached up to 2.5 V in a neutral aqueous Na2SO4(1.0 mol/L)electrolyte.Correspondingly it also exhibits a high performance with an energy density of 59.7 Wh/kg.By means of combining a metal oxide that owns micro-mesoporous structure with graphene,this work provides a new opportunity for preparing high-voltage aqueous asymmetric supercapacitors without addition of conductive agent and binder.展开更多
The phase structure of ZK60-1Er magnesium alloy thermally compressed at the temperature of 450℃ and the strain rate of 1×10 -4 s -1 was determined by transmission electron microscopy(TEM)and high-resolution elec...The phase structure of ZK60-1Er magnesium alloy thermally compressed at the temperature of 450℃ and the strain rate of 1×10 -4 s -1 was determined by transmission electron microscopy(TEM)and high-resolution electron microscopy(HREM).The results show that this magnesium alloy contains many new W phases(Mg3Zn3Er2,FCC structure)in the matrix.Those new W phases have two morphologies,either irregularly rectangular or rod morphology·Lattice constants of the two new W phases are slightly higher than those of W Phase(Mg3Zn3Y2)containing rare earth element of yttrium.展开更多
(K0.47Na0.47Li0.06)NbO3 (KNLN) lead-free ceramics were prepared by molten salt synthesis (MSS) method using k2CO3-Na2CO3 eutectic mixtures as the flux. The microstructure and piezoelectric properties when sintered at ...(K0.47Na0.47Li0.06)NbO3 (KNLN) lead-free ceramics were prepared by molten salt synthesis (MSS) method using k2CO3-Na2CO3 eutectic mixtures as the flux. The microstructure and piezoelectric properties when sintered at 980-1 030 ℃ were investigated. The calcined powders were examined by X-ray diffraction. The microstructure of the calcined powders and sintered bodies was observed using a scanning electron microscope (SEM).The piezoelectric constant d33 was measured using a quasi-static piezoelectric d33 meter. The planar coupling coefficient Kp was calculated by resonance-antiresonance method. The experimental data for each sample's performance indicators were the average values of 8 specimens. The relative densities of sintered specimens are above 97%, and the dielectric loss is below 0.03. It was found that (K0.47Na0.47Li0.06)NbO3 prepared by MSS is compact and lead-free. The piezoelectric constant d33 is 216 pC·N-1 and the planar electromechanical coupling factor Kp is 0.352.展开更多
SnO2-based varistor samples doped with Co2O3,Nb2O5 and Cr2O3 were prepared by ball-mixed oxide method.The microstructure,nonlinear I-V characteristic and surge current performances of these samples were investigated.T...SnO2-based varistor samples doped with Co2O3,Nb2O5 and Cr2O3 were prepared by ball-mixed oxide method.The microstructure,nonlinear I-V characteristic and surge current performances of these samples were investigated.This paper mainly focused on the dependence of the residual voltage ratio behavior of SnO2-based varistors on Nb2O5 addition,different factors influencing the residual voltage ratio in different concentration of Nb2O5 were analyzed.The Nb2O5 addition influences its residual voltage ratio by changing the grain size,forming defects(especially the free electrons) and cumulative effect.The measured results indicated that the optimally obtained sample with 0.07mol% Nb2O5 possesses the lowest residual voltage ratio of 1.86,the corresponding nonlinear coefficient and the threshold electric field are 42.6 and 364.6 V/mm,respectively.展开更多
基金supported by the National Natural Science Foundation of China (No.51673180 and No. 51673180)
文摘Distinguished from commonly used Fe2O3 and Fe3O4,a three-dimensional multilevel macromicro-mesoporous structure of FeC2O4/graphene composite has been prepared as binderfree electrode for supercapacitors.The as-prepared materials are composed of macroporous graphene and microporous/mesoporous ferrous oxalate.Generally,the decomposition voltage of water is 1.23 V and the practical voltage window limit is about 2 V for asymmetric supercapacitors in aqueous electrolytes.When FeC2O4/rGO hydrogel was used as the negative electrode and a pure rGO hydrogel was used as the positive electrode,the asymmetrical supercapacitor voltage window raised to 1.7 V in KOH(1.0 mol/L)electrolyte and reached up to 2.5 V in a neutral aqueous Na2SO4(1.0 mol/L)electrolyte.Correspondingly it also exhibits a high performance with an energy density of 59.7 Wh/kg.By means of combining a metal oxide that owns micro-mesoporous structure with graphene,this work provides a new opportunity for preparing high-voltage aqueous asymmetric supercapacitors without addition of conductive agent and binder.
基金Project(2008329)supported by Liaoning Provincial Education Ministry,ChinaProject supported by the Key Laboratory of Material Processing & Control of Liaoning Province,China
文摘The phase structure of ZK60-1Er magnesium alloy thermally compressed at the temperature of 450℃ and the strain rate of 1×10 -4 s -1 was determined by transmission electron microscopy(TEM)and high-resolution electron microscopy(HREM).The results show that this magnesium alloy contains many new W phases(Mg3Zn3Er2,FCC structure)in the matrix.Those new W phases have two morphologies,either irregularly rectangular or rod morphology·Lattice constants of the two new W phases are slightly higher than those of W Phase(Mg3Zn3Y2)containing rare earth element of yttrium.
基金Supported by National Natural Science Foundation of China (No.10232030)Key Laboratory for Advanced Ceramics and Machining Technology,Ministry of Education,Tianjin University (No. x06050)
文摘(K0.47Na0.47Li0.06)NbO3 (KNLN) lead-free ceramics were prepared by molten salt synthesis (MSS) method using k2CO3-Na2CO3 eutectic mixtures as the flux. The microstructure and piezoelectric properties when sintered at 980-1 030 ℃ were investigated. The calcined powders were examined by X-ray diffraction. The microstructure of the calcined powders and sintered bodies was observed using a scanning electron microscope (SEM).The piezoelectric constant d33 was measured using a quasi-static piezoelectric d33 meter. The planar coupling coefficient Kp was calculated by resonance-antiresonance method. The experimental data for each sample's performance indicators were the average values of 8 specimens. The relative densities of sintered specimens are above 97%, and the dielectric loss is below 0.03. It was found that (K0.47Na0.47Li0.06)NbO3 prepared by MSS is compact and lead-free. The piezoelectric constant d33 is 216 pC·N-1 and the planar electromechanical coupling factor Kp is 0.352.
基金supported by the National Natural Science Foundations of China (Grants Nos 50425721 and 50737001)
文摘SnO2-based varistor samples doped with Co2O3,Nb2O5 and Cr2O3 were prepared by ball-mixed oxide method.The microstructure,nonlinear I-V characteristic and surge current performances of these samples were investigated.This paper mainly focused on the dependence of the residual voltage ratio behavior of SnO2-based varistors on Nb2O5 addition,different factors influencing the residual voltage ratio in different concentration of Nb2O5 were analyzed.The Nb2O5 addition influences its residual voltage ratio by changing the grain size,forming defects(especially the free electrons) and cumulative effect.The measured results indicated that the optimally obtained sample with 0.07mol% Nb2O5 possesses the lowest residual voltage ratio of 1.86,the corresponding nonlinear coefficient and the threshold electric field are 42.6 and 364.6 V/mm,respectively.