采用原位化学反应(in-situ chemical reaction)法制备了Nafion-TiO2复合膜,利用X射线衍射(XRD)、红外衰减全反射法(FT-IR-ATR)和红外(FT-IR)压片法对Nafion膜及Nafion-TiO2复合膜的结构进行了表征。首次用砂纸打磨的方法制备了Nafio...采用原位化学反应(in-situ chemical reaction)法制备了Nafion-TiO2复合膜,利用X射线衍射(XRD)、红外衰减全反射法(FT-IR-ATR)和红外(FT-IR)压片法对Nafion膜及Nafion-TiO2复合膜的结构进行了表征。首次用砂纸打磨的方法制备了Nafion膜的粉末试样,并成功地应用于红外光谱的测试与分析。研究表明砂纸打磨的方法操作更简便,并且所获得的复合膜的结构信息更全面。Nafion膜的孔腔内掺入了纳米级TiO2粒子,TiO2粒子的加入对膜的主体结构没有改变。展开更多
The Al2O3（p）/Al nano-composites were fabricated from Al-K2ZrF6-Na2B4O7 system by sonochemistry in situ reaction. The fabrication mechanisms, including high intensity ultrasonic influence on microstructures and reinf...The Al2O3（p）/Al nano-composites were fabricated from Al-K2ZrF6-Na2B4O7 system by sonochemistry in situ reaction. The fabrication mechanisms, including high intensity ultrasonic influence on microstructures and reinforcement particles-aluminum matrix interface, were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The XRD results show that the component of the as-prepared composites is Al2O3 reinforcement. The SEM analysis results indicate that Al2O3 particles are uniformly distributed in the aluminum matrix. The TEM results show that the morphologies of Al2O3 particles present in nearly sphere-shape, the sizes are in the range of 20-100 nm, and the interfaces are net and no interfacial outgrowth is observed. Analysis with secondary development Image-J software shows that Al2O3 recoveries are firstly improved and then decreased with increasing ultrasonic power. When the power is 0.4 kW, the distribution is the best, and a maximum number of particles are obtained. The reaction mechanisms were investigated.展开更多
Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles a...Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.展开更多
This work presents a study for chemical leaching of sphalerite concentrate under various constant Fe3+ concentrations and redox potential conditions. The effects of Fe3+ concentration and redox potential on chemical l...This work presents a study for chemical leaching of sphalerite concentrate under various constant Fe3+ concentrations and redox potential conditions. The effects of Fe3+ concentration and redox potential on chemical leaching of sphalerite were investigated. The shrinking core model was applied to analyze the experimental results. It was found that both the Fe3+ concentration and the redox potential controlled the chemical leaching rate of sphalerite. A new kinetic model was developed, in which the chemical leaching rate of sphalerite was proportional to Fe3+ concentration and Fe3+ /Fe2+ ratio. All the model parameters were evaluated from the experimental data. The model predictions fit well with the experimental observed values.展开更多
TiC, ZrC and TaC modified layers were in-situ prepared on graphite matrix by chemical vapor infiltration method with metal salts as the activator. Taking the TiC modified layer as an example, through thermodynamic cal...TiC, ZrC and TaC modified layers were in-situ prepared on graphite matrix by chemical vapor infiltration method with metal salts as the activator. Taking the TiC modified layer as an example, through thermodynamic calculation and experiment, the thermal decomposition process of raw materials(Ti/K_(2)TiF_(6)) was analyzed, the formation mechanism of TiC was determined, and the distribution of TiC modified layer was modulated. The results show that activator K_(2)TiF_(6)has higher decomposition temperature than NH4Cl, which is conducive to improving the utilization rate of raw materials in the gas infiltration process. Increasing the content of Ti powder can increase the concentration of reaction gas and contribute to the formation of TiC modified layer. When the molar ratio of Ti to K_(2)TiF_(6)is 3:1, the surface thickness and infiltration depth of Ti C are 5.42 and 136.24 μm, respectively. Increasing the reaction temperature can improve the rate of in-situ reaction and the thickness of TiC surface layer. When the experimental temperature rises to 1600 °C, the TiC surface layer thickness increases to 20.27 μm.展开更多
Electrochemical CO2 reduction reaction(CO2RR)powered by renewable electricity has emerged as the most promising technique for CO2 conversion,making it possible to realize a carbon‐neutral cycle.Highly efficient,robus...Electrochemical CO2 reduction reaction(CO2RR)powered by renewable electricity has emerged as the most promising technique for CO2 conversion,making it possible to realize a carbon‐neutral cycle.Highly efficient,robust,and cost‐effective catalysts are highly demanded for the near‐future practical applications of CO2RR.Previous studies on atomically dispersed metal‐nitrogen(M‐Nx)sites constituted of earth abundant elements with maximum atom‐utilization efficiency have demonstrated their performance towards CO2RR.This review summarizes recent advances on a variety of M‐Nx sites‐containing transition metal‐centered macrocyclic complexes,metal organic frameworks,and M‐Nx‐doped carbon materials for efficient CO2RR,including both experimental and theoretical studies.The roles of metal centers,coordinated ligands,and conductive supports on the intrinsic activity and selectivity,together with the importance of reaction conditions for improved performance are discussed.The mechanisms of CO2RR over these M‐Nx‐containing materials are presented to provide useful guidance for the rational design of efficient catalysts towards CO2RR.展开更多
文摘采用原位化学反应(in-situ chemical reaction)法制备了Nafion-TiO2复合膜,利用X射线衍射(XRD)、红外衰减全反射法(FT-IR-ATR)和红外(FT-IR)压片法对Nafion膜及Nafion-TiO2复合膜的结构进行了表征。首次用砂纸打磨的方法制备了Nafion膜的粉末试样,并成功地应用于红外光谱的测试与分析。研究表明砂纸打磨的方法操作更简便,并且所获得的复合膜的结构信息更全面。Nafion膜的孔腔内掺入了纳米级TiO2粒子,TiO2粒子的加入对膜的主体结构没有改变。
基金Project (50971066) supported by the National Natural Science Foundation of ChinaProject (20070299004) supported by the Research Fund for the Doctoral Program of Higher Education of China+1 种基金Project (2008-46) supported by the Jiangsu Provincial ‘333’ Project of training the High-level Talents Foundation, ChinaProject (BE2009127) supported by the Jiangsu Provincial Science Supporting Item, China
文摘The Al2O3（p）/Al nano-composites were fabricated from Al-K2ZrF6-Na2B4O7 system by sonochemistry in situ reaction. The fabrication mechanisms, including high intensity ultrasonic influence on microstructures and reinforcement particles-aluminum matrix interface, were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The XRD results show that the component of the as-prepared composites is Al2O3 reinforcement. The SEM analysis results indicate that Al2O3 particles are uniformly distributed in the aluminum matrix. The TEM results show that the morphologies of Al2O3 particles present in nearly sphere-shape, the sizes are in the range of 20-100 nm, and the interfaces are net and no interfacial outgrowth is observed. Analysis with secondary development Image-J software shows that Al2O3 recoveries are firstly improved and then decreased with increasing ultrasonic power. When the power is 0.4 kW, the distribution is the best, and a maximum number of particles are obtained. The reaction mechanisms were investigated.
基金Project(2007AA03Z548) supported by High-Tech Research and Development Program of ChinaProject(50971066) supported by the National Natural Science Foundation of ChinaProject(1283000349) supported by the Jiangsu University Research Fund for Advanced Scholars,China
文摘Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.
基金Supported by the National Basic Research Program （2010CB630902, 2004CB619202） the National Natural Science Foundation of China （31070034, 30800011, 31260396）+1 种基金 the Knowledge Innovation Program of CAS （2AKSCX2-YW-JS401） the Reward Fund for Young Scientists of Shandong Province （2007BS08002） of China
文摘This work presents a study for chemical leaching of sphalerite concentrate under various constant Fe3+ concentrations and redox potential conditions. The effects of Fe3+ concentration and redox potential on chemical leaching of sphalerite were investigated. The shrinking core model was applied to analyze the experimental results. It was found that both the Fe3+ concentration and the redox potential controlled the chemical leaching rate of sphalerite. A new kinetic model was developed, in which the chemical leaching rate of sphalerite was proportional to Fe3+ concentration and Fe3+ /Fe2+ ratio. All the model parameters were evaluated from the experimental data. The model predictions fit well with the experimental observed values.
基金financially supported by the National Natural Science Foundation of China(No.11705281)。
文摘TiC, ZrC and TaC modified layers were in-situ prepared on graphite matrix by chemical vapor infiltration method with metal salts as the activator. Taking the TiC modified layer as an example, through thermodynamic calculation and experiment, the thermal decomposition process of raw materials(Ti/K_(2)TiF_(6)) was analyzed, the formation mechanism of TiC was determined, and the distribution of TiC modified layer was modulated. The results show that activator K_(2)TiF_(6)has higher decomposition temperature than NH4Cl, which is conducive to improving the utilization rate of raw materials in the gas infiltration process. Increasing the content of Ti powder can increase the concentration of reaction gas and contribute to the formation of TiC modified layer. When the molar ratio of Ti to K_(2)TiF_(6)is 3:1, the surface thickness and infiltration depth of Ti C are 5.42 and 136.24 μm, respectively. Increasing the reaction temperature can improve the rate of in-situ reaction and the thickness of TiC surface layer. When the experimental temperature rises to 1600 °C, the TiC surface layer thickness increases to 20.27 μm.
基金supported by the National Key R&D Program of China(2017YFA0700102)the National Natural Science Foundation of China(21573222 and 91545202)+1 种基金the Outstanding Youth Talent Project of Dalian(2017RJ03)the DMTO Project of Dalian Institute of Chemical Physics,CAS(DICP DMTO201702),the Strategic Priority Research Program of the Chinese Academy of Sciences(XDB17020200),the Youth Innovation Promotion Association,CAS(2015145)~~
文摘Electrochemical CO2 reduction reaction(CO2RR)powered by renewable electricity has emerged as the most promising technique for CO2 conversion,making it possible to realize a carbon‐neutral cycle.Highly efficient,robust,and cost‐effective catalysts are highly demanded for the near‐future practical applications of CO2RR.Previous studies on atomically dispersed metal‐nitrogen(M‐Nx)sites constituted of earth abundant elements with maximum atom‐utilization efficiency have demonstrated their performance towards CO2RR.This review summarizes recent advances on a variety of M‐Nx sites‐containing transition metal‐centered macrocyclic complexes,metal organic frameworks,and M‐Nx‐doped carbon materials for efficient CO2RR,including both experimental and theoretical studies.The roles of metal centers,coordinated ligands,and conductive supports on the intrinsic activity and selectivity,together with the importance of reaction conditions for improved performance are discussed.The mechanisms of CO2RR over these M‐Nx‐containing materials are presented to provide useful guidance for the rational design of efficient catalysts towards CO2RR.