Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles a...Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.展开更多
Bioreduction as a novel nanoparticle synthesizing technology attracts increasing attention. Dried cells of the bacterium Aeromonas sp. SH10 rapidly reduced [Ag（NH3）2]^＋ to Ago in the solution into which some amount...Bioreduction as a novel nanoparticle synthesizing technology attracts increasing attention. Dried cells of the bacterium Aeromonas sp. SH10 rapidly reduced [Ag（NH3）2]^＋ to Ago in the solution into which some amount of OH^- was introduced. The surface plasmon resonance centered at 425 nm on the UV-vis spectra and five broad Bragg reflections on the XRD pattern showed that stable silver nanoparticles were formed during the bioreduction process. TEM and SEM observations suggested that the silver nanoparticles were uniform in size and well dispersed on the cells and in the solution. Therefore, silver nanoparticles could be prepared rapidly by this bioreduction technology.展开更多
基金Project(2007AA03Z548) supported by High-Tech Research and Development Program of ChinaProject(50971066) supported by the National Natural Science Foundation of ChinaProject(1283000349) supported by the Jiangsu University Research Fund for Advanced Scholars,China
文摘Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.
基金Supported by the National Natural Science Foundation of China (No.20376076).
文摘Bioreduction as a novel nanoparticle synthesizing technology attracts increasing attention. Dried cells of the bacterium Aeromonas sp. SH10 rapidly reduced [Ag（NH3）2]^＋ to Ago in the solution into which some amount of OH^- was introduced. The surface plasmon resonance centered at 425 nm on the UV-vis spectra and five broad Bragg reflections on the XRD pattern showed that stable silver nanoparticles were formed during the bioreduction process. TEM and SEM observations suggested that the silver nanoparticles were uniform in size and well dispersed on the cells and in the solution. Therefore, silver nanoparticles could be prepared rapidly by this bioreduction technology.