Gas blowing is a valid method to remove the impurities from metallurgical grade silicon（MG-Si） melt.The thermodynamic behavior of impurities Fe,Al,Ca,Ti,Cu,C,B and P in MG-Si was studied in the process of O2 blowing...Gas blowing is a valid method to remove the impurities from metallurgical grade silicon（MG-Si） melt.The thermodynamic behavior of impurities Fe,Al,Ca,Ti,Cu,C,B and P in MG-Si was studied in the process of O2 blowing.The removal efficiencies of impurities in MG-Si were investigated using O2 blowing in ladle.It is found that the removal efficiencies are higher than 90% for Ca and Al and nearly 50% for B and Ti.The morphology of inclusions was analyzed and the phases Al3Ni,NiSi2 and Al3Ni were confirmed in MG-Si by X-ray diffraction.It was found that SiB4 exists in Si？B binary system.The chemical composition of inclusions in MG-Si before and after refining was analyzed by SEM-EDS.It is found that the amount of white inclusion reduces for the removal of most Al and Ca in the forms of molten slag inclusion and the contents of Fe,Ni and Mn in inclusion increase for their inertia in silicon melt with O2 blowing.展开更多
The effect of high density pulse electric current (HDPEC) on the solidification structure of the low temperature melt(LTM) of commercial A356 alloy was investigated. In the experiments, the HDPEC was discharged in the...The effect of high density pulse electric current (HDPEC) on the solidification structure of the low temperature melt(LTM) of commercial A356 alloy was investigated. In the experiments, the HDPEC was discharged in the LTM (953?K, 903?K and 873?K). By the control experiments, the results showed that the solidification structure of the LTM of A356 alloy is refined apparently when the HDPEC is discharged in low temperature melt. However, the holding time of melt treated has an adverse effect on the solidification structure. The longer the holding time of the melt treated with HDPEC, the coarser the microstructure. With the same discharge voltage, the lower the temperature of LTM, the more obscure the refinement of solidification structure. Finally, the mechanism of microstructure refining by HDPEC was analyzed.展开更多
基金Projects(51104080,u1137601) supported by the National Natural Science Foundation of ChinaProject(2009CD027) supported by the Natural Science Foundation of Yunnan Province,ChinaProject(14118557) supported by the Personnel Training Foundation of Kunming University of Science and Technology,China
文摘Gas blowing is a valid method to remove the impurities from metallurgical grade silicon（MG-Si） melt.The thermodynamic behavior of impurities Fe,Al,Ca,Ti,Cu,C,B and P in MG-Si was studied in the process of O2 blowing.The removal efficiencies of impurities in MG-Si were investigated using O2 blowing in ladle.It is found that the removal efficiencies are higher than 90% for Ca and Al and nearly 50% for B and Ti.The morphology of inclusions was analyzed and the phases Al3Ni,NiSi2 and Al3Ni were confirmed in MG-Si by X-ray diffraction.It was found that SiB4 exists in Si？B binary system.The chemical composition of inclusions in MG-Si before and after refining was analyzed by SEM-EDS.It is found that the amount of white inclusion reduces for the removal of most Al and Ca in the forms of molten slag inclusion and the contents of Fe,Ni and Mn in inclusion increase for their inertia in silicon melt with O2 blowing.
文摘The effect of high density pulse electric current (HDPEC) on the solidification structure of the low temperature melt(LTM) of commercial A356 alloy was investigated. In the experiments, the HDPEC was discharged in the LTM (953?K, 903?K and 873?K). By the control experiments, the results showed that the solidification structure of the LTM of A356 alloy is refined apparently when the HDPEC is discharged in low temperature melt. However, the holding time of melt treated has an adverse effect on the solidification structure. The longer the holding time of the melt treated with HDPEC, the coarser the microstructure. With the same discharge voltage, the lower the temperature of LTM, the more obscure the refinement of solidification structure. Finally, the mechanism of microstructure refining by HDPEC was analyzed.